供手工业和工业复制模具使用的ELASTOSIL® M硅橡胶
几十年以来， ELASTOSIL® M硅橡胶一直是生产具有高弹性、出色脱模性和最佳耐久性的成型制品的理想解决方案。凭借其卓越的加工性能，ELASTOSIL® M硅橡胶对工业模具和艺术模具生产商而言都不可或缺。
Product Recommendations
Table is scrollable
|
Products
|
Technical data
|
Product properties
|
|||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 动态粘度 | Tear-growth resistance | Shore density A | Breaking strength | Tensile strength | Elongation at break | Resistance | Surface property | Regulation | Product Rheology | Crosslinking Property | Vulcanizate | ||
| 3000 mPa·s[1] 3000 mPa·s[1] | 15 N/mm[10] 15 N/mm[10] | 10[13] 10[13] | 3.5 N/mm²[15] 3.5 N/mm²[15] | - - | 600 %[20] 600 %[20] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 6000 mPa·s[2] 6000 mPa·s[2] | - - | 20[13] 20[13] | 4 N/mm²[15] 4 N/mm²[15] | - - | 500 %[20] 500 %[20] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 8000 mPa·s[3] 8000 mPa·s[3] | 20 N/mm[10] 20 N/mm[10] | 25[13] 25[13] | 5 N/mm²[15] 5 N/mm²[15] | - - | 450 %[20] 450 %[20] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 8000 mPa·s[3] 8000 mPa·s[3] | > 20 N/mm[10] > 20 N/mm[10] | 26[13] 26[13] | 5 N/mm²[15] 5 N/mm²[15] | - - | 500 %[20] 500 %[20] | Resistance against concrete | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 6000 mPa·s[3] 6000 mPa·s[3] | > 20 N/mm[11] > 20 N/mm[11] | 10[13] 10[13] | 4.5 N/mm²[15] 4.5 N/mm²[15] | - - | 950 %[20] 950 %[20] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| - - | > 10 N/mm[10] > 10 N/mm[10] | 45[14] 45[14] | 4.5 N/mm²[16] 4.5 N/mm²[16] | - - | 230 %[21] 230 %[21] | Heat resistant | - | - | Kneadable | Condensation-curing, Two-component | - | ||
| 2500 mPa·s[3] 2500 mPa·s[3] | 5 N/mm[10] 5 N/mm[10] | 17[13] 17[13] | 3 N/mm²[15] 3 N/mm²[15] | - - | 400 %[20] 400 %[20] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 6000 mPa·s[3] 6000 mPa·s[3] | - - | 28[14] 28[14] | 5.0[17] 5.0[17] | - - | 500[21] 500[21] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 350 mPa·s[4] 350 mPa·s[4] | > 4 N/mm[10] > 4 N/mm[10] | 55[13] 55[13] | 3.0 N/mm²[16] 3.0 N/mm²[16] | - - | 130 %[21] 130 %[21] | Heat resistant, Resistance against casting resins, Resistance against low melting metals and metal alloys | - | - | Flowable | Two-component, Addition Curing | - | ||
| 30000 mPa·s[5] 30000 mPa·s[5] | > 3 N/mm[10] > 3 N/mm[10] | 23[14] 23[14] | 2 N/mm²[16] 2 N/mm²[16] | - - | 250 %[21] 250 %[21] | - | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 25000 mPa·s[5] 25000 mPa·s[5] | 4.5 N/mm[10] 4.5 N/mm[10] | 37[14] 37[14] | 2.5 N/mm²[16] 2.5 N/mm²[16] | - - | 220 %[21] 220 %[21] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 15000 mPa·s[6] 15000 mPa·s[6] | > 4 N/mm[10] > 4 N/mm[10] | 60[14] 60[14] | 4.5 N/mm²[16] 4.5 N/mm²[16] | - - | 120 %[21] 120 %[21] | Heat resistant | - | - | Flowable | Condensation-curing, Two-component | Thermally conductive | ||
| 40000 mPa·s[6] 40000 mPa·s[6] | > 20 N/mm[10] > 20 N/mm[10] | 25[13] 25[13] | 20 N/mm²[16] 20 N/mm²[16] | - - | 350 %[21] 350 %[21] | - | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 25000 mPa·s[5] 25000 mPa·s[5] | > 18 N/mm[10] > 18 N/mm[10] | 12[14] 12[14] | 3.5 N/mm²[16] 3.5 N/mm²[16] | - - | 600 %[21] 600 %[21] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 30000 mPa·s[5] 30000 mPa·s[5] | > 24 N/mm[10] > 24 N/mm[10] | 20[14] 20[14] | 3.5 N/mm²[16] 3.5 N/mm²[16] | - - | 500 %[21] 500 %[21] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 35000 mPa·s[6] 35000 mPa·s[6] | > 25 N/mm[10] > 25 N/mm[10] | 25[13] 25[13] | 4.5 N/mm²[16] 4.5 N/mm²[16] | - - | 450 %[21] 450 %[21] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 40000 mPa·s[6] 40000 mPa·s[6] | > 30 N/mm[10] > 30 N/mm[10] | 32[14] 32[14] | 5 N/mm²[16] 5 N/mm²[16] | - - | 400 %[21] 400 %[21] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 20000 mPa·s[6] 20000 mPa·s[6] | > 20 N/mm[10] > 20 N/mm[10] | 20[14] 20[14] | 7[16] 7[16] | - - | 800 %[21] 800 %[21] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 15000 mPa·s[6] 15000 mPa·s[6] | > 30 N/mm[10] > 30 N/mm[10] | 28[14] 28[14] | 6.5 N/mm²[16] 6.5 N/mm²[16] | - - | 700 %[21] 700 %[21] | Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 20000 mPa·s[6] 20000 mPa·s[6] | > 30 N/mm[10] > 30 N/mm[10] | 37[14] 37[14] | 7 N/mm²[16] 7 N/mm²[16] | - - | 480 %[21] 480 %[21] | Resistance against casting resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 40000 mPa·s[6] 40000 mPa·s[6] | > 10 N/mm[10] > 10 N/mm[10] | 48[14] 48[14] | 5 N/mm²[16] 5 N/mm²[16] | - - | 300 %[21] 300 %[21] | Resistance against casting resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 120000 mPa·s[6] 120000 mPa·s[6] | 15 N/mm[10] 15 N/mm[10] | 55[13] 55[13] | - - | 5.5 N/mm²[18] 5.5 N/mm²[18] | 280 %[20] 280 %[20] | Resistance against polyester, Resistance against epoxy resins, Resistance against PU | Dry surface | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 300000 - 400000 mPa·s[7] 300000 - 400000 mPa·s[7] | > 7 N/mm[10] > 7 N/mm[10] | 55[14] 55[14] | - - | 4.5 N/mm²[19] 4.5 N/mm²[19] | 170 %[21] 170 %[21] | - | - | - | Spreadable self-levelling flow | Condensation-curing, Two-component, Fast curing at room temperature | - | ||
| 25000 mPa·s[6] 25000 mPa·s[6] | 30 N/mm[10] 30 N/mm[10] | 25[13] 25[13] | - - | 6.5 N/mm²[18] 6.5 N/mm²[18] | 600 %[20] 600 %[20] | - | - | - | Flowable | Two-component, Addition Curing | - | ||
| 110000 mPa·s[3] 110000 mPa·s[3] | 12 N/mm[10] 12 N/mm[10] | 53[13] 53[13] | - - | 5 N/mm²[18] 5 N/mm²[18] | 280 %[20] 280 %[20] | Resistance against casting resins | - | - | Flowable | Two-component, Addition Curing | - | ||
| - - | > 3 N/mm[12] > 3 N/mm[12] | 45[14] 45[14] | - - | 2 N/mm²[19] 2 N/mm²[19] | 130 %[21] 130 %[21] | - | - | - | - | Condensation-curing, Two-component | - | ||
| 5.000 mPa·s[8] 5.000 mPa·s[8] | 15[10] 15[10] | 15[13] 15[13] | - - | 6.5 N/mm²[18] 6.5 N/mm²[18] | 900 %[20] 900 %[20] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 15.000 mPa·s[9] 15.000 mPa·s[9] | 15 N/mm[10] 15 N/mm[10] | 40[13] 40[13] | - - | 8 N/mm²[18] 8 N/mm²[18] | 450 %[20] 450 %[20] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
Legend
[1] 动态粘度 | Brookfield, [2] 动态粘度 23°C | ISO 3219, [3] 动态粘度 | 23 °C | ISO 3219, [4] 动态粘度 搅拌后 | 23 °C , [5] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219, [6] 动态粘度 after stirring | 23 °C | ISO 3219, [7] 动态粘度 | 23 °C | Brookfield, [8] 动态粘度 23°C, stirred | ISO 3219, [9] 动态粘度 23° C, stirred | ISO 3219, [10] Tear-growth resistance | ASTM D 624 B, [11] Tear-growth resistance | ASTM D 624, Die B, [12] Tear-growth resistance | ASTM 624 B, [13] Shore density A | DIN ISO 48-4, [14] Shore density A | ISO 868, [15] Breaking strength | ISO 37 type 1, [16] Breaking strength | ISO 37, [17] Breaking strength | DIN ISO 37, [18] Tensile strength | ISO 37 type 1, [19] Tensile strength | ISO 37, [20] Elongation at break | ISO 37 type 1, [21] Elongation at break | ISO 37
[1] 动态粘度 | Brookfield, [2] 动态粘度 23°C | ISO 3219, [3] 动态粘度 | 23 °C | ISO 3219, [4] 动态粘度 搅拌后 | 23 °C , [5] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219, [6] 动态粘度 after stirring | 23 °C | ISO 3219, [7] 动态粘度 | 23 °C | Brookfield, [8] 动态粘度 23°C, stirred | ISO 3219, [9] 动态粘度 23° C, stirred | ISO 3219, [10] Tear-growth resistance | ASTM D 624 B, [11] Tear-growth resistance | ASTM D 624, Die B, [12] Tear-growth resistance | ASTM 624 B, [13] Shore density A | DIN ISO 48-4, [14] Shore density A | ISO 868, [15] Breaking strength | ISO 37 type 1, [16] Breaking strength | ISO 37, [17] Breaking strength | DIN ISO 37, [18] Tensile strength | ISO 37 type 1, [19] Tensile strength | ISO 37, [20] Elongation at break | ISO 37 type 1, [21] Elongation at break | ISO 37