SILPURAN® 6600/40 A/B

Liquid silicone rubbers of the SILPURAN® 6600 series are paste-like, easily-pigmentable two-component compounds with short curing times. Their vulcanizates are noted for their high transparency and excellent mechanical and electrical properties. Compared to the SILPURAN® 6000 series the coefficient of friction of a post-cured article made of SILPURAN® 6600 is reduced by 50 - 70 %.
SILPURAN® 6600/40 A/B is designed for medical applications in compliance with the WACKER SILICONES HEALTH CARE POLICY including implantation for < 30 days.


特性

SILPURAN® 6600/40 A/B meets selected test requirements of ISO 10993 and United States Pharmacopoeia (USP) Class VI. It is designed for medical applications in compliance with the WACKER SILICONES HEALTH CARE POLICY including implantation for < 30 days and is particularly suitable for the economical production of large series of injection molded articles.

At service temperatures above approx. 180 °C the addition of heat stabilizers is recommended. Further information about an improvement of the heat stability by use of specific ELASTOSIL® Color Pastes FL can be obtained from the Technical Information Sheet "ELASTOSIL® Color Pastes FL" or the latest edition of our brochures.

SILPURAN® 6600/40 A/B的特殊性能

  • 减少挥发物含量
  • 摩擦系数低
  • 降低自愈合性
  • 食品接触

The following studies were performed on vulcanizates of SILPURAN® 6600/40 A/B according to ISO 10993:
    - Cytotoxicity (ISO 10993-5)
    - Sensitation LLNA (ISO 10993-10)
    - Pyrogenicity (ISO 10993-11)

The following studies were performed on vulcanizates of SILPURAN® 6600/40 A/B according to USP class VI:
    - Acute systemic toxicity
    - Intracutaneous toxicity
    - Implantation test
No adverse effects have been detected at any of the studies performed.

Properly cured and post-cured vulcanizates of SILPURAN® 6600/40 A/B can be used for food contact applications and are suitable for use under the Recommendation "XV. Silicones" of the BfR and FDA 21 CFR §177.2600 "Rubber Articles Intended for Repeated Use" considering any given limitations on extractable and volatile substances.

The A and B components are delivered ready to use in 20 kg pail kits. With adequate metering equipment, they can be pumped directly from the original containers into the injection molding machine and mixed by a static mixer. The mixing ratio is 1 : 1. At room temperature, mixtures of A and B components have a pot life of at least three days.
For detailed information please refer to the latest edition of our brochure "SOLID AND LIQUID SILICONE RUBBER - MATERIAL AND PROCESSING GUIDELINES".

包装

This product is available in 20 kg pail kits. 
SILPURAN® is neither produced nor packed under sterile conditions, so the final product has to be sterilized prior to use, if necessary.

储存

Once opened, containers should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulphur or phosphorus compounds. For detailed information about storage conditions please refer to the latest edition of our brochure "SOLID AND LIQUID SILICONE RUBBER - MATERIAL AND PROCESSING GUIDELINES".
The 'Best use before end' date of each batch is shown on the product label. Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemical Corporation
S State Road 4950
Ann Arbor, MI 48108
美国
+1  888  922-5374 （电话）
Contact Sales

我们可以为您提供什么帮助？

  • 您在选择产品方面需要帮助或者需要技术咨询？ 请联系我们的专家
Ask a question

您是否需要产品样本？

您可以在此处索取产品样本。

索取样本

更多产品

个产品 技术数据
外观 Shore density A Breaking strength 断裂伸长率 Tear-growth resistance 压缩变形
ELASTOSIL® eco LR 5040/20 A/B slightly bluish slightly bluish 20[3] 20[3] 7.9 N/mm²[5] 7.9 N/mm²[5] 890 %[6] 890 %[6] 33 N/mm[8] 33 N/mm[8] - -
ELASTOSIL® eco LR 5040/30 A/B slightly bluish slightly bluish 30[3] 30[3] 8.6 N/mm²[5] 8.6 N/mm²[5] 860 %[6] 860 %[6] 32 N/mm[8] 32 N/mm[8] - -
ELASTOSIL® eco LR 5040/40 A/B slightly bluish slightly bluish 40[3] 40[3] 9.0 N/mm²[5] 9.0 N/mm²[5] 580 %[6] 580 %[6] 38 N/mm[8] 38 N/mm[8] - -
ELASTOSIL® eco LR 5040/50 A/B slightly bluish slightly bluish 50[3] 50[3] 9.1 N/mm²[5] 9.1 N/mm²[5] 490 %[6] 490 %[6] 54 N/mm[8] 54 N/mm[8] - -
ELASTOSIL® eco LR 5040/60 A/B slightly bluish slightly bluish 60[3] 60[3] 9.0 N/mm²[5] 9.0 N/mm²[5] 380 %[6] 380 %[6] 50 N/mm[8] 50 N/mm[8] - -
ELASTOSIL® eco LR 5040/70 A/B slightly bluish slightly bluish 70[3] 70[3] 9.5 N/mm²[5] 9.5 N/mm²[5] 370 %[6] 370 %[6] 36 N/mm[8] 36 N/mm[8] - -
ELASTOSIL® LR 3003/50 US A/B Transparent[1] Transparent[1] 51 51 - - - - 35 kN/m 35 kN/m - -
ELASTOSIL® LR 3003/60 US A/B transparent[2] transparent[2] 59[4] 59[4] - - 420 %[7] 420 %[7] 31 kN/m[9] 31 kN/m[9] - -
ELASTOSIL® LR 3003/70 US A/B transparent[2] transparent[2] 68[4] 68[4] - - - - 31 kN/m[9] 31 kN/m[9] 18 %[10] 18 %[10]
ELASTOSIL® LR 3003/80 US A/B transparent[2] transparent[2] 77[4] 77[4] - - 300 %[7] 300 %[7] 21 N/mm[9] 21 N/mm[9] - -
ELASTOSIL® LR 34004/50 A/B white white 50[3] 50[3] 7.8 N/mm²[5] 7.8 N/mm²[5] 450 %[6] 450 %[6] 26 N/mm[8] 26 N/mm[8] - -
ELASTOSIL® LR 5040/20 A/B slightly bluish slightly bluish 20[3] 20[3] 7.9 N/mm²[5] 7.9 N/mm²[5] 890 %[6] 890 %[6] 33 N/mm[8] 33 N/mm[8] - -
ELASTOSIL® LR 5040/30 A/B slightly bluish slightly bluish 30[3] 30[3] 8.6 N/mm²[5] 8.6 N/mm²[5] 860 %[6] 860 %[6] 32 N/mm[8] 32 N/mm[8] - -
ELASTOSIL® LR 5040/40 A/B slightly bluish slightly bluish 40[3] 40[3] 9.0 N/mm²[5] 9.0 N/mm²[5] 580 %[6] 580 %[6] 38 N/mm[8] 38 N/mm[8] - -
ELASTOSIL® LR 5040/45 A/B slightly bluish slightly bluish 45[3] 45[3] 9.0 N/mm²[5] 9.0 N/mm²[5] 580 %[6] 580 %[6] 41 N/mm[8] 41 N/mm[8] - -
ELASTOSIL® LR 5040/50 A/B slightly bluish slightly bluish 50[3] 50[3] 9.1 N/mm²[5] 9.1 N/mm²[5] 490 %[6] 490 %[6] 54 N/mm[8] 54 N/mm[8] - -
ELASTOSIL® LR 5040/60 A/B slightly bluish slightly bluish 60[3] 60[3] 9.0 N/mm²[5] 9.0 N/mm²[5] 380 %[6] 380 %[6] 50 N/mm[8] 50 N/mm[8] - -
ELASTOSIL® LR 5040/70 A/B slightly bluish slightly bluish 70[3] 70[3] 9.5 N/mm²[5] 9.5 N/mm²[5] 370 %[6] 370 %[6] 36 N/mm[8] 36 N/mm[8] - -
SILPURAN® 6000/05 A/B transparent transparent 5[3] 5[3] 2.5 N/mm²[5] 2.5 N/mm²[5] 700 %[6] 700 %[6] 6 N/mm[8] 6 N/mm[8] - -
SILPURAN® 6000/10 A/B transparent transparent 10[3] 10[3] 4.2 N/mm²[5] 4.2 N/mm²[5] 740 %[6] 740 %[6] 13 N/mm[8] 13 N/mm[8] 15 %[11] 15 %[11]
SILPURAN® 6000/20 A/B transparent transparent 20[3] 20[3] 8.0 N/mm²[5] 8.0 N/mm²[5] 850 %[6] 850 %[6] 21 N/mm[8] 21 N/mm[8] 17 %[11] 17 %[11]
SILPURAN® 6000/30 A/B transparent transparent 30[3] 30[3] 8.6 N/mm²[5] 8.6 N/mm²[5] 650 %[6] 650 %[6] 25 N/mm[8] 25 N/mm[8] 13 %[11] 13 %[11]
SILPURAN® 6000/40 A/B transparent transparent 40[3] 40[3] 9.6 N/mm²[5] 9.6 N/mm²[5] 600 %[6] 600 %[6] 29 N/mm[8] 29 N/mm[8] 11 %[11] 11 %[11]
SILPURAN® 6000/50 A/B transparent transparent 50[3] 50[3] 10.0 N/mm²[5] 10.0 N/mm²[5] 480 %[6] 480 %[6] 30 N/mm[8] 30 N/mm[8] 14 %[11] 14 %[11]
SILPURAN® 6000/60 A/B transparent transparent 60[3] 60[3] 10.0 N/mm²[5] 10.0 N/mm²[5] 350 %[6] 350 %[6] 27 N/mm[8] 27 N/mm[8] 14 %[11] 14 %[11]
SILPURAN® 6000/70 A/B transparent transparent 70[3] 70[3] 9.5 N/mm²[5] 9.5 N/mm²[5] 290 %[6] 290 %[6] 22 N/mm[8] 22 N/mm[8] 11 %[11] 11 %[11]
SILPURAN® 6600/40 A/B transparent transparent 40[3] 40[3] 9.4 N/mm²[5] 9.4 N/mm²[5] 550 %[6] 550 %[6] 32 N/mm[8] 32 N/mm[8] 14 %[11] 14 %[11]
SILPURAN® 6600/50 A/B transparent transparent 50[3] 50[3] 8.9 N/mm²[5] 8.9 N/mm²[5] 440 %[6] 440 %[6] 31 N/mm[8] 31 N/mm[8] 13 %[11] 13 %[11]
SILPURAN® 6600/60 A/B transparent transparent 60[3] 60[3] 9.0 N/mm²[5] 9.0 N/mm²[5] 310 %[6] 310 %[6] 26 N/mm[8] 26 N/mm[8] 14 %[11] 14 %[11]
SILPURAN® 6610/40 A/B white white 40[3] 40[3] 7.2 N/mm²[5] 7.2 N/mm²[5] 510 %[6] 510 %[6] 22 N/mm[8] 22 N/mm[8] 12 %[11] 12 %[11]
SILPURAN® 6610/50 A/B white white 50[3] 50[3] 8.0 N/mm²[5] 8.0 N/mm²[5] 450 %[6] 450 %[6] 25 N/mm[8] 25 N/mm[8] 12 %[11] 12 %[11]
SILPURAN® 6610/60 A/B white white 60[3] 60[3] 7.0 N/mm²[5] 7.0 N/mm²[5] 300 %[6] 300 %[6] 20 N/mm[8] 20 N/mm[8] 15 %[11] 15 %[11]
SILPURAN® 6700/40 A/B transparent transparent 40[3] 40[3] 8.2 N/mm²[5] 8.2 N/mm²[5] 640 %[6] 640 %[6] 23 N/mm[8] 23 N/mm[8] 40 %[12] 40 %[12]
SILPURAN® 6700/50 A/B transparent transparent 50[3] 50[3] 8.5 N/mm²[5] 8.5 N/mm²[5] 590 %[6] 590 %[6] 24 N/mm[8] 24 N/mm[8] 50 %[12] 50 %[12]
SILPURAN® 6700/60 A/B transparent transparent 60[3] 60[3] 9.6 N/mm²[5] 9.6 N/mm²[5] 490 %[6] 490 %[6] 26 N/mm[8] 26 N/mm[8] 60 %[12] 60 %[12]
SILPURAN® 6740/40 A/B transparent transparent 40[3] 40[3] 8.8 N/mm²[5] 8.8 N/mm²[5] 710 %[6] 710 %[6] 27 N/mm[8] 27 N/mm[8] - -
SILPURAN® 6760/50 A/B transparent transparent 50[3] 50[3] 8.4 N/mm²[5] 8.4 N/mm²[5] 600 %[6] 600 %[6] 27 N/mm[8] 27 N/mm[8] - -
说明
[1] 外观 | WSTM 2298,  [2] 外观 | DIN ISO 2137,  [3] Shore density A | DIN ISO 48-4,  [4] Shore density A | ASTM D 2240 Type A,  [5] Breaking strength | ISO 37 type 1,  [6] 断裂伸长率 | ISO 37 type 1,  [7] 断裂伸长率 | ASTM D 412,  [8] Tear-growth resistance | ASTM D 624 B,  [9] Tear-growth resistance | ASTM D 624, Die B,  [10] 压缩变形 | 22 h | 177 °C | WSTM 1114,  [11] 压缩变形 | 22 h | 175 °C | DIN ISO 815-1 type B method A | post-cured 6 h / 200 °C,  [12] 压缩变形 | 22 h | 125 °C | DIN ISO 815-1 type B method A 

购物车

我的媒体


转至订单表

联系方式

Wacker Kimya Ticaret Limited Şirketi
Tevfik Fikret Cad. No: 32/4
34750 Ataşehir / Istanbul
+90  216  569-7050 （电话）

收藏夹

我的产品