Connector Seals
![](/cms/media/images/responsive/application_key_visuals/cables_weatherpacks_wr_img_360.jpg)
The physical, mechanical and insulating properties of ELASTOSIL® silicone rubber grades make them the ideal choice for automotive electrical connectors. Their excellent chemical resistance, flawless insulation and thermal cycling resistance ensure that power is delivered where it's needed – safely and reliably.
Product Recommendations
Products
|
Technical data
|
Product properties
|
||||||
---|---|---|---|---|---|---|---|---|
Appearance | Hardness Shore A | Tensile strength | Elongation at break | Tear strength | Compression Set | Specific Features | ||
transparent transparent | 22[1] 22[1] | 8.3 N/mm²[2] 8.3 N/mm²[2] | 870 %[3] 870 %[3] | 24 N/mm[4] 24 N/mm[4] | 17 %[5] 17 %[5] | Food-contact, General purpose, Reduced volatile content | ||
transparent transparent | 30[1] 30[1] | 7.0 N/mm²[2] 7.0 N/mm²[2] | 610 %[3] 610 %[3] | 21 N/mm[4] 21 N/mm[4] | 10 %[5] 10 %[5] | Food-contact, General purpose, Reduced volatile content | ||
transparent transparent | 40[1] 40[1] | 10.0 N/mm²[2] 10.0 N/mm²[2] | 610 %[3] 610 %[3] | 30 N/mm[4] 30 N/mm[4] | 11 %[5] 11 %[5] | Food-contact, General purpose, Reduced volatile content | ||
transparent transparent | 50[1] 50[1] | 10.3 N/mm²[2] 10.3 N/mm²[2] | 490 %[3] 490 %[3] | 26 N/mm[4] 26 N/mm[4] | 13 %[5] 13 %[5] | Food-contact, General purpose, Reduced volatile content | ||
transparent transparent | 60[1] 60[1] | 9.8 N/mm²[2] 9.8 N/mm²[2] | 340 %[3] 340 %[3] | 27 N/mm[4] 27 N/mm[4] | 16 %[5] 16 %[5] | Food-contact, General purpose, Reduced volatile content | ||
transparent transparent | 70[1] 70[1] | 9.3 N/mm²[2] 9.3 N/mm²[2] | 290 %[3] 290 %[3] | 20 N/mm[4] 20 N/mm[4] | 16 %[5] 16 %[5] | Food-contact, General purpose, Reduced volatile content | ||
transparent transparent | 30[1] 30[1] | 6.0 N/mm²[2] 6.0 N/mm²[2] | 610 %[3] 610 %[3] | 16 N/mm[4] 16 N/mm[4] | 13 %[6] 13 %[6] | Fast curing, Low compression set without post-cure, Reduced volatile content | ||
transparent transparent | 40[1] 40[1] | 7.8 N/mm²[2] 7.8 N/mm²[2] | 600 %[3] 600 %[3] | 22 N/mm[4] 22 N/mm[4] | 16 %[6] 16 %[6] | Fast curing, Low compression set without post-cure, Reduced volatile content | ||
transparent transparent | 50[1] 50[1] | 8.7 N/mm²[2] 8.7 N/mm²[2] | 500 %[3] 500 %[3] | 24 N/mm[4] 24 N/mm[4] | 15 %[6] 15 %[6] | Fast curing, Low compression set without post-cure, Reduced volatile content | ||
transparent transparent | 60[1] 60[1] | 9.5 N/mm²[2] 9.5 N/mm²[2] | 380 %[3] 380 %[3] | 28 N/mm[4] 28 N/mm[4] | 15 %[6] 15 %[6] | Fast curing, Low compression set without post-cure, Reduced volatile content | ||
transparent transparent | 70[1] 70[1] | 8.5 N/mm²[2] 8.5 N/mm²[2] | 330 %[3] 330 %[3] | 23 N/mm[4] 23 N/mm[4] | 19 %[6] 19 %[6] | Fast curing, Low compression set without post-cure, Reduced volatile content | ||
transparent transparent | 30[1] 30[1] | 7.5 N/mm²[2] 7.5 N/mm²[2] | 650 %[3] 650 %[3] | 24 N/mm[4] 24 N/mm[4] | 17 %[6] 17 %[6] | Low compression set without post-cure, Low coefficient of friction, Reduced volatile content | ||
transparent transparent | 50[1] 50[1] | 9.0 N/mm²[2] 9.0 N/mm²[2] | 460 %[3] 460 %[3] | 31 N/mm[4] 31 N/mm[4] | 15 %[6] 15 %[6] | Low compression set without post-cure, Low coefficient of friction, Reduced volatile content | ||
opaque opaque | 30[1] 30[1] | 7.4 N/mm²[2] 7.4 N/mm²[2] | 710 %[3] 710 %[3] | 17 N/mm[4] 17 N/mm[4] | 27 %[7] 27 %[7] | Self-adhesive, Oil bleeding | ||
opaque opaque | 40[1] 40[1] | 8.8 N/mm²[2] 8.8 N/mm²[2] | 620 %[3] 620 %[3] | 21 N/mm[4] 21 N/mm[4] | 21 %[7] 21 %[7] | Self-adhesive, Oil bleeding | ||
opaque opaque | 50[1] 50[1] | 8.6 N/mm²[2] 8.6 N/mm²[2] | 510 %[3] 510 %[3] | 23 N/mm[4] 23 N/mm[4] | 12 %[7] 12 %[7] | Self-adhesive, Oil bleeding | ||
transparent transparent | 30[1] 30[1] | 8.0 N/mm²[2] 8.0 N/mm²[2] | 760 %[3] 760 %[3] | 25 N/mm[4] 25 N/mm[4] | 14 %[7] 14 %[7] | Self-adhesive, Low coefficient of friction | ||
transparent transparent | 50[1] 50[1] | 7.8 N/mm²[2] 7.8 N/mm²[2] | 410 %[3] 410 %[3] | 33 N/mm[4] 33 N/mm[4] | 12 %[7] 12 %[7] | Self-adhesive, Low coefficient of friction | ||
opaque opaque | 50[1] 50[1] | 7.4 N/mm²[2] 7.4 N/mm²[2] | 460 %[3] 460 %[3] | 39 N/mm[4] 39 N/mm[4] | 10 %[6] 10 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
off-white off-white | 30[1] 30[1] | 6.8 N/mm²[2] 6.8 N/mm²[2] | 680 %[3] 680 %[3] | 20 N/mm[4] 20 N/mm[4] | 18 %[6] 18 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
off-white off-white | 50[1] 50[1] | 8.2 N/mm²[2] 8.2 N/mm²[2] | 450 %[3] 450 %[3] | 34 N/mm[4] 34 N/mm[4] | 15 %[6] 15 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
white white | 50[1] 50[1] | 7.5 N/mm²[2] 7.5 N/mm²[2] | 460 %[3] 460 %[3] | 38 N/mm[4] 38 N/mm[4] | 7 %[6] 7 %[6] | Ultra-low compression set, Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 50[1] 50[1] | 9.0 N/mm²[2] 9.0 N/mm²[2] | 490 %[3] 490 %[3] | 30 N/mm[4] 30 N/mm[4] | 13 %[6] 13 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 40[1] 40[1] | 8.0 N/mm²[2] 8.0 N/mm²[2] | 610 %[3] 610 %[3] | 25 N/mm[4] 25 N/mm[4] | 13 %[6] 13 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 50[1] 50[1] | 8.5 N/mm²[2] 8.5 N/mm²[2] | 460 %[3] 460 %[3] | 37 N/mm[4] 37 N/mm[4] | 12 %[6] 12 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 60[1] 60[1] | 9.2 N/mm²[2] 9.2 N/mm²[2] | 420 %[3] 420 %[3] | 32 N/mm[4] 32 N/mm[4] | 13 %[6] 13 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 68[1] 68[1] | 8.5 N/mm²[2] 8.5 N/mm²[2] | 350 %[3] 350 %[3] | 28 N/mm[4] 28 N/mm[4] | 16 %[6] 16 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 30[1] 30[1] | 8.0 N/mm²[2] 8.0 N/mm²[2] | 680 %[3] 680 %[3] | 22 N/mm[4] 22 N/mm[4] | 16 %[6] 16 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 30[1] 30[1] | 7.2 N/mm²[2] 7.2 N/mm²[2] | 700 %[3] 700 %[3] | 22 N/mm[4] 22 N/mm[4] | 15 %[6] 15 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 50[1] 50[1] | 8.5 N/mm²[2] 8.5 N/mm²[2] | 500 %[3] 500 %[3] | 36 N/mm[4] 36 N/mm[4] | 14 %[6] 14 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 21[1] 21[1] | 6.1 N/mm²[2] 6.1 N/mm²[2] | 800 %[3] 800 %[3] | 16 N/mm[4] 16 N/mm[4] | 16 %[6] 16 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 30[1] 30[1] | 7.0 N/mm²[2] 7.0 N/mm²[2] | 750 %[3] 750 %[3] | 19 N/mm[4] 19 N/mm[4] | 15 %[6] 15 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 21[1] 21[1] | 6.2 N/mm²[2] 6.2 N/mm²[2] | 850 %[3] 850 %[3] | 16 N/mm[4] 16 N/mm[4] | 18 %[6] 18 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
opaque opaque | 32[1] 32[1] | 6.5 N/mm²[2] 6.5 N/mm²[2] | 600 %[3] 600 %[3] | 25 N/mm[4] 25 N/mm[4] | 14 %[6] 14 %[6] | Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content | ||
- - | 23[1] 23[1] | 6.3 N/mm²[2] 6.3 N/mm²[2] | 880 %[3] 880 %[3] | 15 N/mm[4] 15 N/mm[4] | 14 %[8] 14 %[8] | Oil bleeding, One-component, Addition Curing | ||
- - | 30[1] 30[1] | 10.8 N/mm²[2] 10.8 N/mm²[2] | 1100 %[3] 1100 %[3] | 34 N/mm[4] 34 N/mm[4] | 19 %[8] 19 %[8] | Oil bleeding, One-component, Addition Curing |
[1] Hardness Shore A | DIN ISO 48-4, [2] Tensile strength | ISO 37 type 1, [3] Elongation at break | ISO 37 type 1, [4] Tear strength | ASTM D 624 B, [5] Compression Set | 22 h | 175 °C | DIN ISO 815-1 type B method A | post-cured 6 h / 200 °C, [6] Compression Set | 22 h | 175 °C | DIN ISO 815-1 type B method A, [7] Compression Set | 22 h | 125 °C | DIN ISO 815-1 type B method A, [8] Compression Set | 22 h | 175 °C | DIN ISO 815-1 type B method A | post-cured 4 h / 200 °C, [] Suited, [] Well suited, [] Ideally suited