WACKER SilGel®

WACKER SilGel® comprises highly transparent, silicone rubber compounds that cure to form silicone gels. They stand out due to their low viscosity and strong inherent tack, often rendering a primer or adhesion promoter superfluous. All products can be fully automatically processed in mixing and metering units, and are ideal for efficient mass production.

WACKER SilGel® products are addition-curing, RTV-2-silicone elastomers that cure both at room temperature and at higher temperatures.

Benefits:

  • Extremely low viscosity
  • High inherent tack
  • High flexibility
  • Self-healing capacity
  • Transparency in the visible light spectrum
  • Excellent damping behavior
  • Stability over a wide temperature range (−50 °C to +200 °C)

Applications:

  • Encapsulation of sensitive electronic devices and power modules
  • Optical applications, especially in photovoltaics

Industries:

  • Semiconductor
  • Power electronics
  • Consumer and industrial electronics
  • Automotive and e-mobility

Produktempfehlungen

Produkte
Technische Daten
dynamische Viskosität Penetration
WACKER SilGel® 610 A/B 7500.0 mPa·s[1] 7500.0 mPa·s[1] 50 - 65 1/10mm[3] 50 - 65 1/10mm[3]
WACKER SilGel® 612 A/B 1000 mPa·s[2] 1000 mPa·s[2] 300 1/10mm[4] 300 1/10mm[4]
WACKER SilGel® 612 EH A/B 1000 mPa·s[1] 1000 mPa·s[1] 150 1/10mm[5] 150 1/10mm[5]
WACKER SilGel® 613 - - 70 1/10mm[6] 70 1/10mm[6]
WACKER SilGel® 616 A/B 300 mPa·s[2] 300 mPa·s[2] 280.0 1/10mm[7] 280.0 1/10mm[7]
Legend
[1] dynamische Viskosität | 25 °C | DIN EN ISO 3219,  [2] dynamische Viskosität | 25 °C | ISO 3219,  [3] Penetration | DIN ISO 2137 | quarter cone, 9.38g, 5 sec.,  [4] Penetration (150 g Hohlkegel) | DIN ISO 2137 | 150 g hollow cone, 1 min.,  [5] Penetration | DIN ISO 2137 | 150 g hollow cone, 1 min.,  [6] Penetration Hohlkonus, 9.38 g | DIN ISO 2137,  [7] Penetration | DIN ISO 2137 | 150 g hollow cone, 60 sec.