SILPURAN® 6610/50 A/B

Liquid silicone rubbers of the SILPURAN® 6610 series are paste-like, two-component compounds. Their vulcanizates are noted for their significantly reduced tendency towards a radical induced reattachment, i.e. healing, of slit valve surfaces during sterilization by gamma irradiation and ebeam (≤ 75 kGy). SILPURAN® 6610/50 A/B is designed for medical applications in compliance with the WACKER SILICONES HEALTH CARE POLICY including implantation for < 30 days.


Eigenschaften

SILPURAN® 6610/50 A/B meets selected test requirements of ISO 10993 and United States Pharmacopoeia (USP) Class VI. It is designed for medical applications in compliance with the WACKER SILICONES HEALTH CARE POLICY including implantation for < 30 days and is particularly suitable for the economical production of large series of injection molded articles.

At service temperatures above approx. 180 °C the addition of heat stabilizers is recommended. Further information about an improvement of the heat stability by use of specific ELASTOSIL® Color Pastes FL can be obtained from the Technical Information Sheet "ELASTOSIL® Color Pastes FL" or the latest edition of our brochures.

Spezifische Merkmale von SILPURAN® 6610/50 A/B

  • Lebensmittelkontakt
  • Reduzierter Flüchtigengehalt
  • weniger selbstheilend

The following studies were performed on vulcanizates of SILPURAN® 6610/50 A/B according to ISO 10993:
    - Cytotoxicity (ISO 10993-5)
    - Sensitation LLNA (ISO 10993-10)
    - Pyrogenicity (ISO 10993-11)

The following studies were performed on vulcanizates of SILPURAN® 6610/50 A/B according to USP class VI:
    - Acute systemic toxicity
    - Intracutaneous toxicity
    - Implantation test
No adverse effects have been detected at any of the studies performed.

Properly cured and post-cured vulcanizates of SILPURAN® 6610/50 A/B can be used for food contact applications and are suitable for use under the Recommendation "XV. Silicones" of the BfR and FDA 21 CFR §177.2600 "Rubber Articles Intended for Repeated Use" considering any given limitations on extractable and volatile substances. Solely contact with acidic foodstuff is not recommended as this might lead to an elution of one type of filler.

The A and B components are delivered ready to use in 20 kg pail kits. With adequate metering equipment, they can be pumped directly from the original containers into the injection molding machine and mixed by a static mixer. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days.
For detailed information please refer to the latest edition of our brochure "SOLID AND LIQUID SILICONE RUBBER - MATERIAL AND PROCESSING GUIDELINES".
 

Verpackung / Gebinde

This product is available in 20 kg pail kits. 
SILPURAN® is neither produced nor packed under sterile conditions, so the final product has to be sterilized prior to use, if necessary.

Lagerung

Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulphur or phosphorus compounds. For detailed information about storage conditions please refer to the latest edition of our brochure "SOLID AND LIQUID SILICONE RUBBER - MATERIAL AND PROCESSING GUIDELINES".
The 'Best use before end' date of each batch is shown on the product label. Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

Vertrieb & Support

Wacker Chemicals Middle East
Dubai Silicon Oasis s/n
0001 Dubai
Vereinigte Arabische Emirate
+971  4  709-9999 (Phone)
+971 4 709-9911  (Fax)
Kontakt

Wie können wir Ihnen helfen?

  • Benötigen Sie Unterstützung bei der Produktauswahl oder wünschen Sie eine technische Beratung? Kontaktieren Sie unsere Experten.
Frage stellen

Sie möchten ein Produktmuster?

Hier können Sie ein Produktmuster anfordern.

Muster anfordern

Mehr Produkte

Produkte Technische Daten
Aussehen Härte Shore A Reißfestigkeit Reißdehnung Weiterreißwiderstand Druckverformungsrest
ELASTOSIL® eco LR 5040/20 A/B slightly bluish slightly bluish 20[1] 20[1] 7,9 N/mm²[2] 7,9 N/mm²[2] 890 %[3] 890 %[3] 33 N/mm[4] 33 N/mm[4] - -
ELASTOSIL® eco LR 5040/30 A/B slightly bluish slightly bluish 30[1] 30[1] 8,6 N/mm²[2] 8,6 N/mm²[2] 860 %[3] 860 %[3] 32 N/mm[4] 32 N/mm[4] - -
ELASTOSIL® eco LR 5040/40 A/B slightly bluish slightly bluish 40[1] 40[1] 9,0 N/mm²[2] 9,0 N/mm²[2] 580 %[3] 580 %[3] 38 N/mm[4] 38 N/mm[4] - -
ELASTOSIL® eco LR 5040/50 A/B slightly bluish slightly bluish 50[1] 50[1] 9,1 N/mm²[2] 9,1 N/mm²[2] 490 %[3] 490 %[3] 54 N/mm[4] 54 N/mm[4] - -
ELASTOSIL® eco LR 5040/60 A/B slightly bluish slightly bluish 60[1] 60[1] 9,0 N/mm²[2] 9,0 N/mm²[2] 380 %[3] 380 %[3] 50 N/mm[4] 50 N/mm[4] - -
ELASTOSIL® eco LR 5040/70 A/B slightly bluish slightly bluish 70[1] 70[1] 9,5 N/mm²[2] 9,5 N/mm²[2] 370 %[3] 370 %[3] 36 N/mm[4] 36 N/mm[4] - -
ELASTOSIL® LR 34004/50 A/B white white 50[1] 50[1] 7,8 N/mm²[2] 7,8 N/mm²[2] 450 %[3] 450 %[3] 26 N/mm[4] 26 N/mm[4] - -
ELASTOSIL® LR 5040/20 A/B slightly bluish slightly bluish 20[1] 20[1] 7,9 N/mm²[2] 7,9 N/mm²[2] 890 %[3] 890 %[3] 33 N/mm[4] 33 N/mm[4] - -
ELASTOSIL® LR 5040/30 A/B slightly bluish slightly bluish 30[1] 30[1] 8,6 N/mm²[2] 8,6 N/mm²[2] 860 %[3] 860 %[3] 32 N/mm[4] 32 N/mm[4] - -
ELASTOSIL® LR 5040/40 A/B slightly bluish slightly bluish 40[1] 40[1] 9,0 N/mm²[2] 9,0 N/mm²[2] 580 %[3] 580 %[3] 38 N/mm[4] 38 N/mm[4] - -
ELASTOSIL® LR 5040/45 A/B slightly bluish slightly bluish 45[1] 45[1] 9,0 N/mm²[2] 9,0 N/mm²[2] 580 %[3] 580 %[3] 41 N/mm[4] 41 N/mm[4] - -
ELASTOSIL® LR 5040/50 A/B slightly bluish slightly bluish 50[1] 50[1] 9,1 N/mm²[2] 9,1 N/mm²[2] 490 %[3] 490 %[3] 54 N/mm[4] 54 N/mm[4] - -
ELASTOSIL® LR 5040/60 A/B slightly bluish slightly bluish 60[1] 60[1] 9,0 N/mm²[2] 9,0 N/mm²[2] 380 %[3] 380 %[3] 50 N/mm[4] 50 N/mm[4] - -
ELASTOSIL® LR 5040/70 A/B slightly bluish slightly bluish 70[1] 70[1] 9,5 N/mm²[2] 9,5 N/mm²[2] 370 %[3] 370 %[3] 36 N/mm[4] 36 N/mm[4] - -
SILPURAN® 6000/05 A/B transparent transparent 5[1] 5[1] 2,5 N/mm²[2] 2,5 N/mm²[2] 700 %[3] 700 %[3] 6 N/mm[4] 6 N/mm[4] - -
SILPURAN® 6000/10 A/B transparent transparent 10[1] 10[1] 4,2 N/mm²[2] 4,2 N/mm²[2] 740 %[3] 740 %[3] 13 N/mm[4] 13 N/mm[4] 15 %[5] 15 %[5]
SILPURAN® 6000/20 A/B transparent transparent 20[1] 20[1] 8,0 N/mm²[2] 8,0 N/mm²[2] 850 %[3] 850 %[3] 21 N/mm[4] 21 N/mm[4] 17 %[5] 17 %[5]
SILPURAN® 6000/30 A/B transparent transparent 30[1] 30[1] 8,6 N/mm²[2] 8,6 N/mm²[2] 650 %[3] 650 %[3] 25 N/mm[4] 25 N/mm[4] 13 %[5] 13 %[5]
SILPURAN® 6000/40 A/B transparent transparent 40[1] 40[1] 9,6 N/mm²[2] 9,6 N/mm²[2] 600 %[3] 600 %[3] 29 N/mm[4] 29 N/mm[4] 11 %[5] 11 %[5]
SILPURAN® 6000/50 A/B transparent transparent 50[1] 50[1] 10,0 N/mm²[2] 10,0 N/mm²[2] 480 %[3] 480 %[3] 30 N/mm[4] 30 N/mm[4] 14 %[5] 14 %[5]
SILPURAN® 6000/60 A/B transparent transparent 60[1] 60[1] 10,0 N/mm²[2] 10,0 N/mm²[2] 350 %[3] 350 %[3] 27 N/mm[4] 27 N/mm[4] 14 %[5] 14 %[5]
SILPURAN® 6000/70 A/B transparent transparent 70[1] 70[1] 9,5 N/mm²[2] 9,5 N/mm²[2] 290 %[3] 290 %[3] 22 N/mm[4] 22 N/mm[4] 11 %[5] 11 %[5]
SILPURAN® 6600/40 A/B transparent transparent 40[1] 40[1] 9,4 N/mm²[2] 9,4 N/mm²[2] 550 %[3] 550 %[3] 32 N/mm[4] 32 N/mm[4] 14 %[5] 14 %[5]
SILPURAN® 6600/50 A/B transparent transparent 50[1] 50[1] 8,9 N/mm²[2] 8,9 N/mm²[2] 440 %[3] 440 %[3] 31 N/mm[4] 31 N/mm[4] 13 %[5] 13 %[5]
SILPURAN® 6600/60 A/B transparent transparent 60[1] 60[1] 9,0 N/mm²[2] 9,0 N/mm²[2] 310 %[3] 310 %[3] 26 N/mm[4] 26 N/mm[4] 14 %[5] 14 %[5]
SILPURAN® 6610/40 A/B white white 40[1] 40[1] 7,2 N/mm²[2] 7,2 N/mm²[2] 510 %[3] 510 %[3] 22 N/mm[4] 22 N/mm[4] 12 %[5] 12 %[5]
SILPURAN® 6610/50 A/B white white 50[1] 50[1] 8,0 N/mm²[2] 8,0 N/mm²[2] 450 %[3] 450 %[3] 25 N/mm[4] 25 N/mm[4] 12 %[5] 12 %[5]
SILPURAN® 6610/60 A/B white white 60[1] 60[1] 7,0 N/mm²[2] 7,0 N/mm²[2] 300 %[3] 300 %[3] 20 N/mm[4] 20 N/mm[4] 15 %[5] 15 %[5]
SILPURAN® 6700/40 A/B transparent transparent 40[1] 40[1] 8,2 N/mm²[2] 8,2 N/mm²[2] 640 %[3] 640 %[3] 23 N/mm[4] 23 N/mm[4] 40 %[6] 40 %[6]
SILPURAN® 6700/50 A/B transparent transparent 50[1] 50[1] 8,5 N/mm²[2] 8,5 N/mm²[2] 590 %[3] 590 %[3] 24 N/mm[4] 24 N/mm[4] 50 %[6] 50 %[6]
SILPURAN® 6700/60 A/B transparent transparent 60[1] 60[1] 9,6 N/mm²[2] 9,6 N/mm²[2] 490 %[3] 490 %[3] 26 N/mm[4] 26 N/mm[4] 60 %[6] 60 %[6]
SILPURAN® 6740/40 A/B transparent transparent 40[1] 40[1] 8,8 N/mm²[2] 8,8 N/mm²[2] 710 %[3] 710 %[3] 27 N/mm[4] 27 N/mm[4] - -
SILPURAN® 6760/50 A/B transparent transparent 50[1] 50[1] 8,4 N/mm²[2] 8,4 N/mm²[2] 600 %[3] 600 %[3] 27 N/mm[4] 27 N/mm[4] - -
Legend
[1] Härte Shore A | DIN ISO 48-4,  [2] Reißfestigkeit | ISO 37 Type 1,  [3] Reißdehnung | ISO 37 Type 1,  [4] Weiterreißwiderstand | ASTM D 624 B,  [5] Druckverformungsrest | 22 h | 175 °C | DIN ISO 815-1 Typ B Methode A | post-cured 6 h / 200 °C,  [6] Druckverformungsrest | 22 h | 125 °C | DIN ISO 815-1 Typ B Methode A 

Bestellen

Meine Medien


Zum Bestellformular

Vertriebskontakt

Wacker Chemie AG
Gisela-Stein-Strasse 1
81671 Munich
+49  89  6279-0 (Phone)

Meine Favoriten

Meine Produkte