ELASTOSIL® RT 563

ELASTOSIL® RT 563 is a pourable, room-temperature-vulcanizing, condensation-curing, two-component silicone rubber.

 

Main application: encapsulation of electronic components


特性

  • Excellent flow
  • High hardness

ELASTOSIL® RT 563的特殊性能

  • 双组分
  • 易流动的
  • 缩合固化
  •  Encapsulation of electronic components

ELASTOSIL® RT 563 is cured by adding Catalyst T37 for long pot lives and curing times, or Catalyst T40 for short pot lives and curing times.


The pot life is the period of time at 23 °C / 50 % rel. humidity during which the catalyzed mix to attain a viscosity of 100,000 mPa s and still be just pourable


Catalyst T 37 and T 40 act as solvents until curing is complete. Preliminary tests must therefore be carried out to ensure that they are compatible with the components.


Please check also our brochures and info sheets.

储存

The 'Best use before end' date of each batch is shown on the product label.

 

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemicals Middle East
Dubai Silicon Oasis s/n
0001 Dubai
阿拉伯联合酋长国
+971  4  709-9999 （电话）
+971 4 709-9911  （传真）
Contact Sales

我们可以为您提供什么帮助？

  • 您在选择产品方面需要帮助或者需要技术咨询？ 请联系我们的专家
Ask a question

Would you like a product sample?

You can request a product sample here.

Request sample

更多产品

个产品 技术数据
动态粘度 Tear strength Hardness Shore A 邵氏00硬度 Tensile strength Elongation at break 断裂伸长率
ELASTOSIL® RT 426 - - > 4 N/mm[1] > 4 N/mm[1] 60[2] 60[2] - - 4.5 N/mm²[5] 4.5 N/mm²[5] 120 %[8] 120 %[8] - -
ELASTOSIL® RT 563 - - 3 N/mm[1] 3 N/mm[1] 55[2] 55[2] - - 4.5 N/mm²[5] 4.5 N/mm²[5] - - 120 %[9] 120 %[9]
ELASTOSIL® RT 602 A/B 5000 mPa·s[12] 5000 mPa·s[12] - - 30[3] 30[3] - - 1.5 N/mm²[6] 1.5 N/mm²[6] - - 130 %[10] 130 %[10]
ELASTOSIL® RT 607 A/B 15000 mPa·s[13] 15000 mPa·s[13] - - 55[3] 55[3] - - 3 N/mm²[6] 3 N/mm²[6] - - 100 %[10] 100 %[10]
ELASTOSIL® RT 622 A/B 18000.0 mPa·s[14] 18000.0 mPa·s[14] 30 N/mm[1] 30 N/mm[1] 27[4] 27[4] - - 6.5 N/mm²[7] 6.5 N/mm²[7] - - 550 %[11] 550 %[11]
ELASTOSIL® SOLAR 2205 - - - - - - 50[16] 50[16] - - - - - -
SEMICOSIL® 949 UV A 150.0 mPa·s[15] 150.0 mPa·s[15] - - - - 40[17] 40[17] - - - - - -
SEMICOSIL® 949 UV B 150.0 mPa·s[15] 150.0 mPa·s[15] - - - - 40[17] 40[17] - - - - - -
说明
[1] Tear strength | ASTM D 624 B,  [2] Hardness Shore A | ISO 868,  [3] Hardness Shore A | DIN ISO 48-4,  [4] Hardness Shore A | DIN 53505 / ISO 868,  [5] Tensile strength | ISO 37,  [6] Tensile strength | ISO 37 type 1,  [7] Tensile strength | DIN 53504 S1 / ISO 37,  [8] Elongation at break | ISO 37,  [9] 断裂伸长率 | ISO 37,  [10] 断裂伸长率 | ISO 37 type 1,  [11] 断裂伸长率 | DIN 53504 S1 / ISO 37,  [12] 动态粘度 | 23 °C | ISO 3219,  [13] 动态粘度 | 23 °C | DIN EN ISO 3219,  [14] 动态粘度 搅拌后 | 23 °C | DIN EN ISO 3219 | Spindle 4; 2,5 UpM; 23 °C,  [15] 动态粘度 | 25.0 °C | DIN EN ISO 3219,  [16] 邵氏00硬度 | ASTM D 2240,  [17] Shore 00 | 23 °C | ASTM D 2240 | 10 sec 140 mW/cm² followed by 30 min 150°C 