Machine Building

Adhesives used in machine building have to meet a large range of requirements. While high heat or chemical resistance are desirable for some applications, others may need special electrical properties or short curing cycles. With their outstanding property profiles, tailor-made ELASTOSIL®, SilGel® or SILRES® products master even the most sophisticated machine building requirements. What’s more, they are ecologically and physiologically safe and can also be used in food-contact applications on a case-by-case basis.

Machine Building

Properties:

  • Heat resistance (up to 300 °C)
  • Adhesion without pretreatment
  • Chemical resistance
  • Stable electrical properties
  • Thermally conductive (from up to 2.5 W x K–1 x m–1)
  • Radiation resistance (from microwave to UV range)
  • Permanent elasticity (-45 °C to over 200 °C)

Produktempfehlungen

Tabelle ist scrollbar
Produkte
Technische Daten
Produktmerkmale
Härte Shore A Reißfestigkeit Reißdehnung Viscosity, dynamic Tear strength Hardness Shore A Beständigkeit Regulatorisch Rheologie Vernetzungseigenschaft Vulkanisat
ELASTOSIL® A234 WHITE - - 2.5 N/mm²[12] 2.5 N/mm²[12] 200 %[17] 200 %[17] 25000 mPa·s[3] 25000 mPa·s[3] 3.5 N/mm[1] 3.5 N/mm[1] 35[9] 35[9] hitzebeständig - - - -
ELASTOSIL® A316 - - 0.8 N/mm²[12] 0.8 N/mm²[12] 200 %[17] 200 %[17] - - - - 15[9] 15[9] - - - - -
ELASTOSIL® A33 IVORY - - 2.5 N/mm²[12] 2.5 N/mm²[12] 300 %[17] 300 %[17] 1000000 mPa·s[4] 1000000 mPa·s[4] 7.8 N/mm[2] 7.8 N/mm[2] 28[9] 28[9] ölbeständig - standfest - -
ELASTOSIL® A59 GRAY - - 1.2 N/mm²[12] 1.2 N/mm²[12] 300 %[17] 300 %[17] 40000 mPa·s[5] 40000 mPa·s[5] 3.0 N/mm[1] 3.0 N/mm[1] 20[9] 20[9] ölbeständig, hitzebeständig - Selbstnivellierend - -
ELASTOSIL® E10 ROT - - 2.5 N/mm²[13] 2.5 N/mm²[13] 300 %[18] 300 %[18] - - 8.0 N/mm[1] 8.0 N/mm[1] 25[9] 25[9] hitzebeständig lösemittelfrei Fließfähig - -
ELASTOSIL® E14 Red - - 2.5 N/mm²[12] 2.5 N/mm²[12] 400 %[17] 400 %[17] - - 7 N/mm[1] 7 N/mm[1] 32[9] 32[9] hitzebeständig MIL-A 46106 Type standfest - -
ELASTOSIL® E303 TRANSLUZENT - - 5 N/mm²[14] 5 N/mm²[14] 400 %[19] 400 %[19] - - - - 30[9] 30[9] - lösemittelhaltig - - -
ELASTOSIL® E4 - - 2 N/mm²[15] 2 N/mm²[15] 750 %[20] 750 %[20] - - 7.3 N/mm[1] 7.3 N/mm[1] 15[9] 15[9] - - standfest - -
ELASTOSIL® E41 TRANSPARENT - - 6.0 N/mm²[15] 6.0 N/mm²[15] 350 %[20] 350 %[20] 100000 mPa·s[6] 100000 mPa·s[6] 11.5 N/mm[1] 11.5 N/mm[1] 40[9] 40[9] - - Selbstnivellierend - -
ELASTOSIL® E43 BLACK - - 6.5 N/mm²[16] 6.5 N/mm²[16] 500 %[21] 500 %[21] 250000 mPa·s[3] 250000 mPa·s[3] 11.5 N/mm[1] 11.5 N/mm[1] 30[9] 30[9] - lösemittelfrei - - -
ELASTOSIL® E43 N BLACK - - 7.5 N/mm²[12] 7.5 N/mm²[12] 500 %[17] 500 %[17] - - - - 30[9] 30[9] - - thixotropierend - -
ELASTOSIL® E43 N TRANSPARENT - - 7.8 N/mm²[12] 7.8 N/mm²[12] 450 %[17] 450 %[17] - - - - 30[9] 30[9] - - thixotropierend - -
ELASTOSIL® E43 TRANSPARENT - - 6.50 N/mm²[15] 6.50 N/mm²[15] 500 %[20] 500 %[20] 250000 mPa·s[7] 250000 mPa·s[7] 11.5 N/mm[1] 11.5 N/mm[1] 30[9] 30[9] - lösemittelfrei - - -
ELASTOSIL® E47 TRANSPARENT - - 4.5 N/mm²[16] 4.5 N/mm²[16] 450 %[21] 450 %[21] 600000 mPa·s[7] 600000 mPa·s[7] 10 N/mm[1] 10 N/mm[1] 37[9] 37[9] - MIL-A 46106 Type standfest, thixotropierend - -
ELASTOSIL® E50 N TRANSPARENT - - 2.6 N/mm²[12] 2.6 N/mm²[12] 200 %[17] 200 %[17] - - - - 35[9] 35[9] - MIL-A 46106 Type - - -
ELASTOSIL® E60 N BLACK - - 2.1 N/mm²[12] 2.1 N/mm²[12] 200 %[17] 200 %[17] - - - - 30[9] 30[9] - - - - -
ELASTOSIL® E60 N GREY - - 3.0 N/mm²[12] 3.0 N/mm²[12] 250 %[17] 250 %[17] - - - - 32[9] 32[9] - - - - -
ELASTOSIL® E60 N RED - - 3.2 N/mm²[12] 3.2 N/mm²[12] 250 %[17] 250 %[17] - - - - 32[9] 32[9] - - - - -
ELASTOSIL® N 2010 - - 1 N/mm²[13] 1 N/mm²[13] 200 %[19] 200 %[19] 10.000 mPa·s[8] 10.000 mPa·s[8] - - 25[9] 25[9] - - Scherverdünnend, Selbstnivellierend - -
ELASTOSIL® N 2034 35[10] 35[10] 2 N/mm²[13] 2 N/mm²[13] 200 %[19] 200 %[19] 30000 mPa·s[7] 30000 mPa·s[7] - - - - - schwer entflammbar - - -
ELASTOSIL® N 2076 36[10] 36[10] 1.6 N/mm²[12] 1.6 N/mm²[12] 150 %[17] 150 %[17] - - - - - - - schwer entflammbar Fließfähig - -
ELASTOSIL® N 2189 45[10] 45[10] 1.5 N/mm²[13] 1.5 N/mm²[13] 200 %[19] 200 %[19] 250000 mPa·s[7] 250000 mPa·s[7] 5.0 N/mm[1] 5.0 N/mm[1] - - ölbeständig, hitzebeständig schwer entflammbar standfest - -
ELASTOSIL® N 2199 30[10] 30[10] 2.5 N/mm²[13] 2.5 N/mm²[13] 400 %[19] 400 %[19] 950000 mPa·s[3] 950000 mPa·s[3] 6.5 N/mm[1] 6.5 N/mm[1] - - - - standfest - -
ELASTOSIL® N9111 BLACK 30[10] 30[10] 2.0 N/mm²[13] 2.0 N/mm²[13] 450 %[18] 450 %[18] 1000000 mPa·s[7] 1000000 mPa·s[7] 8.5 N/mm[2] 8.5 N/mm[2] - - - schwer entflammbar standfest, thixotropierend - -
ELASTOSIL® N9111 GREY 30[10] 30[10] 2.2 N/mm²[13] 2.2 N/mm²[13] 500 %[18] 500 %[18] 1000000 mPa·s[7] 1000000 mPa·s[7] 10 N/mm[2] 10 N/mm[2] - - - - standfest, thixotropierend - -
ELASTOSIL® N9111 WHITE 30[10] 30[10] 2.20 N/mm²[13] 2.20 N/mm²[13] 500 %[18] 500 %[18] 900000 mPa·s[3] 900000 mPa·s[3] 10 N/mm[2] 10 N/mm[2] - - - schwer entflammbar standfest, thixotropierend - -
ELASTOSIL® N9189 45[10] 45[10] 2.8 N/mm²[12] 2.8 N/mm²[12] 330 %[17] 330 %[17] - - - - - - hitzebeständig - Scherverdünnend, standfest - -
ELASTOSIL® RT 702 40[10] 40[10] 6.1 N/mm²[12] 6.1 N/mm²[12] 500 %[17] 500 %[17] - - 10.1[1] 10.1[1] - - hitzebeständig - thixotropierend einkomponentig selbsthaftend
ELASTOSIL® RT 723 A/B - - 5.9 N/mm²[12] 5.9 N/mm²[12] 500 %[17] 500 %[17] 600000 mPa·s[4] 600000 mPa·s[4] 13.8 N/mm[1] 13.8 N/mm[1] - - medienbeständig, hitzebeständig, UV-stabil - - Schnelle Aushärtung unter Hitze, zweikomponentig, Additionsvernetzend -
ELASTOSIL® RT 771 45[10] 45[10] 1 N/mm²[12] 1 N/mm²[12] 180 %[17] 180 %[17] - - - - - - medienbeständig - Scherverdünnend, thixotropierend kondensationsvernetzend, zweikomponentig selbsthaftend, elektrisch isolierend
ELASTOSIL® RT 772 32[10] 32[10] 2.0 N/mm²[12] 2.0 N/mm²[12] 130 %[17] 130 %[17] - - 3.8 N/mm[1] 3.8 N/mm[1] - - hitzebeständig, dampfbeständig - - kondensationsvernetzend, zweikomponentig selbsthaftend, elektrisch isolierend
ELASTOSIL® RT 778 50[10] 50[10] 3.5 N/mm²[12] 3.5 N/mm²[12] 120 %[17] 120 %[17] - - 7.0[1] 7.0[1] - - hitzebeständig - Scherverdünnend, standfest kondensationsvernetzend, zweikomponentig, Schnelle Aushärtung bei Raumtemperatur selbsthaftend, elektrisch isolierend
ELASTOSIL® RT 779 50[11] 50[11] 2.8 N/mm²[12] 2.8 N/mm²[12] 250 %[17] 250 %[17] - - 9.5 N/mm[1] 9.5 N/mm[1] - - ölbeständig - Scherverdünnend, thixotropierend, standfest kondensationsvernetzend, zweikomponentig selbsthaftend, elektrisch isolierend
Legend
[1] Tear strength | ASTM D 624 B,  [2] Tear strength | ASTM D 624 B | 23°C / 2mm,  [3] Viscosity, dynamic D = 0,5 1/s | 25 °C | DIN EN ISO 3219,  [4] Viscosity, dynamic | 25 °C | 0.5 1/s | DIN EN ISO 3219,  [5] Viscosity, dynamic | 25 °C | DIN EN ISO 3219,  [6] Viscosity, dynamic D = 1 1/s | 25 °C | DIN EN ISO 3219,  [7] Viscosity, dynamic D = 0.5 1/s | 25 °C | DIN EN ISO 3219,  [8] Viscosity, dynamic | 25 1/s | ISO 3219,  [9] Hardness Shore A | DIN ISO 48-4,  [10] Härte Shore A | DIN ISO 48-4,  [11] Härte Shore A | ISO 1183-1 A,  [12] Reißfestigkeit | ISO 37 Type 1,  [13] Reißfestigkeit | ISO 37 | Type 3 / 23°C / 2mm,  [14] Reißfestigkeit | ISO 37 | Type 3 / 23 °C / d = 2 mm,  [15] Reißfestigkeit | ISO 37 Type 1 | Type 3 / 23°C / 2mm,  [16] Reißfestigkeit | ISO 37 Type 1 | Type 3 /23°C / 2mm,  [17] Reißdehnung | ISO 37 Type 1,  [18] Reißdehnung | ISO 37 | Type 3 / 23°C / 2mm,  [19] Reißdehnung | ISO 37,  [20] Reißdehnung | ISO 37 Type 1 | Type 3 / 23°C / 2mm,  [21] Reißdehnung | ISO 37 Type 1 | Type 3 /23°C / 2mm,  [] Geeignet,  [] Gut geeignet,  [] Ideal geeignet