WACKER SilGel®
WACKER SilGel® comprises highly transparent, silicone rubber compounds that cure to form silicone gels. They stand out due to their low viscosity and strong inherent tack, often rendering a primer or adhesion promoter superfluous. All products can be fully automatically processed in mixing and metering units, and are ideal for efficient mass production.
WACKER SilGel® products are addition-curing, RTV-2-silicone elastomers that cure both at room temperature and at higher temperatures.
Benefits:
- Extremely low viscosity
- High inherent tack
- High flexibility
- Self-healing capacity
- Transparency in the visible light spectrum
- Excellent damping behavior
- Stability over a wide temperature range (−50 °C to +200 °C)
Applications:
- Encapsulation of sensitive electronic devices and power modules
- Optical applications, especially in photovoltaics
Industries:
- Semiconductor
- Power electronics
- Consumer and industrial electronics
- Automotive and e-mobility
Product Recommendations
Products
|
Technical data
|
||
---|---|---|---|
Viscosity, dynamic | Penetration | ||
7500.0 mPa·s[1] 7500.0 mPa·s[1] | 50 - 65 1/10mm[3] 50 - 65 1/10mm[3] | ||
1000 mPa·s[2] 1000 mPa·s[2] | 300 1/10mm[4] 300 1/10mm[4] | ||
1000 mPa·s[1] 1000 mPa·s[1] | 150 1/10mm[4] 150 1/10mm[4] | ||
- - | 70 1/10mm[5] 70 1/10mm[5] | ||
300 mPa·s[2] 300 mPa·s[2] | 280.0 1/10mm[6] 280.0 1/10mm[6] |
[1] Viscosity, dynamic | 25 °C | DIN EN ISO 3219, [2] Viscosity, dynamic | 25 °C | ISO 3219, [3] Penetration | DIN ISO 2137 | quarter cone, 9.38g, 5 sec., [4] Penetration | DIN ISO 2137 | 150 g hollow cone, 1 min., [5] Penetration (hollow cone, 9.38 g) | DIN ISO 2137, [6] Penetration | DIN ISO 2137 | 150 g hollow cone, 60 sec.