ELASTOSIL® M 4645 A/B
Pourable, addition-curing, two-component silicone rubber that vulcanizes at room temperature.
Main application: Vacuum casting for rapid prototyping.
ELASTOSIL® M 4645 A/B
更多产品
| 个产品 | 技术数据 | ||||
|---|---|---|---|---|---|
| 动态粘度 | Tear-growth resistance | Shore density A | Breaking strength | 断裂伸长率 | |
| ELASTOSIL® M 4641 A/B | 50000 mPa·s[1] 50000 mPa·s[1] | > 25 N/mm[5] > 25 N/mm[5] | 43[6] 43[6] | > 4.5 N/mm²[8] > 4.5 N/mm²[8] | > 300 %[10] > 300 %[10] |
| ELASTOSIL® M 4644 A/B | 70000 mPa·s[2] 70000 mPa·s[2] | > 25 N/mm[5] > 25 N/mm[5] | 40[6] 40[6] | 5.5 N/mm²[8] 5.5 N/mm²[8] | 400 %[10] 400 %[10] |
| ELASTOSIL® M 4645 A/B | 50000 mPa·s[2] 50000 mPa·s[2] | > 28 N/mm[5] > 28 N/mm[5] | 40[6] 40[6] | 5 N/mm²[8] 5 N/mm²[8] | 330 %[10] 330 %[10] |
| ELASTOSIL® M 4670 A/B | 120000 mPa·s[2] 120000 mPa·s[2] | 15 N/mm[5] 15 N/mm[5] | 55[7] 55[7] | 5.5 N/mm²[9] 5.5 N/mm²[9] | 280 %[11] 280 %[11] |
| ELASTOSIL® VARIO 15 | 5.000 mPa·s[3] 5.000 mPa·s[3] | 15[5] 15[5] | 15[7] 15[7] | 6.5 N/mm²[9] 6.5 N/mm²[9] | 900 %[11] 900 %[11] |
| ELASTOSIL® VARIO 40 | 15.000 mPa·s[4] 15.000 mPa·s[4] | 15 N/mm[5] 15 N/mm[5] | 40[7] 40[7] | 8 N/mm²[9] 8 N/mm²[9] | 450 %[11] 450 %[11] |
说明
[1] 动态粘度 搅拌后 | 23 °C | ISO 3219, [2] 动态粘度 after stirring | 23 °C | ISO 3219, [3] 动态粘度 23°C, stirred | ISO 3219, [4] 动态粘度 23° C, stirred | ISO 3219, [5] Tear-growth resistance | ASTM D 624 B, [6] Shore density A | ISO 868, [7] Shore density A | DIN ISO 48-4, [8] Breaking strength | ISO 37, [9] Breaking strength | ISO 37 type 1, [10] 断裂伸长率 | ISO 37, [11] 断裂伸长率 | ISO 37 type 1
[1] 动态粘度 搅拌后 | 23 °C | ISO 3219, [2] 动态粘度 after stirring | 23 °C | ISO 3219, [3] 动态粘度 23°C, stirred | ISO 3219, [4] 动态粘度 23° C, stirred | ISO 3219, [5] Tear-growth resistance | ASTM D 624 B, [6] Shore density A | ISO 868, [7] Shore density A | DIN ISO 48-4, [8] Breaking strength | ISO 37, [9] Breaking strength | ISO 37 type 1, [10] 断裂伸长率 | ISO 37, [11] 断裂伸长率 | ISO 37 type 1