ELASTOSIL® M 4600 A/B

$ELASTOSIL<sup>®</sup> M 4600 A/B

Pourable, addition-curing, two-component silicone rubber that vulcanizes at room temperature.

 

Main application: Making shrink-free molds with excellent reproduction accuracy, food contact (FDA/ BfR compliant).


特性

  • Very good flow
  • Fast and non-shrink cure at room temperature which
  • Can be accelerated considerably by the application of heat
  • Low Shore A hardness (approx. 20)
  • Good transparency
  • High tear strength
  • Excellent long-term stability of the mechanical properties of the cured rubber
  • Outstanding resistance to common casting resins

ELASTOSIL® M 4600 A/B的特殊性能

  • 加成固化
  • 双组分
  • 无化学收缩
  • 易流动的
  • 符合BfR
  • 符合FDA
  • 食品接触

Due to the outstanding resistance to casting resins as well as the superior mechanical properties, ELASTOSIL® M 4600 A/B is especially suitable for all molds of models with extensive undercuts that are to be reproduced in casting resins.

In addition to the low hardness, which facilitates demolding, ELASTOSIL® M 4600 A/B has the advantage of being transparent. This makes it possible to cut onepart molds under visual control along a parting line which has been established before or is determined by the shape of the model, a method which often saves making a two- or multi-part mold.

As a low-Shore addition-curing RTV-2 silicone rubber that cures without undergoing dimensional shrinkage, ELASTOSIL® M 4600 A/B is also extremely suitable for casting all other common reproduction materials, particularly if absolutely accurate copies of models with pronounced undercuts are required

Detailed instructions for preparation and use are given in the brochure “Room Temperature Vulcanizing (RTV) Silicones - Material and Processing Guidelines”.

 

Important note:
The platinum catalyst is in component B.


Caution:
A and B components may only be used together if they have the same batch number.

储存

The 'Best use before end' date of each batch is shown on the product label.

 

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemicals (China) Co.,Ltd.
Caohejing Hi-Tech Park
200233 Shanghai
中国大陆
+86  21  6130-2000 （电话）
+86 21 6130-2500  （传真）
Contact Sales

我们可以为您提供什么帮助？

  • 您在选择产品方面需要帮助或者需要技术咨询？ 请联系我们的专家
Ask a question

Would you like a product sample?

You can request a product sample here.

Request sample

更多产品

个产品 技术数据
Viscosity, dynamic Tear strength Hardness Shore A Tensile strength Elongation at break
CENUSIL® M 810 A/B 3000 mPa·s[1] 3000 mPa·s[1] 15 N/mm[10] 15 N/mm[10] 10[13] 10[13] 3.5 N/mm²[15] 3.5 N/mm²[15] 600 %[18] 600 %[18]
CENUSIL® M 820 A/B 6000 mPa·s[2] 6000 mPa·s[2] - - 20[13] 20[13] 4 N/mm²[15] 4 N/mm²[15] 500 %[18] 500 %[18]
CENUSIL® M 825 A/B 8000 mPa·s[3] 8000 mPa·s[3] 20 N/mm[10] 20 N/mm[10] 25[13] 25[13] 5 N/mm²[15] 5 N/mm²[15] 450 %[18] 450 %[18]
CENUSIL® M 830 A/B 8000 mPa·s[3] 8000 mPa·s[3] > 20 N/mm[10] > 20 N/mm[10] 26[13] 26[13] 5 N/mm²[15] 5 N/mm²[15] 500 %[18] 500 %[18]
ELASTOSIL® FX 10 A/B 6000 mPa·s[3] 6000 mPa·s[3] > 20 N/mm[11] > 20 N/mm[11] 10[13] 10[13] 4.5 N/mm²[15] 4.5 N/mm²[15] 950 %[18] 950 %[18]
ELASTOSIL® M 1470 - - > 10 N/mm[10] > 10 N/mm[10] 45[14] 45[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 230 %[19] 230 %[19]
ELASTOSIL® M 4115 A/B 2500 mPa·s[3] 2500 mPa·s[3] 5 N/mm[10] 5 N/mm[10] 17[13] 17[13] 3 N/mm²[15] 3 N/mm²[15] 400 %[18] 400 %[18]
ELASTOSIL® M 4125 F A/B 6000 mPa·s[3] 6000 mPa·s[3] - - 28[14] 28[14] 5.0[17] 5.0[17] 500[19] 500[19]
ELASTOSIL® M 4370 A/B 350 mPa·s[4] 350 mPa·s[4] > 4 N/mm[10] > 4 N/mm[10] 55[13] 55[13] 3.0 N/mm²[16] 3.0 N/mm²[16] 130 %[19] 130 %[19]
ELASTOSIL® M 4400 30000 mPa·s[5] 30000 mPa·s[5] > 3 N/mm[10] > 3 N/mm[10] 23[14] 23[14] 2 N/mm²[16] 2 N/mm²[16] 250 %[19] 250 %[19]
ELASTOSIL® M 4440 25000 mPa·s[5] 25000 mPa·s[5] 4.5 N/mm[10] 4.5 N/mm[10] 37[14] 37[14] 2.5 N/mm²[16] 2.5 N/mm²[16] 220 %[19] 220 %[19]
ELASTOSIL® M 4470 15000 mPa·s[6] 15000 mPa·s[6] > 4 N/mm[10] > 4 N/mm[10] 60[14] 60[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 120 %[19] 120 %[19]
ELASTOSIL® M 4503 40000 mPa·s[6] 40000 mPa·s[6] > 20 N/mm[10] > 20 N/mm[10] 25[13] 25[13] 20 N/mm²[16] 20 N/mm²[16] 350 %[19] 350 %[19]
ELASTOSIL® M 4511 25000 mPa·s[5] 25000 mPa·s[5] > 18 N/mm[10] > 18 N/mm[10] 12[14] 12[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 600 %[19] 600 %[19]
ELASTOSIL® M 4512 30000 mPa·s[5] 30000 mPa·s[5] > 24 N/mm[10] > 24 N/mm[10] 20[14] 20[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 500 %[19] 500 %[19]
ELASTOSIL® M 4514 35000 mPa·s[6] 35000 mPa·s[6] > 25 N/mm[10] > 25 N/mm[10] 25[13] 25[13] 4.5 N/mm²[16] 4.5 N/mm²[16] 450 %[19] 450 %[19]
ELASTOSIL® M 4541 40000 mPa·s[6] 40000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 32[14] 32[14] 5 N/mm²[16] 5 N/mm²[16] 400 %[19] 400 %[19]
ELASTOSIL® M 4600 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 20 N/mm[10] > 20 N/mm[10] 20[14] 20[14] 7[16] 7[16] 800 %[19] 800 %[19]
ELASTOSIL® M 4601 A/B 15000 mPa·s[6] 15000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 28[14] 28[14] 6.5 N/mm²[16] 6.5 N/mm²[16] 700 %[19] 700 %[19]
ELASTOSIL® M 4642 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 37[14] 37[14] 7 N/mm²[16] 7 N/mm²[16] 480 %[19] 480 %[19]
ELASTOSIL® M 4643 A/B 40000 mPa·s[6] 40000 mPa·s[6] > 10 N/mm[10] > 10 N/mm[10] 48[14] 48[14] 5 N/mm²[16] 5 N/mm²[16] 300 %[19] 300 %[19]
ELASTOSIL® M 4670 A/B 120000 mPa·s[6] 120000 mPa·s[6] 15 N/mm[10] 15 N/mm[10] 55[13] 55[13] 5.5 N/mm²[15] 5.5 N/mm²[15] 280 %[18] 280 %[18]
ELASTOSIL® RT 480 300000 - 400000 mPa·s[7] 300000 - 400000 mPa·s[7] > 7 N/mm[10] > 7 N/mm[10] 55[14] 55[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 170 %[19] 170 %[19]
ELASTOSIL® RT 625 A/B 25000 mPa·s[6] 25000 mPa·s[6] 30 N/mm[10] 30 N/mm[10] 25[13] 25[13] 6.5 N/mm²[15] 6.5 N/mm²[15] 600 %[18] 600 %[18]
ELASTOSIL® RT 646 A/B 110000 mPa·s[3] 110000 mPa·s[3] 12 N/mm[10] 12 N/mm[10] 53[13] 53[13] 5 N/mm²[15] 5 N/mm²[15] 280 %[18] 280 %[18]
ELASTOSIL® RT K - - > 3 N/mm[12] > 3 N/mm[12] 45[14] 45[14] 2 N/mm²[16] 2 N/mm²[16] 130 %[19] 130 %[19]
ELASTOSIL® VARIO 15 5.000 mPa·s[8] 5.000 mPa·s[8] 15[10] 15[10] 15[13] 15[13] 6.5 N/mm²[15] 6.5 N/mm²[15] 900 %[18] 900 %[18]
ELASTOSIL® VARIO 40 15.000 mPa·s[9] 15.000 mPa·s[9] 15 N/mm[10] 15 N/mm[10] 40[13] 40[13] 8 N/mm²[15] 8 N/mm²[15] 450 %[18] 450 %[18]
说明
[1] Viscosity, dynamic | Brookfield,  [2] Viscosity, dynamic 23°C | ISO 3219,  [3] Viscosity, dynamic | 23 °C | ISO 3219,  [4] Viscosity, dynamic after stirring | 23 °C ,  [5] Viscosity, dynamic after stirring | 23 °C | DIN EN ISO 3219,  [6] Viscosity, dynamic after stirring | 23 °C | ISO 3219,  [7] Viscosity, dynamic | 23 °C | Brookfield,  [8] Viscosity, dynamic 23°C, stirred | ISO 3219,  [9] Viscosity, dynamic 23° C, stirred | ISO 3219,  [10] Tear strength | ASTM D 624 B,  [11] Tear strength | ASTM D 624, Die B,  [12] Tear strength | ASTM 624 B,  [13] Hardness Shore A | DIN ISO 48-4,  [14] Hardness Shore A | ISO 868,  [15] Tensile strength | ISO 37 type 1,  [16] Tensile strength | ISO 37,  [17] Tensile strength | DIN ISO 37,  [18] Elongation at break | ISO 37 type 1,  [19] Elongation at break | ISO 37 

购物车

我的媒体


转至订单表

联系方式

Wacker Chemicals Middle East
Dubai Silicon Oasis s/n
0001 Dubai
+971  4  709-9999 (Phone)

收藏夹

我的产品