SILPURAN® 2100 A/B
Two-component, addition-curing silicone composition curing to a soft silicone adhesive
More products
Products | Technical data | |
---|---|---|
Viscosity, dynamic | Penetration | |
SILPURAN® 2100 A/B | 34000 mPa·s[1] 34000 mPa·s[1] | 205 1/10mm[2] 205 1/10mm[2] |
SILPURAN® 2112 A/B | 11600 mPa·s[1] 11600 mPa·s[1] | 225 1/10mm[2] 225 1/10mm[2] |
SILPURAN® 2114 A/B | 12000 mPa·s[1] 12000 mPa·s[1] | 200 1/10mm[2] 200 1/10mm[2] |
SILPURAN® 2114 OT A/B | 12000 mPa·s[1] 12000 mPa·s[1] | 170 1/10mm[2] 170 1/10mm[2] |
SILPURAN® 2117 A/B | 33000 mPa·s[1] 33000 mPa·s[1] | 205 1/10mm[2] 205 1/10mm[2] |
SILPURAN® 2124 A/B | 3200 mPa·s[1] 3200 mPa·s[1] | 155 1/10mm[2] 155 1/10mm[2] |
SILPURAN® 2130 A/B | 1000 mPa·s[1] 1000 mPa·s[1] | 220 1/10mm[2] 220 1/10mm[2] |
[1] Viscosity, dynamic | DIN EN ISO 3219, [2] Penetration | DIN ISO 2137 | hollow cone of 62.5 g, 60 s