建筑装饰成型
要获得外形精美、结构稳定的混凝土和人造石铸件，良好的耐碱性、平整和不平整表面复制的有效性以及最终产品的长期耐久性都不可或缺。在这方面，加成固化ELASTOSIL® M系列产品被视为行业基准。
优点：
- 出色的尺寸准确性/无收缩
- 无需添加离型剂
- 可制作大量混凝土、人造石或石膏材质的复制品
应用领域：
- 外墙构件、装饰部件
- 用于室内应用的面砖
- 冲压混凝土印章模具
- 瓷砖
- 浴缸、水槽等浴室配件
Product Recommendations
Table is scrollable
|
Products
|
Technical data
|
Product properties
|
||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Viscosity, dynamic | Tear strength | Hardness Shore A | Tensile strength | Elongation at break | Resistance | Regulation | Product Rheology | Crosslinking Property | ||
| 8000 mPa·s[1] 8000 mPa·s[1] | > 20 N/mm[4] > 20 N/mm[4] | 26[6] 26[6] | 5 N/mm²[9] 5 N/mm²[9] | 500 %[11] 500 %[11] | Resistance against concrete | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | ||
| 25000 cP[1] 25000 cP[1] | 31.5 N/mm[4] 31.5 N/mm[4] | 20[7] 20[7] | 7.00 N/mm²[10] 7.00 N/mm²[10] | 800 %[12] 800 %[12] | - | - | - | - | ||
| 15000 mPa·s[2] 15000 mPa·s[2] | > 30 N/mm[4] > 30 N/mm[4] | 28[7] 28[7] | 6.5 N/mm²[10] 6.5 N/mm²[10] | 700 %[12] 700 %[12] | Resistance against concrete, Resistance against casting resins | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | ||
| 20000 mPa·s[2] 20000 mPa·s[2] | > 30 N/mm[4] > 30 N/mm[4] | 37[7] 37[7] | 7 N/mm²[10] 7 N/mm²[10] | 480 %[12] 480 %[12] | Resistance against concrete, Resistance against casting resins | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | ||
| 20000 mPa·s[3] 20000 mPa·s[3] | 170 ppi[5] 170 ppi[5] | 37[7] 37[7] | 950 psi[10] 950 psi[10] | 480 %[12] 480 %[12] | - | - | - | - | ||
| 150000 mPa·s[2] 150000 mPa·s[2] | > 68 lb/in[4] > 68 lb/in[4] | 55[8] 55[8] | 795[10] 795[10] | 300 %[12] 300 %[12] | - | - | - | - | ||
| 14000 mPa·s[3] 14000 mPa·s[3] | 140 ppi[5] 140 ppi[5] | 22[7] 22[7] | 950 psi[10] 950 psi[10] | 580 %[12] 580 %[12] | - | - | Flowable | Fast curing under heat, Two-component, Addition Curing | ||
| 17000 mPa·s[3] 17000 mPa·s[3] | 110 ppi[5] 110 ppi[5] | 30[7] 30[7] | 900 psi[10] 900 psi[10] | 400 %[12] 400 %[12] | - | - | - | - | ||
Legend
[1] Viscosity, dynamic | 23 °C | ISO 3219, [2] Viscosity, dynamic after stirring | 23 °C | ISO 3219, [3] Viscosity, dynamic | 23 °C | Brookfield, [4] Tear strength | ASTM D 624 B, [5] Tear strength | ASTM 624 B, [6] Hardness Shore A | DIN ISO 48-4, [7] Hardness Shore A | ISO 868, [8] Hardness Shore A | ISO 867, [9] Tensile strength | ISO 37 type 1, [10] Tensile strength | ISO 37, [11] Elongation at break | ISO 37 type 1, [12] Elongation at break | ISO 37
[1] Viscosity, dynamic | 23 °C | ISO 3219, [2] Viscosity, dynamic after stirring | 23 °C | ISO 3219, [3] Viscosity, dynamic | 23 °C | Brookfield, [4] Tear strength | ASTM D 624 B, [5] Tear strength | ASTM 624 B, [6] Hardness Shore A | DIN ISO 48-4, [7] Hardness Shore A | ISO 868, [8] Hardness Shore A | ISO 867, [9] Tensile strength | ISO 37 type 1, [10] Tensile strength | ISO 37, [11] Elongation at break | ISO 37 type 1, [12] Elongation at break | ISO 37