ELASTOSIL® M 4470

$ELASTOSIL<sup>®</sup> M 4470

Pourable, condensation-curing, two-component silicone rubber that vulcanizes at room temperature.

 

Main application: Making molds for casting of low melting metal alloys.


Properties

  • Good flowability and self-deaeration
  • High Shore A hardness (approx. 60)
  • Outstanding resistance to common casting resins
  • Low viscosity

Specific features of ELASTOSIL® M 4470

  • Condensation-curing
  • Flowable
  • Heat resistant
  • Low viscosity
  • Thermally conductive
  • Two-component

ELASTOSIL® M 4470 is particularly suitable for molding applications in which high elongation and tear strength can be sacrificed in favor of excellent deformation resistance and thermal stability, e. g., for making molds of models of models with nor or only minor undercuts if good heat dissipation and high rigidity are required.


Typical applications are molds with

  • high rigidity for foaming resins (for foaming polyurethanes, it is advisable to use a barrier coat!)
  • high swelling resistance to components of casting resins, such as styrene in the case of polyesters
  • high thermal stability and heat dissipation for casting low-melting metal alloys

ELASTOSIL® M 4470 is cured by adding Catalyst T37 for long pot lives and curing times, or Catalyst T40 for short pot lives and curing times.


Thin-walled molds are best suited for casting low-melting metal alloys (melting point: 300 °C max.) and should be placed on a sheet of aluminum or other material with high thermal conductivity. Before the casting process, the old should be post-cured for a few hours at about 150 °C. In order to improve wetting by the molten metal, a thin layer of extremely fine silicon carbide, graphite powder or acetylene black should be applied to the mold surface.
The first castings have normally to be discarded since the rubber still emits gases, giving the surface of the casting a pockmarked appearance.
The pot life is the period of time at 23 °C / 50 % rel. humidity during which the catalyzed mix to attain a viscosity of 100,000 mPa s and still be just pourable

 

Please check also our brochures and info sheets.

Storage

The 'Best use before end' date of each batch is shown on the product label.


Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

Sales and support

Wacker Chemicals Middle East
Dubai Silicon Oasis s/n
0001 Dubai
United Arab Emirates
+971  4  709-9999 (Phone)
+971 4 709-9911  (Fax)
Contact

How can we help you?

  • Do you need help in choosing a product or do you require technical support? If so, please contact our experts.
Ask a question

Would you like a product sample?

You can request a product sample here.

Request sample

More products

Products Technical data
动态粘度 Tear strength Tear-growth resistance Hardness Shore A Tensile strength Elongation at break
CENUSIL® M 810 A/B 3000 mPa·s[1] 3000 mPa·s[1] - - 15 N/mm[10] 15 N/mm[10] 10[14] 10[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 600 %[19] 600 %[19]
CENUSIL® M 820 A/B 6000 mPa·s[2] 6000 mPa·s[2] - - - - 20[14] 20[14] 4 N/mm²[16] 4 N/mm²[16] 500 %[19] 500 %[19]
CENUSIL® M 825 A/B 8000 mPa·s[3] 8000 mPa·s[3] - - 20 N/mm[10] 20 N/mm[10] 25[14] 25[14] 5 N/mm²[16] 5 N/mm²[16] 450 %[19] 450 %[19]
CENUSIL® M 830 A/B 8000 mPa·s[3] 8000 mPa·s[3] - - > 20 N/mm[10] > 20 N/mm[10] 26[14] 26[14] 5 N/mm²[16] 5 N/mm²[16] 500 %[19] 500 %[19]
ELASTOSIL® FX 10 A/B 6000 mPa·s[3] 6000 mPa·s[3] - - > 20 N/mm[11] > 20 N/mm[11] 10[14] 10[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 950 %[19] 950 %[19]
ELASTOSIL® M 1470 - - - - > 10 N/mm[10] > 10 N/mm[10] 45[15] 45[15] 4.5 N/mm²[17] 4.5 N/mm²[17] 230 %[20] 230 %[20]
ELASTOSIL® M 4115 A/B 2500 mPa·s[3] 2500 mPa·s[3] 5 N/mm[12] 5 N/mm[12] - - 17[14] 17[14] 3 N/mm²[16] 3 N/mm²[16] 400 %[19] 400 %[19]
ELASTOSIL® M 4125 F A/B 6000 mPa·s[3] 6000 mPa·s[3] - - - - 28[15] 28[15] 5.0[18] 5.0[18] 500[20] 500[20]
ELASTOSIL® M 4370 A/B 350 mPa·s[4] 350 mPa·s[4] > 4 N/mm[12] > 4 N/mm[12] - - 55[14] 55[14] 3.0 N/mm²[17] 3.0 N/mm²[17] 130 %[20] 130 %[20]
ELASTOSIL® M 4400 30000 mPa·s[5] 30000 mPa·s[5] > 3 N/mm[12] > 3 N/mm[12] - - 23[15] 23[15] 2 N/mm²[17] 2 N/mm²[17] 250 %[20] 250 %[20]
ELASTOSIL® M 4440 25000 mPa·s[5] 25000 mPa·s[5] 4.5 N/mm[12] 4.5 N/mm[12] - - 37[15] 37[15] 2.5 N/mm²[17] 2.5 N/mm²[17] 220 %[20] 220 %[20]
ELASTOSIL® M 4470 15000 mPa·s[6] 15000 mPa·s[6] > 4 N/mm[12] > 4 N/mm[12] - - 60[15] 60[15] 4.5 N/mm²[17] 4.5 N/mm²[17] 120 %[20] 120 %[20]
ELASTOSIL® M 4503 40000 mPa·s[6] 40000 mPa·s[6] > 20 N/mm[12] > 20 N/mm[12] - - 25[14] 25[14] 20 N/mm²[17] 20 N/mm²[17] 350 %[20] 350 %[20]
ELASTOSIL® M 4511 25000 mPa·s[5] 25000 mPa·s[5] > 18 N/mm[12] > 18 N/mm[12] - - 12[15] 12[15] 3.5 N/mm²[17] 3.5 N/mm²[17] 600 %[20] 600 %[20]
ELASTOSIL® M 4512 30000 mPa·s[5] 30000 mPa·s[5] > 24 N/mm[12] > 24 N/mm[12] - - 20[15] 20[15] 3.5 N/mm²[17] 3.5 N/mm²[17] 500 %[20] 500 %[20]
ELASTOSIL® M 4514 35000 mPa·s[6] 35000 mPa·s[6] > 25 N/mm[12] > 25 N/mm[12] - - 25[14] 25[14] 4.5 N/mm²[17] 4.5 N/mm²[17] 450 %[20] 450 %[20]
ELASTOSIL® M 4541 40000 mPa·s[6] 40000 mPa·s[6] > 30 N/mm[12] > 30 N/mm[12] - - 32[15] 32[15] 5 N/mm²[17] 5 N/mm²[17] 400 %[20] 400 %[20]
ELASTOSIL® M 4600 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 20 N/mm[12] > 20 N/mm[12] - - 20[15] 20[15] 7[17] 7[17] 800 %[20] 800 %[20]
ELASTOSIL® M 4601 A/B 15000 mPa·s[6] 15000 mPa·s[6] > 30 N/mm[12] > 30 N/mm[12] - - 28[15] 28[15] 6.5 N/mm²[17] 6.5 N/mm²[17] 700 %[20] 700 %[20]
ELASTOSIL® M 4642 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 30 N/mm[12] > 30 N/mm[12] - - 37[15] 37[15] 7 N/mm²[17] 7 N/mm²[17] 480 %[20] 480 %[20]
ELASTOSIL® M 4643 A/B 40000 mPa·s[6] 40000 mPa·s[6] > 10 N/mm[12] > 10 N/mm[12] - - 48[15] 48[15] 5 N/mm²[17] 5 N/mm²[17] 300 %[20] 300 %[20]
ELASTOSIL® M 4670 A/B 120000 mPa·s[6] 120000 mPa·s[6] 15 N/mm[12] 15 N/mm[12] - - 55[14] 55[14] 5.5 N/mm²[16] 5.5 N/mm²[16] 280 %[19] 280 %[19]
ELASTOSIL® RT 480 300000 - 400000 mPa·s[7] 300000 - 400000 mPa·s[7] > 7 N/mm[12] > 7 N/mm[12] - - 55[15] 55[15] 4.5 N/mm²[17] 4.5 N/mm²[17] 170 %[20] 170 %[20]
ELASTOSIL® RT 625 A/B 25000 mPa·s[6] 25000 mPa·s[6] 30 N/mm[12] 30 N/mm[12] - - 25[14] 25[14] 6.5 N/mm²[16] 6.5 N/mm²[16] 600 %[19] 600 %[19]
ELASTOSIL® RT 646 A/B 110000 mPa·s[3] 110000 mPa·s[3] 12 N/mm[12] 12 N/mm[12] - - 53[14] 53[14] 5 N/mm²[16] 5 N/mm²[16] 280 %[19] 280 %[19]
ELASTOSIL® RT K - - > 3 N/mm[13] > 3 N/mm[13] - - 45[15] 45[15] 2 N/mm²[17] 2 N/mm²[17] 130 %[20] 130 %[20]
ELASTOSIL® VARIO 15 5.000 mPa·s[8] 5.000 mPa·s[8] 15[12] 15[12] - - 15[14] 15[14] 6.5 N/mm²[16] 6.5 N/mm²[16] 900 %[19] 900 %[19]
ELASTOSIL® VARIO 40 15.000 mPa·s[9] 15.000 mPa·s[9] 15 N/mm[12] 15 N/mm[12] - - 40[14] 40[14] 8 N/mm²[16] 8 N/mm²[16] 450 %[19] 450 %[19]
Legend
[1] 动态粘度 | Brookfield,  [2] 动态粘度 23°C | ISO 3219,  [3] 动态粘度 | 23 °C | ISO 3219,  [4] 动态粘度 搅拌后 | 23 °C ,  [5] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219,  [6] 动态粘度 after stirring | 23 °C | ISO 3219,  [7] 动态粘度 | 23 °C | Brookfield,  [8] 动态粘度 23°C, stirred | ISO 3219,  [9] 动态粘度 23° C, stirred | ISO 3219,  [10] Tear-growth resistance | ASTM D 624 B,  [11] Tear-growth resistance | ASTM D 624, Die B,  [12] Tear strength | ASTM D 624 B,  [13] Tear strength | ASTM 624 B,  [14] Hardness Shore A | DIN ISO 48-4,  [15] Hardness Shore A | ISO 868,  [16] Tensile strength | ISO 37 type 1,  [17] Tensile strength | ISO 37,  [18] Tensile strength | DIN ISO 37,  [19] Elongation at break | ISO 37 type 1,  [20] Elongation at break | ISO 37 

Order

My media


Go to order form

Sales Contact

Wacker Chemicals Middle East
Dubai Silicon Oasis s/n
0001 Dubai
+971  4  709-9999 (Phone)

My favorites

My products