医疗
VINNAPAS®威耐实®乳液可以为您面向医疗应用的终端产品提供所需的特定性能。
优势
- 亲水性
- 舒适的棉质触感
- 高透气性
应用
- 手术铺单
Product Recommendations
Table is scrollable
|
Products
|
Technical data
|
Product properties
|
医疗
|
||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Solids content | 外观 | Viscosity, dynamic | Hardness Shore A | Biocompatibility | Tensile strength | Elongation at break | Tear strength | Compression Set | Glass transition temperature | Regulation | Specific Features | Vulcanizate |
Binding of Cellulosic Fibers
|
Soft Hand
|
Hydrophilicity
|
Wet Tensile Strength
|
Drape
|
||
| - - | transparent transparent | - - | 20[1] 20[1] | - - | 5.3 N/mm²[2] 5.3 N/mm²[2] | 720 %[3] 720 %[3] | 11 N/mm[4] 11 N/mm[4] | 25 %[5] 25 %[5] | - - | - | Self-adhesive | - | - | - | - | - | - | ||
| - - | transparent transparent | - - | 30[1] 30[1] | - - | 5.9 N/mm²[2] 5.9 N/mm²[2] | 660 %[3] 660 %[3] | 12 N/mm[4] 12 N/mm[4] | 13 %[5] 13 %[5] | - - | - | Self-adhesive | - | - | - | - | - | - | ||
| - - | transparent transparent | - - | 40[1] 40[1] | - - | 7.6 N/mm²[2] 7.6 N/mm²[2] | 600 %[3] 600 %[3] | 19 N/mm[4] 19 N/mm[4] | 19 %[5] 19 %[5] | - - | - | Self-adhesive | - | - | - | - | - | - | ||
| - - | transparent transparent | - - | 50[1] 50[1] | - - | 8.2 N/mm²[2] 8.2 N/mm²[2] | 490 %[3] 490 %[3] | 21 N/mm[4] 21 N/mm[4] | 15 %[5] 15 %[5] | - - | - | Self-adhesive | - | - | - | - | - | - | ||
| - - | transparent transparent | - - | 60[1] 60[1] | - - | 8.9 N/mm²[2] 8.9 N/mm²[2] | 460 %[3] 460 %[3] | 27 N/mm[4] 27 N/mm[4] | 13 %[5] 13 %[5] | - - | - | Self-adhesive | - | - | - | - | - | - | ||
| - - | transparent transparent | - - | 70[1] 70[1] | - - | 7.7 N/mm²[2] 7.7 N/mm²[2] | 350 %[3] 350 %[3] | 25 N/mm[4] 25 N/mm[4] | 10 %[5] 10 %[5] | - - | - | Self-adhesive | - | - | - | - | - | - | ||
| - - | - - | - - | 27[1] 27[1] | yes[6] yes[6] | - - | - - | - - | - - | - - | Food-contact, Biocompatible | - | Precise, Flexible at low (-40 °C) and high temperatures (+180 °C), Electrically insulating, Gas permeable | - | - | - | - | - | ||
| - - | - - | - - | 27[1] 27[1] | yes[6] yes[6] | - - | - - | - - | - - | - - | Food-contact, Biocompatible | - | Precise, Flexible at low (-40 °C) and high temperatures (+180 °C), Electrically insulating, Gas permeable | - | - | - | - | - | ||
| 52 - 54 % 52 - 54 % | - - | 100 - 600 mPa·s 100 - 600 mPa·s | - - | - - | - - | - - | - - | - - | 约 -11 °C[7] 约 12.2 °F[7] | - | - | - | |||||||
Legend
[1] Hardness Shore A | DIN ISO 48-4, [2] Tensile strength | ISO 37 type 1, [3] Elongation at break | ISO 37 type 1, [4] Tear strength | ASTM D 624 B, [5] Compression Set | 22 h | 125 °C | DIN ISO 815-1 type B method A, [6] Biocompatibility (USP class VI) | ISO 10993, [7] Glass transition temperature | specific method, [] Suited, [] Well suited, [] Ideally suited
[1] Hardness Shore A | DIN ISO 48-4, [2] Tensile strength | ISO 37 type 1, [3] Elongation at break | ISO 37 type 1, [4] Tear strength | ASTM D 624 B, [5] Compression Set | 22 h | 125 °C | DIN ISO 815-1 type B method A, [6] Biocompatibility (USP class VI) | ISO 10993, [7] Glass transition temperature | specific method, [] Suited, [] Well suited, [] Ideally suited