Moldmaking & Prototype Molding
ELASTOSIL® RTV-2 silicone elastomers for mold making yield highly accurate reproductions, exhibit good release properties and are highly resistant to common reproduction materials. Applications of ELASTOSIL® M and RT range from arts and crafts to industrial mass production.
Industrial Printing
WACKER offers a high-quality product range of ELASTOSIL® RT silicone rubber grades for pad printing processes of all types. Anti-static variants for printing on sensitive materials and additional ELASTOSIL® systems round off our portfolio of high-performance products.
More about
English
Download
Produktempfehlungen
Tabelle ist scrollbar
|
Produkte
|
Technische Daten
|
Produktmerkmale
|
||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| dynamische Viskosität | Viscosity, dynamic | Weiterreißwiderstand | Härte Shore A | Härte Shore 00 | Reißfestigkeit | Reißdehnung | Beständigkeit | Oberflächeneigenschaft | Regulatorisch | Rheologie | Vernetzungseigenschaft | Vulkanisat | ||
| - - | 3000 mPa·s[1] 3000 mPa·s[1] | 15 N/mm[16] 15 N/mm[16] | 10[19] 10[19] | - - | 3.5 N/mm²[21] 3.5 N/mm²[21] | 600 %[24] 600 %[24] | - | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | 6000 mPa·s[2] 6000 mPa·s[2] | - - | 20[19] 20[19] | - - | 4 N/mm²[21] 4 N/mm²[21] | 500 %[24] 500 %[24] | - | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | 8000 mPa·s[3] 8000 mPa·s[3] | 20 N/mm[16] 20 N/mm[16] | 25[19] 25[19] | - - | 5 N/mm²[21] 5 N/mm²[21] | 450 %[24] 450 %[24] | - | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | 8000 mPa·s[3] 8000 mPa·s[3] | > 20 N/mm[16] > 20 N/mm[16] | 26[19] 26[19] | - - | 5 N/mm²[21] 5 N/mm²[21] | 500 %[24] 500 %[24] | Beständigkeit gegenüber Beton | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| - - | 20000 mPa·s[3] 20000 mPa·s[3] | 25 N/mm[16] 25 N/mm[16] | 25[19] 25[19] | - - | 5 N/mm²[21] 5 N/mm²[21] | 500 %[24] 500 %[24] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber Epoxidharzen | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| - - | - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| - - | 6000 mPa·s[3] 6000 mPa·s[3] | > 20 N/mm[17] > 20 N/mm[17] | 10[19] 10[19] | - - | 4.5 N/mm²[21] 4.5 N/mm²[21] | 950 %[24] 950 %[24] | - | - | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | 5000 mPa·s[4] 5000 mPa·s[4] | 25 N/mm[17] 25 N/mm[17] | 20[19] 20[19] | - - | > 6 N/mm²[21] > 6 N/mm²[21] | > 750 %[24] > 750 %[24] | - | - | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | 10000 mPa·s[4] 10000 mPa·s[4] | 28 N/mm[16] 28 N/mm[16] | 28[19] 28[19] | - - | 6 N/mm²[21] 6 N/mm²[21] | 500 %[24] 500 %[24] | - | - | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | 4000 mPa·s[5] 4000 mPa·s[5] | 5.5 N/mm[17] 5.5 N/mm[17] | - - | 30[26] 30[26] | > 1.5 N/mm²[21] > 1.5 N/mm²[21] | > 900 %[24] > 900 %[24] | - | - | Hautverträglich | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| - - | - - | > 10 N/mm[16] > 10 N/mm[16] | 45[20] 45[20] | - - | 4.5 N/mm²[22] 4.5 N/mm²[22] | 230 %[25] 230 %[25] | hitzebeständig | - | - | knetbar | kondensationsvernetzend, zweikomponentig | - | ||
| 2500 mPa·s[6] 2500 mPa·s[6] | - - | 5 N/mm[16] 5 N/mm[16] | 17[19] 17[19] | - - | 3 N/mm²[21] 3 N/mm²[21] | 400 %[24] 400 %[24] | - | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| 6000 mPa·s[6] 6000 mPa·s[6] | - - | - - | 28[20] 28[20] | - - | 5.0[23] 5.0[23] | 500[25] 500[25] | - | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend, Schnelle Aushärtung bei Raumtemperatur | - | ||
| 350 mPa·s[7] 350 mPa·s[7] | - - | > 4 N/mm[16] > 4 N/mm[16] | 55[19] 55[19] | - - | 3.0 N/mm²[22] 3.0 N/mm²[22] | 130 %[25] 130 %[25] | hitzebeständig, Beständigkeit gegenüber Gießharzen, Beständigkeit gegenüber niederschmelzenden Metallen und Metalllegierungen | - | - | Fließfähig | zweikomponentig, Additionsvernetzend | - | ||
| 30000 mPa·s[8] 30000 mPa·s[8] | - - | > 3 N/mm[16] > 3 N/mm[16] | 23[20] 23[20] | - - | 2 N/mm²[22] 2 N/mm²[22] | 250 %[25] 250 %[25] | - | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 25000 mPa·s[9] 25000 mPa·s[9] | - - | 4.5 N/mm[16] 4.5 N/mm[16] | 37[20] 37[20] | - - | 2.5 N/mm²[22] 2.5 N/mm²[22] | 220 %[25] 220 %[25] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber PU | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 15000 mPa·s[10] 15000 mPa·s[10] | - - | > 4 N/mm[16] > 4 N/mm[16] | 60[20] 60[20] | - - | 4.5 N/mm²[22] 4.5 N/mm²[22] | 120 %[25] 120 %[25] | hitzebeständig | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | wärmeleitfähig | ||
| 40000 mPa·s[11] 40000 mPa·s[11] | - - | > 20 N/mm[16] > 20 N/mm[16] | 25[19] 25[19] | - - | 20 N/mm²[22] 20 N/mm²[22] | 350 %[25] 350 %[25] | - | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 25000 mPa·s[12] 25000 mPa·s[12] | - - | > 18 N/mm[16] > 18 N/mm[16] | 12[20] 12[20] | - - | 3.5 N/mm²[22] 3.5 N/mm²[22] | 600 %[25] 600 %[25] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber PU | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 30000 mPa·s[12] 30000 mPa·s[12] | - - | > 24 N/mm[16] > 24 N/mm[16] | 20[20] 20[20] | - - | 3.5 N/mm²[22] 3.5 N/mm²[22] | 500 %[25] 500 %[25] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber PU | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 35000 mPa·s[11] 35000 mPa·s[11] | - - | > 25 N/mm[16] > 25 N/mm[16] | 25[19] 25[19] | - - | 4.5 N/mm²[22] 4.5 N/mm²[22] | 450 %[25] 450 %[25] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber PU | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 40000 mPa·s[11] 40000 mPa·s[11] | - - | > 30 N/mm[16] > 30 N/mm[16] | 32[20] 32[20] | - - | 5 N/mm²[22] 5 N/mm²[22] | 400 %[25] 400 %[25] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber PU | - | - | Fließfähig | kondensationsvernetzend, zweikomponentig | - | ||
| 20000 mPa·s[11] 20000 mPa·s[11] | - - | > 20 N/mm[16] > 20 N/mm[16] | 20[20] 20[20] | - - | 7[22] 7[22] | 800 %[25] 800 %[25] | - | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 15000 mPa·s[11] 15000 mPa·s[11] | - - | > 30 N/mm[16] > 30 N/mm[16] | 28[20] 28[20] | - - | 6.5 N/mm²[22] 6.5 N/mm²[22] | 700 %[25] 700 %[25] | Beständigkeit gegenüber Gießharzen | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 15000 mPa·s[11] 15000 mPa·s[11] | - - | > 30 N/mm[16] > 30 N/mm[16] | 28[20] 28[20] | - - | 6.5 N/mm²[22] 6.5 N/mm²[22] | 700 %[25] 700 %[25] | Beständigkeit gegenüber Beton, Beständigkeit gegenüber Gießharzen | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 20000 mPa·s[11] 20000 mPa·s[11] | - - | > 30 N/mm[16] > 30 N/mm[16] | 37[20] 37[20] | - - | 7 N/mm²[22] 7 N/mm²[22] | 480 %[25] 480 %[25] | Beständigkeit gegenüber Beton, Beständigkeit gegenüber Gießharzen | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 50000 mPa·s[13] 50000 mPa·s[13] | - - | > 25 N/mm[16] > 25 N/mm[16] | 43[20] 43[20] | - - | > 4.5 N/mm²[22] > 4.5 N/mm²[22] | > 300 %[25] > 300 %[25] | Beständigkeit gegenüber PU | Trockene Oberfläche | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | hochtransparent | ||
| 20000 mPa·s[11] 20000 mPa·s[11] | - - | > 30 N/mm[16] > 30 N/mm[16] | 37[20] 37[20] | - - | 7 N/mm²[22] 7 N/mm²[22] | 480 %[25] 480 %[25] | Beständigkeit gegenüber Gießharzen | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 40000 mPa·s[11] 40000 mPa·s[11] | - - | > 10 N/mm[16] > 10 N/mm[16] | 48[20] 48[20] | - - | 5 N/mm²[22] 5 N/mm²[22] | 300 %[25] 300 %[25] | Beständigkeit gegenüber Gießharzen | - | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 70000 mPa·s[11] 70000 mPa·s[11] | - - | > 25 N/mm[16] > 25 N/mm[16] | 40[20] 40[20] | - - | 5.5 N/mm²[22] 5.5 N/mm²[22] | 400 %[25] 400 %[25] | Beständigkeit gegenüber PU | Leicht ölausschwitzend | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | hochtransparent | ||
| 50000 mPa·s[11] 50000 mPa·s[11] | - - | > 28 N/mm[16] > 28 N/mm[16] | 40[20] 40[20] | - - | 5 N/mm²[22] 5 N/mm²[22] | 330 %[25] 330 %[25] | Beständigkeit gegenüber PU | Stark ölausschwitzend | - | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | hochtransparent | ||
| 120000 mPa·s[11] 120000 mPa·s[11] | - - | 15 N/mm[16] 15 N/mm[16] | 55[19] 55[19] | - - | 5.5 N/mm²[21] 5.5 N/mm²[21] | 280 %[24] 280 %[24] | Beständigkeit gegenüber Polyester, Beständigkeit gegenüber Epoxidharzen, Beständigkeit gegenüber PU | Trockene Oberfläche | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 300000 - 400000 mPa·s[14] 300000 - 400000 mPa·s[14] | - - | > 7 N/mm[16] > 7 N/mm[16] | 55[20] 55[20] | - - | 4.5 N/mm²[22] 4.5 N/mm²[22] | 170 %[25] 170 %[25] | - | - | - | Streichbar - selbstnivellierend | kondensationsvernetzend, zweikomponentig, Schnelle Aushärtung bei Raumtemperatur | - | ||
| 25000 mPa·s[10] 25000 mPa·s[10] | - - | 30 N/mm[16] 30 N/mm[16] | 25[19] 25[19] | - - | 6.5 N/mm²[21] 6.5 N/mm²[21] | 600 %[24] 600 %[24] | - | - | - | Fließfähig | zweikomponentig, Additionsvernetzend | - | ||
| 110000 mPa·s[6] 110000 mPa·s[6] | - - | 12 N/mm[16] 12 N/mm[16] | 53[19] 53[19] | - - | 5 N/mm²[21] 5 N/mm²[21] | 280 %[24] 280 %[24] | Beständigkeit gegenüber Gießharzen | - | - | Fließfähig | zweikomponentig, Additionsvernetzend | - | ||
| - - | - - | > 3 N/mm[18] > 3 N/mm[18] | 45[20] 45[20] | - - | 2 N/mm²[22] 2 N/mm²[22] | 130 %[25] 130 %[25] | - | - | - | - | kondensationsvernetzend, zweikomponentig | - | ||
| 5.000 mPa·s[15] 5.000 mPa·s[15] | - - | 15[16] 15[16] | 15[19] 15[19] | - - | 6.5 N/mm²[21] 6.5 N/mm²[21] | 900 %[24] 900 %[24] | - | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| 15.000 mPa·s[15] 15.000 mPa·s[15] | - - | 15 N/mm[16] 15 N/mm[16] | 40[19] 40[19] | - - | 8 N/mm²[21] 8 N/mm²[21] | 450 %[24] 450 %[24] | - | - | Lebensmittelkontakt | Fließfähig | kein chemischer Schrumpf, zweikomponentig, Additionsvernetzend | - | ||
| - - | - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
Legend
[1] Viscosity, dynamic | Brookfield, [2] Viscosity, dynamic 23°C | ISO 3219, [3] Viscosity, dynamic | 23 °C | ISO 3219, [4] Viscosity, dynamic after stirring | 23 °C | ISO 3219, [5] Viscosity, dynamic aufgerührt | 23 °C | ISO 3219, [6] dynamische Viskosität | 23 °C | ISO 3219, [7] dynamische Viskosität nach Aufrühren | 23 °C , [8] dynamische Viskosität nach Aufrühren | 23 °C | DIN EN ISO 3219, [9] dynamische Viskosität after stirring | 23 °C | DIN EN ISO 3219, [10] dynamische Viskosität after stirring | 23 °C | ISO 3219, [11] dynamische Viskosität aufgerührt | 23 °C | ISO 3219, [12] dynamische Viskosität aufgerührt | 23 °C | DIN EN ISO 3219, [13] dynamische Viskosität nach Umrühren | 23 °C | ISO 3219, [14] dynamische Viskosität | 23 °C | Brookfield, [15] dynamische Viskosität 23°C | ISO 3219, [16] Weiterreißwiderstand | ASTM D 624 B, [17] Weiterreißwiderstand | ASTM D 624, Die B, [18] Weiterreißwiderstand | ASTM 624 B, [19] Härte Shore A | DIN ISO 48-4, [20] Härte Shore A | ISO 868, [21] Reißfestigkeit | ISO 37 Type 1, [22] Reißfestigkeit | ISO 37, [23] Reißfestigkeit | DIN ISO 37, [24] Reißdehnung | ISO 37 Type 1, [25] Reißdehnung | ISO 37, [26] Härte Shore 00 | ASTM D 2240
[1] Viscosity, dynamic | Brookfield, [2] Viscosity, dynamic 23°C | ISO 3219, [3] Viscosity, dynamic | 23 °C | ISO 3219, [4] Viscosity, dynamic after stirring | 23 °C | ISO 3219, [5] Viscosity, dynamic aufgerührt | 23 °C | ISO 3219, [6] dynamische Viskosität | 23 °C | ISO 3219, [7] dynamische Viskosität nach Aufrühren | 23 °C , [8] dynamische Viskosität nach Aufrühren | 23 °C | DIN EN ISO 3219, [9] dynamische Viskosität after stirring | 23 °C | DIN EN ISO 3219, [10] dynamische Viskosität after stirring | 23 °C | ISO 3219, [11] dynamische Viskosität aufgerührt | 23 °C | ISO 3219, [12] dynamische Viskosität aufgerührt | 23 °C | DIN EN ISO 3219, [13] dynamische Viskosität nach Umrühren | 23 °C | ISO 3219, [14] dynamische Viskosität | 23 °C | Brookfield, [15] dynamische Viskosität 23°C | ISO 3219, [16] Weiterreißwiderstand | ASTM D 624 B, [17] Weiterreißwiderstand | ASTM D 624, Die B, [18] Weiterreißwiderstand | ASTM 624 B, [19] Härte Shore A | DIN ISO 48-4, [20] Härte Shore A | ISO 868, [21] Reißfestigkeit | ISO 37 Type 1, [22] Reißfestigkeit | ISO 37, [23] Reißfestigkeit | DIN ISO 37, [24] Reißdehnung | ISO 37 Type 1, [25] Reißdehnung | ISO 37, [26] Härte Shore 00 | ASTM D 2240