Tapes & Electronics

Release liners are essential for adhesive tapes: they protect the self-adhesive material right up to the final application and make it easier to process. Release liners are indispensable process aids for bonding electronic components.
Release coatings from WACKER give release liners ideal properties such as:
- Minimal migration
- Stable release forces even for aggressive adhesives
- Precisely adjustable release forces
- Good anchorage to a number of substrates
Product Recommendations
Products
|
Technical data
|
Product properties
|
|||
---|---|---|---|---|---|
Viscosity, dynamic | Content | Product Type | Specific Features | ||
approx. 600 mPa·s[1] approx. 600 mPa·s[1] | - - | Controlled Release Additive | Solvent-free | ||
approx. 3 mPa·s[1] approx. 3 mPa·s[1] | - - | Controlled Release Additive | Solvent-based | ||
approx. 600 mPa·s[1] approx. 600 mPa·s[1] | - - | Controlled Release Additive | Solvent-free | ||
approx. 525 mPa·s[1] approx. 525 mPa·s[1] | 100 %[2] 100 %[2] | Polymer | Solvent-free | ||
approx. 215 mPa·s[1] approx. 215 mPa·s[1] | 100 %[2] 100 %[2] | Polymer | Solvent-free | ||
approx. 20000 mPa·s[1] approx. 20000 mPa·s[1] | 30 %[3] 30 %[3] | Polymer | Solvent-based | ||
approx. 1200 mPa·s[1] approx. 1200 mPa·s[1] | 55 %[3] 55 %[3] | Polymer | Solvent-based | ||
approx. 350 mPa·s[1] approx. 350 mPa·s[1] | 100 %[2] 100 %[2] | Polymer | Solvent-free | ||
approx. 525 mPa·s[1] approx. 525 mPa·s[1] | 100 %[2] 100 %[2] | Polymer | Solvent-free | ||
approx. 210 mPa·s[1] approx. 210 mPa·s[1] | 100 %[2] 100 %[2] | Polymer | Solvent-free | ||
approx. 565 mPa·s[1] approx. 565 mPa·s[1] | approx. 0.115 %[4] approx. 0.115 %[4] | Catalyst | Solvent-free | ||
approx. 565 mPa·s[1] approx. 565 mPa·s[1] | approx. 0.115 %[4] approx. 0.115 %[4] | Catalyst | Solvent-free | ||
approx. 850 mPa·s[1] approx. 850 mPa·s[1] | approx. 1.00 %[4] approx. 1.00 %[4] | Catalyst | Solvent-free | ||
approx. 850 mPa·s[1] approx. 850 mPa·s[1] | approx. 1.00 %[4] approx. 1.00 %[4] | Catalyst | Solvent-free | ||
approx. 22 mPa·s[1] approx. 22 mPa·s[1] | 100 % 100 % | Crosslinker | Solvent-free | ||
approx. 30 mPa·s[1] approx. 30 mPa·s[1] | 100 % 100 % | Crosslinker | Solvent-free | ||
approx. 40 mPa·s[1] approx. 40 mPa·s[1] | 100 % 100 % | Crosslinker | Solvent-free | ||
approx. 22 mPa·s[1] approx. 22 mPa·s[1] | 100 % 100 % | Crosslinker | Solvent-free | ||
approx. 30 mPa·s[1] approx. 30 mPa·s[1] | 100 % 100 % | Crosslinker | Solvent-free | ||
approx. 40 mPa·s[1] approx. 40 mPa·s[1] | 100 % 100 % | Crosslinker | Solvent-free |
[1] Viscosity, dynamic | 25 °C , [2] Content of active agent, [3] Solid content, [4] Platinum content, [] Suited, [] Well suited, [] Ideally suited