Appliances Industry

The outstanding properties of silicones make ELASTOSIL® products ideal for high-end applications such as white goods, household appliances, small appliances and kitchenware. The application determines whether room-temperature curing or heat-curing silicone elastomers are the best choice.
Product Recommendations
Products
|
Technical data
|
Product properties
|
|||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Hardness Shore A | Tensile strength | Elongation at break | Tear strength | Viscosity, dynamic | Compression Set | Resistance | Regulation | Product Rheology | Specific Features | Crosslinking Property | Vulcanizate | ||
20[10] 20[10] | 1.5 N/mm²[11] 1.5 N/mm²[11] | 300 %[16] 300 %[16] | 4.0 N/mm[1] 4.0 N/mm[1] | 8000 mPa·s[3] 8000 mPa·s[3] | - - | - | Solvent-based | Flowable | - | - | - | ||
35[10] 35[10] | 2.5 N/mm²[11] 2.5 N/mm²[11] | 200 %[16] 200 %[16] | 3.5 N/mm[1] 3.5 N/mm[1] | 25000 mPa·s[4] 25000 mPa·s[4] | - - | Heat resistant | - | - | - | - | - | ||
28[10] 28[10] | 2.5 N/mm²[11] 2.5 N/mm²[11] | 300 %[16] 300 %[16] | 7.8 N/mm[2] 7.8 N/mm[2] | 1000000 mPa·s[5] 1000000 mPa·s[5] | - - | Oil resistant | - | Non-slump | - | - | - | ||
20[10] 20[10] | 1.2 N/mm²[11] 1.2 N/mm²[11] | 300 %[16] 300 %[16] | 3.0 N/mm[1] 3.0 N/mm[1] | 40000 mPa·s[6] 40000 mPa·s[6] | - - | Oil resistant, Heat resistant | - | Self-levelling | - | - | - | ||
25[10] 25[10] | 2.5 N/mm²[12] 2.5 N/mm²[12] | 300 %[17] 300 %[17] | 8.0 N/mm[1] 8.0 N/mm[1] | - - | - - | Heat resistant | Solvent-free | Flowable | - | - | - | ||
32[10] 32[10] | 2.5 N/mm²[11] 2.5 N/mm²[11] | 400 %[16] 400 %[16] | 7 N/mm[1] 7 N/mm[1] | - - | - - | Heat resistant | MIL-A 46106 grade | Non-slump | - | - | - | ||
30[10] 30[10] | 5 N/mm²[13] 5 N/mm²[13] | 400 %[18] 400 %[18] | - - | - - | - - | - | Solvent-based | - | - | - | - | ||
15[10] 15[10] | 2 N/mm²[14] 2 N/mm²[14] | 750 %[19] 750 %[19] | 7.3 N/mm[1] 7.3 N/mm[1] | - - | - - | - | - | Non-slump | - | - | - | ||
40[10] 40[10] | 6.0 N/mm²[14] 6.0 N/mm²[14] | 350 %[19] 350 %[19] | 11.5 N/mm[1] 11.5 N/mm[1] | 100000 mPa·s[7] 100000 mPa·s[7] | - - | - | - | Self-levelling | - | - | - | ||
30[10] 30[10] | 6.5 N/mm²[15] 6.5 N/mm²[15] | 500 %[20] 500 %[20] | 11.5 N/mm[1] 11.5 N/mm[1] | 250000 mPa·s[4] 250000 mPa·s[4] | - - | - | Solvent-free | - | - | - | - | ||
30[10] 30[10] | 7.5 N/mm²[11] 7.5 N/mm²[11] | 500 %[16] 500 %[16] | - - | - - | - - | - | - | Thixotropic | - | - | - | ||
30[10] 30[10] | 7.8 N/mm²[11] 7.8 N/mm²[11] | 450 %[16] 450 %[16] | - - | - - | - - | - | - | Thixotropic | - | - | - | ||
30[10] 30[10] | 6.50 N/mm²[14] 6.50 N/mm²[14] | 500 %[19] 500 %[19] | 11.5 N/mm[1] 11.5 N/mm[1] | 250000 mPa·s[8] 250000 mPa·s[8] | - - | - | Solvent-free | - | - | - | - | ||
37[10] 37[10] | 4.5 N/mm²[15] 4.5 N/mm²[15] | 450 %[20] 450 %[20] | 10 N/mm[1] 10 N/mm[1] | 600000 mPa·s[8] 600000 mPa·s[8] | - - | - | MIL-A 46106 grade | Non-slump, Thixotropic | - | - | - | ||
35[10] 35[10] | 2.6 N/mm²[11] 2.6 N/mm²[11] | 200 %[16] 200 %[16] | - - | - - | - - | - | MIL-A 46106 grade | - | - | - | - | ||
35[10] 35[10] | 1.5 N/mm²[11] 1.5 N/mm²[11] | 150 %[16] 150 %[16] | 5.0 N/mm[1] 5.0 N/mm[1] | 50000 mPa·s[9] 50000 mPa·s[9] | - - | - | MIL-A 46106 grade | Self-levelling | - | - | - | ||
30[10] 30[10] | 2.1 N/mm²[11] 2.1 N/mm²[11] | 200 %[16] 200 %[16] | - - | - - | - - | - | - | - | - | - | - | ||
32[10] 32[10] | 3.0 N/mm²[11] 3.0 N/mm²[11] | 250 %[16] 250 %[16] | - - | - - | - - | - | - | - | - | - | - | ||
32[10] 32[10] | 3.2 N/mm²[11] 3.2 N/mm²[11] | 250 %[16] 250 %[16] | - - | - - | - - | - | - | - | - | - | - | ||
30[10] 30[10] | 7.5 N/mm²[11] 7.5 N/mm²[11] | 600 %[16] 600 %[16] | 20 N/mm[1] 20 N/mm[1] | - - | 10 %[21] 10 %[21] | - | - | - | Food-contact, Reduced volatile content | - | - | ||
25[10] 25[10] | 1 N/mm²[12] 1 N/mm²[12] | 200 %[18] 200 %[18] | - - | - - | - - | - | - | Shear thinning, Self-levelling | - | - | - | ||
35[10] 35[10] | 2 N/mm²[12] 2 N/mm²[12] | 200 %[18] 200 %[18] | - - | - - | - - | - | Flame retardant | - | - | - | - | ||
36[10] 36[10] | 1.6 N/mm²[11] 1.6 N/mm²[11] | 150 %[16] 150 %[16] | - - | - - | - - | - | Flame retardant | Flowable | - | - | - | ||
45[10] 45[10] | 1.5 N/mm²[12] 1.5 N/mm²[12] | 200 %[18] 200 %[18] | 5.0 N/mm[1] 5.0 N/mm[1] | - - | - - | Oil resistant, Heat resistant | Flame retardant | Non-slump | - | - | - | ||
30[10] 30[10] | 2.5 N/mm²[12] 2.5 N/mm²[12] | 400 %[18] 400 %[18] | 6.5 N/mm[1] 6.5 N/mm[1] | - - | - - | - | - | Non-slump | - | - | - | ||
30[10] 30[10] | 2.0 N/mm²[12] 2.0 N/mm²[12] | 450 %[17] 450 %[17] | 8.5 N/mm[2] 8.5 N/mm[2] | - - | - - | - | Flame retardant | Non-slump, Thixotropic | - | - | - | ||
30[10] 30[10] | 2.2 N/mm²[12] 2.2 N/mm²[12] | 500 %[17] 500 %[17] | 10 N/mm[2] 10 N/mm[2] | - - | - - | - | - | Non-slump, Thixotropic | - | - | - | ||
30[10] 30[10] | 2.20 N/mm²[12] 2.20 N/mm²[12] | 500 %[17] 500 %[17] | 10 N/mm[2] 10 N/mm[2] | - - | - - | - | Flame retardant | Non-slump, Thixotropic | - | - | - | ||
40[10] 40[10] | 2.8 N/mm²[11] 2.8 N/mm²[11] | 300 %[16] 300 %[16] | - - | - - | - - | Heat resistant | - | Shear thinning, Non-slump | - | - | - | ||
40[10] 40[10] | 6.1 N/mm²[11] 6.1 N/mm²[11] | 500 %[16] 500 %[16] | 10.1[1] 10.1[1] | - - | - - | Heat resistant | - | Thixotropic | - | One-component | Self-adhesive | ||
42[10] 42[10] | 3.0 N/mm²[11] 3.0 N/mm²[11] | 180 %[16] 180 %[16] | 4.6 N/mm[1] 4.6 N/mm[1] | - - | - - | Steam resistant, Heat resistant | - | Thixotropic | - | One-component | Self-adhesive | ||
32[10] 32[10] | 1.9 N/mm²[11] 1.9 N/mm²[11] | 180 %[16] 180 %[16] | 3.2 N/mm[1] 3.2 N/mm[1] | - - | - - | Steam resistant, Heat resistant | - | - | - | One-component | Self-adhesive | ||
45[10] 45[10] | 3.5 N/mm²[11] 3.5 N/mm²[11] | 200 %[16] 200 %[16] | - - | - - | - - | Steam resistant, Heat resistant | - | - | - | One-component | Self-adhesive | ||
42[10] 42[10] | 4.0 N/mm²[11] 4.0 N/mm²[11] | 250 %[16] 250 %[16] | 6.3 N/mm[1] 6.3 N/mm[1] | - - | - - | Steam resistant, Heat resistant | - | Thixotropic | - | One-component | Self-adhesive | ||
45[10] 45[10] | 1 N/mm²[11] 1 N/mm²[11] | 180 %[16] 180 %[16] | - - | - - | - - | Media resistant | - | Shear thinning, Thixotropic | - | Condensation-curing, Two-component | Self-adhesive, Electrically insulating | ||
32[10] 32[10] | 2.0 N/mm²[11] 2.0 N/mm²[11] | 130 %[16] 130 %[16] | 3.8 N/mm[1] 3.8 N/mm[1] | - - | - - | Heat resistant, Steam resistant | - | - | - | Condensation-curing, Two-component | Self-adhesive, Electrically insulating | ||
35[10] 35[10] | 1.2 N/mm²[11] 1.2 N/mm²[11] | 75 %[16] 75 %[16] | 4.7 N/mm[1] 4.7 N/mm[1] | - - | - - | Media resistant | - | Shear thinning, Thixotropic, Non-slump | - | Condensation-curing, Two-component | Self-adhesive, Compressible, Low density, Electrically insulating | ||
50[10] 50[10] | 3.5 N/mm²[11] 3.5 N/mm²[11] | 120 %[16] 120 %[16] | 7.0[1] 7.0[1] | - - | - - | Heat resistant | - | Shear thinning, Non-slump | - | Condensation-curing, Two-component, Fast curing at room temperature | Self-adhesive, Electrically insulating |
[1] Tear strength | ASTM D 624 B, [2] Tear strength | ASTM D 624 B | 23°C / 2mm, [3] Viscosity, dynamic | 23 °C | DIN EN ISO 2555 | Brookfield: spindle 3, 5 rpm, [4] Viscosity, dynamic D = 0,5 1/s | 25 °C | DIN EN ISO 3219, [5] Viscosity, dynamic | 25 °C | 0.5 1/s | DIN EN ISO 3219, [6] Viscosity, dynamic | 25 °C | DIN EN ISO 3219, [7] Viscosity, dynamic D = 1 1/s | 25 °C | DIN EN ISO 3219, [8] Viscosity, dynamic D = 0.5 1/s | 25 °C | DIN EN ISO 3219, [9] Viscosity, dynamic (2.5 rpm) | 23 °C | Brookfield, [10] Hardness Shore A | DIN ISO 48-4, [11] Tensile strength | ISO 37 type 1, [12] Tensile strength | ISO 37 | Type 3 / 23°C / 2mm, [13] Tensile strength | ISO 37 | Type 3 / 23 °C / d = 2 mm, [14] Tensile strength | ISO 37 type 1 | Type 3 / 23°C / 2mm, [15] Tensile strength | ISO 37 type 1 | Type 3 /23°C / 2mm, [16] Elongation at break | ISO 37 type 1, [17] Elongation at break | ISO 37 | Type 3 / 23°C / 2mm, [18] Elongation at break | ISO 37, [19] Elongation at break | ISO 37 type 1 | Type 3 / 23°C / 2mm, [20] Elongation at break | ISO 37 type 1 | Type 3 /23°C / 2mm, [21] Compression Set | 22 h | 175 °C | DIN ISO 815-1 type B method A | post-cured 6 h / 200 °C, [] Suited, [] Well suited, [] Ideally suited