Orthotics & Prosthetics

WACKER RTV-2 Systems Make All the Difference
ELASTOSIL® P and SILPURAN® room-temperature-vulcanizing (RTV) silicone elastomers and gels are specially designed to meet specific prosthetic and orthotic demands. Orthotics focus on properties such the ability to cushion shock and vibration, and to apply gentle, comfortable compression. Prosthetics is a highly sensitive area of application. The aim is to make prostheses and epitheses that fit perfectly, are comfortable to wear, and are barely noticeable.
ELASTOSIL® P and SILPURAN®’s exceptional set of properties allow customized production of:
- Orthotic pelottes/pads
- Insoles, shoe orthotics
- Heel cushions, toe spacers, toe caps
- Anti-decubitus mats
- Aesthetic and functional finger, hand and partial-foot prostheses
- Epitheses
- Orthoses
- Liners
- External mammary prostheses
Benefits of ELASTOSIL® P and SILPURAN® silicone elastomers:
- Biocompatibility
- Durability: low surface tension, thermal stability and chemical stability
- Good resistance to a large number of solvents and chemicals
- No organic plasticizers involved
- Sterilizable for single and repeated use (sterilizable with steam, ethylene oxide, electron beams and γ-rays)
- The excellent mechanical properties are highly resistant to aging, weathering, heat and radiation
- Silicones do not support microbial growth (hydrophobic)
- Easy processing due to low viscosity and good mixing characteristics
- RTV-2 silicone rubber systems do not release any by-products on curing
- Broad hardness range
- High degree of comfort for wearer; breathability
Additional Information
Produktempfehlungen
Produkte
|
Technische Daten
|
Produktmerkmale
|
|||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
dynamische Viskosität | Weiterreißwiderstand | Penetration | Härte Shore A | Härte Shore 00 | Reißfestigkeit | Reißdehnung | Regulatorisch | Rheologie | Vernetzungseigenschaft | ||
6000 mPa·s[1] 6000 mPa·s[1] | > 20 N/mm[6] > 20 N/mm[6] | - - | 10[8] 10[8] | - - | 4,5 N/mm²[10] 4,5 N/mm²[10] | 950 %[12] 950 %[12] | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
5000 mPa·s[2] 5000 mPa·s[2] | 25 N/mm[6] 25 N/mm[6] | - - | 20[8] 20[8] | - - | > 6 N/mm²[10] > 6 N/mm²[10] | > 750 %[12] > 750 %[12] | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
10000 mPa·s[2] 10000 mPa·s[2] | 28 N/mm[7] 28 N/mm[7] | - - | 28[8] 28[8] | - - | 6 N/mm²[10] 6 N/mm²[10] | 500 %[12] 500 %[12] | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
4000 mPa·s[2] 4000 mPa·s[2] | 5,5 N/mm[6] 5,5 N/mm[6] | - - | - - | 30[14] 30[14] | > 1,5 N/mm²[10] > 1,5 N/mm²[10] | > 900 %[12] > 900 %[12] | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
100 mPa·s[3] 100 mPa·s[3] | - - | 150 1/10mm[15] 150 1/10mm[15] | - - | - - | - - | - - | Hautverträglich | - | zweikomponentig, Additionsvernetzend | ||
4000 mPa·s[3] 4000 mPa·s[3] | 1,5 N/mm[7] 1,5 N/mm[7] | - - | - - | 26[14] 26[14] | 1 N/mm²[10] 1 N/mm²[10] | 600 %[12] 600 %[12] | Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
350 mPa·s[4] 350 mPa·s[4] | - - | 160 1/10mm[16] 160 1/10mm[16] | - - | - - | - - | - - | Hautverträglich | - | zweikomponentig, Additionsvernetzend | ||
100 mPa·s[3] 100 mPa·s[3] | - - | 145 1/10mm[16] 145 1/10mm[16] | - - | - - | - - | - - | Hautverträglich | - | zweikomponentig, Additionsvernetzend | ||
8000 mPa·s[4] 8000 mPa·s[4] | - - | 220 1/10mm[17] 220 1/10mm[17] | - - | - - | - - | - - | Hautverträglich | - | zweikomponentig, Additionsvernetzend | ||
1800 mPa·s[4] 1800 mPa·s[4] | 2,1 N/mm[7] 2,1 N/mm[7] | - - | 7[8] 7[8] | 55[14] 55[14] | 1,8 N/mm²[10] 1,8 N/mm²[10] | 600 %[12] 600 %[12] | Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
1800 mPa·s[5] 1800 mPa·s[5] | 1,5 N/mm[7] 1,5 N/mm[7] | - - | - - | 18[14] 18[14] | 0,5 N/mm²[10] 0,5 N/mm²[10] | 400 %[12] 400 %[12] | Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
1400 mPa·s 1400 mPa·s | 2,0 N/mm[7] 2,0 N/mm[7] | - - | - - | 25 25 | 1,0 N/mm²[11] 1,0 N/mm²[11] | 500 %[13] 500 %[13] | Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
2000 mPa·s[4] 2000 mPa·s[4] | 6 N/mm[7] 6 N/mm[7] | - - | 4[8] 4[8] | 40[14] 40[14] | 2 N/mm²[10] 2 N/mm²[10] | 600 %[12] 600 %[12] | Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
2000 mPa·s[4] 2000 mPa·s[4] | 13 N/mm[7] 13 N/mm[7] | - - | 12[8] 12[8] | 60[14] 60[14] | 3 N/mm²[10] 3 N/mm²[10] | 600 %[12] 600 %[12] | Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
- - | 5 N/mm[7] 5 N/mm[7] | - - | 17[8] 17[8] | 70[14] 70[14] | 1,2 N/mm²[10] 1,2 N/mm²[10] | 550 %[12] 550 %[12] | Hautverträglich | knetbar | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
- - | 7 N/mm[7] 7 N/mm[7] | - - | 34[9] 34[9] | - - | 2,4 N/mm²[10] 2,4 N/mm²[10] | 250 %[12] 250 %[12] | Hautverträglich | knetbar | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | ||
2500 mPa·s[4] 2500 mPa·s[4] | 13 N/mm[7] 13 N/mm[7] | - - | 12[8] 12[8] | 60[14] 60[14] | 3,5 N/mm²[10] 3,5 N/mm²[10] | 680 %[12] 680 %[12] | biokompatibel, Hautverträglich | Fließfähig | zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur |
[1] dynamische Viskosität | 23 °C | ISO 3219, [2] dynamische Viskosität aufgerührt | 23 °C | ISO 3219, [3] dynamische Viskosität | ISO 3219, [4] dynamische Viskosität | DIN EN ISO 3219, [5] dynamische Viskosität (rotation) | DIN EN ISO 3219, [6] Weiterreißwiderstand | ASTM D 624, Die B, [7] Weiterreißwiderstand | ASTM D 624 B, [8] Härte Shore A | DIN ISO 48-4, [9] Härte Shore A | DIN ISO 48-4 | after 30 min, [10] Reißfestigkeit | ISO 37 Type 1, [11] Reißfestigkeit | ISO 37, [12] Reißdehnung | ISO 37 Type 1, [13] Reißdehnung | ISO 37, [14] Härte Shore 00 | ASTM D 2240, [15] Penetration | DIN ISO 2137 | hollow cone of 62.5 g, 5 s, [16] Penetration | DIN ISO 2137 | hollow cone of 25 g, 5 s, [17] Penetration | DIN ISO 2137 | hollow cone of 62,5 g, 5 s