POWERSIL® 732 CS A/B
POWERSIL® 732 CS A/B is a two-component, liquid silicone rubber with excellent processing properties. Its vulcanizates are noted for their excellent mechanical and electrical properties. POWERSIL® 732 CS A/B is especially designed for cold shrink applications.
POWERSIL® 732 CS A/B
更多产品
个产品 | 技术数据 | |||||||
---|---|---|---|---|---|---|---|---|
外观 | Shore density A | Breaking strength | Reißfestigkeit | Reißdehnung | 断裂伸长率 | Tear-growth resistance | 压缩变形 | |
ELASTOSIL® LR 3002/35 A/B | colourless colourless | 33[1] 33[1] | 7.0 N/mm²[2] 7.0 N/mm²[2] | - - | 460 %[5] 460 %[5] | - - | 29 N/mm[7] 29 N/mm[7] | 11 %[8] 11 %[8] |
ELASTOSIL® LR 3003/20 TR A/B | transparent transparent | 22[1] 22[1] | 8.3 N/mm²[2] 8.3 N/mm²[2] | - - | 870 %[5] 870 %[5] | - - | 24 N/mm[7] 24 N/mm[7] | 17 %[8] 17 %[8] |
ELASTOSIL® LR 3003/30 A/B | transparent transparent | 30[1] 30[1] | 7.0 N/mm²[2] 7.0 N/mm²[2] | - - | 610 %[5] 610 %[5] | - - | 21 N/mm[7] 21 N/mm[7] | 10 %[8] 10 %[8] |
ELASTOSIL® LR 3003/40 A/B | transparent transparent | 40[1] 40[1] | 10.0 N/mm²[2] 10.0 N/mm²[2] | - - | 610 %[5] 610 %[5] | - - | 30 N/mm[7] 30 N/mm[7] | 11 %[8] 11 %[8] |
ELASTOSIL® LR 3003/50 A/B | transparent transparent | 50[1] 50[1] | 10.3 N/mm²[2] 10.3 N/mm²[2] | - - | 490 %[5] 490 %[5] | - - | 26 N/mm[7] 26 N/mm[7] | 13 %[8] 13 %[8] |
ELASTOSIL® LR 3003/60 A/B | transparent transparent | 60[1] 60[1] | 9.8 N/mm²[2] 9.8 N/mm²[2] | - - | 340 %[5] 340 %[5] | - - | 27 N/mm[7] 27 N/mm[7] | 16 %[8] 16 %[8] |
ELASTOSIL® LR 3003/70 A/B | transparent transparent | 70[1] 70[1] | 9.3 N/mm²[2] 9.3 N/mm²[2] | - - | 290 %[5] 290 %[5] | - - | 20 N/mm[7] 20 N/mm[7] | 16 %[8] 16 %[8] |
ELASTOSIL® LR 3004/40 A/B | transparent transparent | 40[1] 40[1] | 9.2 N/mm²[2] 9.2 N/mm²[2] | - - | 610 %[5] 610 %[5] | - - | 29 N/mm[7] 29 N/mm[7] | 10 %[8] 10 %[8] |
ELASTOSIL® LR 3005/60 A/B | transparent transparent | 60[1] 60[1] | 9.5 N/mm²[3] 9.5 N/mm²[3] | - - | - - | 380 %[6] 380 %[6] | 28 N/mm[7] 28 N/mm[7] | 15 %[9] 15 %[9] |
ELASTOSIL® LR 3043/40 A/B | transparent transparent | 40[1] 40[1] | - - | 9.8 N/mm²[4] 9.8 N/mm²[4] | - - | 660 %[6] 660 %[6] | 36 N/mm[7] 36 N/mm[7] | 25 %[8] 25 %[8] |
POWERSIL® 466 A/B | black black | 38[1] 38[1] | - - | 7.0 N/mm²[4] 7.0 N/mm²[4] | - - | 650 %[6] 650 %[6] | 28 N/mm[7] 28 N/mm[7] | 11 %[8] 11 %[8] |
POWERSIL® 466 LV A/B | black black | 35[1] 35[1] | - - | 7.0 N/mm²[4] 7.0 N/mm²[4] | - - | 650 %[6] 650 %[6] | 20 N/mm[7] 20 N/mm[7] | 11 %[8] 11 %[8] |
POWERSIL® 730 A/B | white white | 35[1] 35[1] | - - | 8.0 N/mm²[4] 8.0 N/mm²[4] | - - | 600 %[6] 600 %[6] | 26 N/mm[7] 26 N/mm[7] | - - |
POWERSIL® 732 CS A/B | transparent transparent | 33[1] 33[1] | - - | 9.0 N/mm²[4] 9.0 N/mm²[4] | - - | 750 %[6] 750 %[6] | 35 N/mm[7] 35 N/mm[7] | - - |
POWERSIL® 735 LIGHTGRAY A/B | gray gray | 39[1] 39[1] | - - | 8.0 N/mm²[4] 8.0 N/mm²[4] | - - | 500 %[6] 500 %[6] | 30 N/mm[7] 30 N/mm[7] | - - |
POWERSIL® 740 DARK GRAY A/B | gray gray | 40[1] 40[1] | - - | 9.8 N/mm²[4] 9.8 N/mm²[4] | - - | 650 %[6] 650 %[6] | 35 N/mm[7] 35 N/mm[7] | - - |
POWERSIL® 740 LIGHTGRAY A/B | gray gray | 40[1] 40[1] | - - | 9.8 N/mm²[4] 9.8 N/mm²[4] | - - | 650 %[6] 650 %[6] | 35 N/mm[7] 35 N/mm[7] | - - |
POWERSIL® XLR® 630 A/B | light gray light gray | 35[1] 35[1] | - - | 7.0 N/mm²[4] 7.0 N/mm²[4] | - - | 450 %[6] 450 %[6] | 25 N/mm[7] 25 N/mm[7] | - - |
说明
[1] Shore density A | DIN ISO 48-4, [2] Breaking strength | ISO 37 type 1, [3] Breaking strength | ISO 37 Type 1, [4] Reißfestigkeit | ISO 37 Type 1, [5] Reißdehnung | ISO 37 Type 1, [6] 断裂伸长率 | ISO 37 type 1, [7] Tear-growth resistance | ASTM D 624 B, [8] 压缩变形 | 22 h | 175 °C | DIN ISO 815-1 type B method A | post-cured 6 h / 200 °C, [9] 压缩变形 | 22 h | 175 °C | DIN ISO 815-1 type B method A
[1] Shore density A | DIN ISO 48-4, [2] Breaking strength | ISO 37 type 1, [3] Breaking strength | ISO 37 Type 1, [4] Reißfestigkeit | ISO 37 Type 1, [5] Reißdehnung | ISO 37 Type 1, [6] 断裂伸长率 | ISO 37 type 1, [7] Tear-growth resistance | ASTM D 624 B, [8] 压缩变形 | 22 h | 175 °C | DIN ISO 815-1 type B method A | post-cured 6 h / 200 °C, [9] 压缩变形 | 22 h | 175 °C | DIN ISO 815-1 type B method A