ELASTOSIL® M 4503

$ELASTOSIL<sup>®</sup> M 4503

Pourable, condensation-curing, two-component silicone rubber that vulcanizes at room temperature.

 

Main application: Making cost effective molds, particularly for casting PE resins.


特性

  • Good flow
  • Low Shore A hardness (approx. 25)
  • Great extensibility and elasticity
  • High resistance to casting resins, particularly polyesters

ELASTOSIL® M 4503的特殊性能

  • 双组分
  • 易流动的
  • 缩合固化

Due to its good mechanical properties of the cured material as well as its high resistance to polyester resins, ELASTOSIL® M 4503 is particularly suitable as a mold-making material for reproducing models with very pronounced undercuts in polyester resins.

 

Other materials, such as plaster or wax, may also be cast without any problems from molds made of ELASTOSIL® M 4503.

ELASTOSIL® M 4503 is cured by adding 2 wt % Catalyst T 40. Pot life and curing time may be accelerated, and thus adjusted to suit the individual application by adding up to 4 wt % Catalyst T 40.

 

Further instructions for preparation and use are given in our brochure “Room Temperature Vulcanizing (RTV) Silicones
- Material and Processing Guidelines”.

 

Detailed information on other mold-making compounds in the ELASTOSIL ® M range is contained in our brochure “ELASTOSIL® M. Silicone Rubber for Mold Making”.

储存

The 'Best use before end' date of each batch is shown on the product label.

 

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemie AG
Gisela-Stein-Strasse 1
81671 Munich
德国
+49  89  6279-0 （电话）
+49 89 6279-1770  （传真）
Contact Sales
网站

我们可以为您提供什么帮助？

  • 您在选择产品方面需要帮助或者需要技术咨询？ 请联系我们的专家
Ask a question

您是否需要产品样本？

您可以在此处索取产品样本。

索取样本

Mehr Produkte

Produkte Technische Daten
dynamische Viskosität 动态粘度 Weiterreißwiderstand Härte Shore A Reißfestigkeit Reißdehnung
CENUSIL® M 810 A/B - - 3000 mPa·s[1] 3000 mPa·s[1] 15 N/mm[13] 15 N/mm[13] 10[16] 10[16] 3.5 N/mm²[18] 3.5 N/mm²[18] 600 %[21] 600 %[21]
CENUSIL® M 820 A/B - - 6000 mPa·s[2] 6000 mPa·s[2] - - 20[16] 20[16] 4 N/mm²[18] 4 N/mm²[18] 500 %[21] 500 %[21]
CENUSIL® M 825 A/B - - 8000 mPa·s[3] 8000 mPa·s[3] 20 N/mm[13] 20 N/mm[13] 25[16] 25[16] 5 N/mm²[18] 5 N/mm²[18] 450 %[21] 450 %[21]
CENUSIL® M 830 A/B - - 8000 mPa·s[3] 8000 mPa·s[3] > 20 N/mm[13] > 20 N/mm[13] 26[16] 26[16] 5 N/mm²[18] 5 N/mm²[18] 500 %[21] 500 %[21]
ELASTOSIL® FX 10 A/B - - 6000 mPa·s[3] 6000 mPa·s[3] > 20 N/mm[14] > 20 N/mm[14] 10[16] 10[16] 4.5 N/mm²[18] 4.5 N/mm²[18] 950 %[21] 950 %[21]
ELASTOSIL® M 1470 - - - - > 10 N/mm[13] > 10 N/mm[13] 45[17] 45[17] 4.5 N/mm²[19] 4.5 N/mm²[19] 230 %[22] 230 %[22]
ELASTOSIL® M 4115 A/B - - 2500 mPa·s[3] 2500 mPa·s[3] 5 N/mm[13] 5 N/mm[13] 17[16] 17[16] 3 N/mm²[18] 3 N/mm²[18] 400 %[21] 400 %[21]
ELASTOSIL® M 4125 F A/B - - 6000 mPa·s[3] 6000 mPa·s[3] - - 28[17] 28[17] 5.0[20] 5.0[20] 500[22] 500[22]
ELASTOSIL® M 4370 A/B - - 350 mPa·s[4] 350 mPa·s[4] > 4 N/mm[13] > 4 N/mm[13] 55[16] 55[16] 3.0 N/mm²[19] 3.0 N/mm²[19] 130 %[22] 130 %[22]
ELASTOSIL® M 4400 30000 mPa·s[5] 30000 mPa·s[5] - - > 3 N/mm[13] > 3 N/mm[13] 23[17] 23[17] 2 N/mm²[19] 2 N/mm²[19] 250 %[22] 250 %[22]
ELASTOSIL® M 4440 25000 mPa·s[6] 25000 mPa·s[6] - - 4.5 N/mm[13] 4.5 N/mm[13] 37[17] 37[17] 2.5 N/mm²[19] 2.5 N/mm²[19] 220 %[22] 220 %[22]
ELASTOSIL® M 4470 15000 mPa·s[7] 15000 mPa·s[7] - - > 4 N/mm[13] > 4 N/mm[13] 60[17] 60[17] 4.5 N/mm²[19] 4.5 N/mm²[19] 120 %[22] 120 %[22]
ELASTOSIL® M 4503 40000 mPa·s[8] 40000 mPa·s[8] - - > 20 N/mm[13] > 20 N/mm[13] 25[16] 25[16] 20 N/mm²[19] 20 N/mm²[19] 350 %[22] 350 %[22]
ELASTOSIL® M 4511 25000 mPa·s[9] 25000 mPa·s[9] - - > 18 N/mm[13] > 18 N/mm[13] 12[17] 12[17] 3.5 N/mm²[19] 3.5 N/mm²[19] 600 %[22] 600 %[22]
ELASTOSIL® M 4512 30000 mPa·s[9] 30000 mPa·s[9] - - > 24 N/mm[13] > 24 N/mm[13] 20[17] 20[17] 3.5 N/mm²[19] 3.5 N/mm²[19] 500 %[22] 500 %[22]
ELASTOSIL® M 4514 35000 mPa·s[8] 35000 mPa·s[8] - - > 25 N/mm[13] > 25 N/mm[13] 25[16] 25[16] 4.5 N/mm²[19] 4.5 N/mm²[19] 450 %[22] 450 %[22]
ELASTOSIL® M 4541 40000 mPa·s[8] 40000 mPa·s[8] - - > 30 N/mm[13] > 30 N/mm[13] 32[17] 32[17] 5 N/mm²[19] 5 N/mm²[19] 400 %[22] 400 %[22]
ELASTOSIL® M 4600 A/B 20000 mPa·s[8] 20000 mPa·s[8] - - > 20 N/mm[13] > 20 N/mm[13] 20[17] 20[17] 7[19] 7[19] 800 %[22] 800 %[22]
ELASTOSIL® M 4601 A/B 15000 mPa·s[8] 15000 mPa·s[8] - - > 30 N/mm[13] > 30 N/mm[13] 28[17] 28[17] 6.5 N/mm²[19] 6.5 N/mm²[19] 700 %[22] 700 %[22]
ELASTOSIL® M 4642 A/B 20000 mPa·s[8] 20000 mPa·s[8] - - > 30 N/mm[13] > 30 N/mm[13] 37[17] 37[17] 7 N/mm²[19] 7 N/mm²[19] 480 %[22] 480 %[22]
ELASTOSIL® M 4643 A/B 40000 mPa·s[8] 40000 mPa·s[8] - - > 10 N/mm[13] > 10 N/mm[13] 48[17] 48[17] 5 N/mm²[19] 5 N/mm²[19] 300 %[22] 300 %[22]
ELASTOSIL® M 4670 A/B 120000 mPa·s[8] 120000 mPa·s[8] - - 15 N/mm[13] 15 N/mm[13] 55[16] 55[16] 5.5 N/mm²[18] 5.5 N/mm²[18] 280 %[21] 280 %[21]
ELASTOSIL® RT 480 300000 - 400000 mPa·s[10] 300000 - 400000 mPa·s[10] - - > 7 N/mm[13] > 7 N/mm[13] 55[17] 55[17] 4.5 N/mm²[19] 4.5 N/mm²[19] 170 %[22] 170 %[22]
ELASTOSIL® RT 625 A/B 25000 mPa·s[7] 25000 mPa·s[7] - - 30 N/mm[13] 30 N/mm[13] 25[16] 25[16] 6.5 N/mm²[18] 6.5 N/mm²[18] 600 %[21] 600 %[21]
ELASTOSIL® RT 646 A/B 110000 mPa·s[11] 110000 mPa·s[11] - - 12 N/mm[13] 12 N/mm[13] 53[16] 53[16] 5 N/mm²[18] 5 N/mm²[18] 280 %[21] 280 %[21]
ELASTOSIL® RT K - - - - > 3 N/mm[15] > 3 N/mm[15] 45[17] 45[17] 2 N/mm²[19] 2 N/mm²[19] 130 %[22] 130 %[22]
ELASTOSIL® VARIO 15 5.000 mPa·s[12] 5.000 mPa·s[12] - - 15[13] 15[13] 15[16] 15[16] 6.5 N/mm²[18] 6.5 N/mm²[18] 900 %[21] 900 %[21]
ELASTOSIL® VARIO 40 15.000 mPa·s[12] 15.000 mPa·s[12] - - 15 N/mm[13] 15 N/mm[13] 40[16] 40[16] 8 N/mm²[18] 8 N/mm²[18] 450 %[21] 450 %[21]
Legend
[1] 动态粘度 | Brookfield,  [2] 动态粘度 23°C | ISO 3219,  [3] 动态粘度 | 23 °C | ISO 3219,  [4] 动态粘度 搅拌后 | 23 °C ,  [5] dynamische Viskosität nach Aufrühren | 23 °C | DIN EN ISO 3219,  [6] dynamische Viskosität after stirring | 23 °C | DIN EN ISO 3219,  [7] dynamische Viskosität after stirring | 23 °C | ISO 3219,  [8] dynamische Viskosität aufgerührt | 23 °C | ISO 3219,  [9] dynamische Viskosität aufgerührt | 23 °C | DIN EN ISO 3219,  [10] dynamische Viskosität | 23 °C | Brookfield,  [11] dynamische Viskosität | 23 °C | ISO 3219,  [12] dynamische Viskosität 23°C | ISO 3219,  [13] Weiterreißwiderstand | ASTM D 624 B,  [14] Weiterreißwiderstand | ASTM D 624, Die B,  [15] Weiterreißwiderstand | ASTM 624 B,  [16] Härte Shore A | DIN ISO 48-4,  [17] Härte Shore A | ISO 868,  [18] Reißfestigkeit | ISO 37 Type 1,  [19] Reißfestigkeit | ISO 37,  [20] Reißfestigkeit | DIN ISO 37,  [21] Reißdehnung | ISO 37 Type 1,  [22] Reißdehnung | ISO 37 

购物车

我的媒体


转至订单表

联系方式

Wacker Chemie AG
Gisela-Stein-Strasse 1
81671 Munich
+49  89  6279-0 （电话）

收藏夹

我的产品