Moldmaking & Prototype Molding
ELASTOSIL® RTV-2 silicone elastomers for mold making yield highly accurate reproductions, exhibit good release properties and are highly resistant to common reproduction materials. Applications of ELASTOSIL® M and RT range from arts and crafts to industrial mass production.
Industrial Printing
WACKER offers a high-quality product range of ELASTOSIL® RT silicone rubber grades for pad printing processes of all types. Anti-static variants for printing on sensitive materials and additional ELASTOSIL® systems round off our portfolio of high-performance products.
More about
English
Download
Product Recommendations
Table is scrollable
|
Products
|
Technical data
|
Product properties
|
|||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Viscosity, dynamic | Tear strength | Hardness Shore A | Hardness Shore 00 | Tensile strength | Elongation at break | Resistance | Surface property | Regulation | Product Rheology | Crosslinking Property | Vulcanizate | ||
| 3000 mPa·s[1] 3000 mPa·s[1] | 15 N/mm[13] 15 N/mm[13] | 10[16] 10[16] | - - | 3.5 N/mm²[19] 3.5 N/mm²[19] | 600 %[22] 600 %[22] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 6000 mPa·s[2] 6000 mPa·s[2] | - - | 20[16] 20[16] | - - | 4 N/mm²[19] 4 N/mm²[19] | 500 %[22] 500 %[22] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 8000 mPa·s[3] 8000 mPa·s[3] | 20 N/mm[13] 20 N/mm[13] | 25[16] 25[16] | - - | 5 N/mm²[19] 5 N/mm²[19] | 450 %[22] 450 %[22] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 8000 mPa·s[3] 8000 mPa·s[3] | > 20 N/mm[13] > 20 N/mm[13] | 26[16] 26[16] | - - | 5 N/mm²[19] 5 N/mm²[19] | 500 %[22] 500 %[22] | Resistance against concrete | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 20000 mPa·s[3] 20000 mPa·s[3] | 25 N/mm[13] 25 N/mm[13] | 25[16] 25[16] | - - | 5 N/mm²[19] 5 N/mm²[19] | 500 %[22] 500 %[22] | Resistance against polyester, Resistance against epoxy resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 26000 mPa·s[4] 26000 mPa·s[4] | 25 N/mm[13] 25 N/mm[13] | 27[17] 27[17] | - - | 5 N/mm²[20] 5 N/mm²[20] | - - | - | - | - | - | - | - | ||
| - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| 6000 mPa·s[3] 6000 mPa·s[3] | > 20 N/mm[14] > 20 N/mm[14] | 10[16] 10[16] | - - | 4.5 N/mm²[19] 4.5 N/mm²[19] | 950 %[22] 950 %[22] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 5000 mPa·s[5] 5000 mPa·s[5] | 25 N/mm[14] 25 N/mm[14] | 20[16] 20[16] | - - | > 6 N/mm²[19] > 6 N/mm²[19] | > 750 %[22] > 750 %[22] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 10000 mPa·s[5] 10000 mPa·s[5] | 28 N/mm[13] 28 N/mm[13] | 28[16] 28[16] | - - | 6 N/mm²[19] 6 N/mm²[19] | 500 %[22] 500 %[22] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 4000 mPa·s[5] 4000 mPa·s[5] | 5.5 N/mm[14] 5.5 N/mm[14] | - - | 30[24] 30[24] | > 1.5 N/mm²[19] > 1.5 N/mm²[19] | > 900 %[22] > 900 %[22] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| - - | > 10 N/mm[13] > 10 N/mm[13] | 45[17] 45[17] | - - | 4.5 N/mm²[20] 4.5 N/mm²[20] | 230 %[23] 230 %[23] | Heat resistant | - | - | Kneadable | Condensation-curing, Two-component | - | ||
| 2500 mPa·s[3] 2500 mPa·s[3] | 5 N/mm[13] 5 N/mm[13] | 17[16] 17[16] | - - | 3 N/mm²[19] 3 N/mm²[19] | 400 %[22] 400 %[22] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 6000 mPa·s[3] 6000 mPa·s[3] | - - | 28[17] 28[17] | - - | 5.0[21] 5.0[21] | 500[23] 500[23] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 350 mPa·s[6] 350 mPa·s[6] | > 4 N/mm[13] > 4 N/mm[13] | 55[16] 55[16] | - - | 3.0 N/mm²[20] 3.0 N/mm²[20] | 130 %[23] 130 %[23] | Heat resistant, Resistance against casting resins, Resistance against low melting metals and metal alloys | - | - | Flowable | Two-component, Addition Curing | - | ||
| 30000 mPa·s[7] 30000 mPa·s[7] | > 3 N/mm[13] > 3 N/mm[13] | 23[17] 23[17] | - - | 2 N/mm²[20] 2 N/mm²[20] | 250 %[23] 250 %[23] | - | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 25000 mPa·s[7] 25000 mPa·s[7] | 4.5 N/mm[13] 4.5 N/mm[13] | 37[17] 37[17] | - - | 2.5 N/mm²[20] 2.5 N/mm²[20] | 220 %[23] 220 %[23] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 15000 mPa·s[5] 15000 mPa·s[5] | > 4 N/mm[13] > 4 N/mm[13] | 60[17] 60[17] | - - | 4.5 N/mm²[20] 4.5 N/mm²[20] | 120 %[23] 120 %[23] | Heat resistant | - | - | Flowable | Condensation-curing, Two-component | Thermally conductive | ||
| 40000 mPa·s[5] 40000 mPa·s[5] | > 20 N/mm[13] > 20 N/mm[13] | 25[16] 25[16] | - - | 20 N/mm²[20] 20 N/mm²[20] | 350 %[23] 350 %[23] | - | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 25000 mPa·s[7] 25000 mPa·s[7] | > 18 N/mm[13] > 18 N/mm[13] | 12[17] 12[17] | - - | 3.5 N/mm²[20] 3.5 N/mm²[20] | 600 %[23] 600 %[23] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 30000 mPa·s[7] 30000 mPa·s[7] | > 24 N/mm[13] > 24 N/mm[13] | 20[17] 20[17] | - - | 3.5 N/mm²[20] 3.5 N/mm²[20] | 500 %[23] 500 %[23] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 35000 mPa·s[5] 35000 mPa·s[5] | > 25 N/mm[13] > 25 N/mm[13] | 25[16] 25[16] | - - | 4.5 N/mm²[20] 4.5 N/mm²[20] | 450 %[23] 450 %[23] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 40000 mPa·s[5] 40000 mPa·s[5] | > 30 N/mm[13] > 30 N/mm[13] | 32[17] 32[17] | - - | 5 N/mm²[20] 5 N/mm²[20] | 400 %[23] 400 %[23] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 20000 mPa·s[5] 20000 mPa·s[5] | > 20 N/mm[13] > 20 N/mm[13] | 20[17] 20[17] | - - | 7[20] 7[20] | 800 %[23] 800 %[23] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 25000 cP[3] 25000 cP[3] | 31.5 N/mm[13] 31.5 N/mm[13] | 20[17] 20[17] | - - | 7.00 N/mm²[20] 7.00 N/mm²[20] | 800 %[23] 800 %[23] | - | - | - | - | - | - | ||
| 15000 mPa·s[5] 15000 mPa·s[5] | > 30 N/mm[13] > 30 N/mm[13] | 28[17] 28[17] | - - | 6.5 N/mm²[20] 6.5 N/mm²[20] | 700 %[23] 700 %[23] | Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 25000 mPa·s[8] 25000 mPa·s[8] | > 170 lb/in[13] > 170 lb/in[13] | 28[17] 28[17] | - - | 940 psi[20] 940 psi[20] | 700 %[23] 700 %[23] | - | - | - | - | - | - | ||
| 15000 mPa·s[5] 15000 mPa·s[5] | > 30 N/mm[13] > 30 N/mm[13] | 28[17] 28[17] | - - | 6.5 N/mm²[20] 6.5 N/mm²[20] | 700 %[23] 700 %[23] | Resistance against concrete, Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 12000 mPa·s[9] 12000 mPa·s[9] | 170 lb/in[15] 170 lb/in[15] | 20[17] 20[17] | - - | 740 psi[20] 740 psi[20] | 640 %[23] 640 %[23] | - | - | - | - | - | - | ||
| 20000 mPa·s[5] 20000 mPa·s[5] | > 30 N/mm[13] > 30 N/mm[13] | 37[17] 37[17] | - - | 7 N/mm²[20] 7 N/mm²[20] | 480 %[23] 480 %[23] | Resistance against concrete, Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 20000 mPa·s[10] 20000 mPa·s[10] | 170 ppi[15] 170 ppi[15] | 37[17] 37[17] | - - | 950 psi[20] 950 psi[20] | 480 %[23] 480 %[23] | - | - | - | - | - | - | ||
| 50000 mPa·s[5] 50000 mPa·s[5] | > 25 N/mm[13] > 25 N/mm[13] | 43[17] 43[17] | - - | > 4.5 N/mm²[20] > 4.5 N/mm²[20] | > 300 %[23] > 300 %[23] | Resistance against PU | Dry surface | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | Highly transparent | ||
| 60000 cP[3] 60000 cP[3] | > 24.5 N/mm[13] > 24.5 N/mm[13] | 43[18] 43[18] | - - | > 4.50 N/mm²[20] > 4.50 N/mm²[20] | > 300 %[23] > 300 %[23] | - | - | - | - | - | - | ||
| 20000 mPa·s[5] 20000 mPa·s[5] | > 30 N/mm[13] > 30 N/mm[13] | 37[17] 37[17] | - - | 7 N/mm²[20] 7 N/mm²[20] | 480 %[23] 480 %[23] | Resistance against casting resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 40000 mPa·s[5] 40000 mPa·s[5] | > 10 N/mm[13] > 10 N/mm[13] | 48[17] 48[17] | - - | 5 N/mm²[20] 5 N/mm²[20] | 300 %[23] 300 %[23] | Resistance against casting resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 70000 mPa·s[5] 70000 mPa·s[5] | > 25 N/mm[13] > 25 N/mm[13] | 40[17] 40[17] | - - | 5.5 N/mm²[20] 5.5 N/mm²[20] | 400 %[23] 400 %[23] | Resistance against PU | Slightly oil bleeding | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | Highly transparent | ||
| 50000 mPa·s[5] 50000 mPa·s[5] | > 28 N/mm[13] > 28 N/mm[13] | 40[17] 40[17] | - - | 5 N/mm²[20] 5 N/mm²[20] | 330 %[23] 330 %[23] | Resistance against PU | Strong oil bleeding | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | Highly transparent | ||
| 120000 mPa·s[5] 120000 mPa·s[5] | 15 N/mm[13] 15 N/mm[13] | 55[16] 55[16] | - - | 5.5 N/mm²[19] 5.5 N/mm²[19] | 280 %[22] 280 %[22] | Resistance against polyester, Resistance against epoxy resins, Resistance against PU | Dry surface | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 150000 mPa·s[5] 150000 mPa·s[5] | > 68 lb/in[13] > 68 lb/in[13] | 55[18] 55[18] | - - | 795[20] 795[20] | 300 %[23] 300 %[23] | - | - | - | - | - | - | ||
| 14000 mPa·s[10] 14000 mPa·s[10] | 140 ppi[15] 140 ppi[15] | 22[17] 22[17] | - - | 950 psi[20] 950 psi[20] | 580 %[23] 580 %[23] | - | - | - | Flowable | Fast curing under heat, Two-component, Addition Curing | - | ||
| 17000 mPa·s[10] 17000 mPa·s[10] | 110 ppi[15] 110 ppi[15] | 30[17] 30[17] | - - | 900 psi[20] 900 psi[20] | 400 %[23] 400 %[23] | - | - | - | - | - | - | ||
| 300000 - 400000 mPa·s[10] 300000 - 400000 mPa·s[10] | > 7 N/mm[13] > 7 N/mm[13] | 55[17] 55[17] | - - | 4.5 N/mm²[20] 4.5 N/mm²[20] | 170 %[23] 170 %[23] | - | - | - | Spreadable self-levelling flow | Condensation-curing, Two-component, Fast curing at room temperature | - | ||
| 25000 mPa·s[10] 25000 mPa·s[10] | 170 ppi[15] 170 ppi[15] | 31[17] 31[17] | - - | 1000 psi[20] 1000 psi[20] | 700 %[23] 700 %[23] | - | - | - | - | - | - | ||
| 25000 mPa·s[5] 25000 mPa·s[5] | 30 N/mm[13] 30 N/mm[13] | 25[16] 25[16] | - - | 6.5 N/mm²[19] 6.5 N/mm²[19] | 600 %[22] 600 %[22] | - | - | - | Flowable | Two-component, Addition Curing | - | ||
| 110000 mPa·s[3] 110000 mPa·s[3] | 12 N/mm[13] 12 N/mm[13] | 53[16] 53[16] | - - | 5 N/mm²[19] 5 N/mm²[19] | 280 %[22] 280 %[22] | Resistance against casting resins | - | - | Flowable | Two-component, Addition Curing | - | ||
| - - | > 3 N/mm[15] > 3 N/mm[15] | 45[17] 45[17] | - - | 2 N/mm²[20] 2 N/mm²[20] | 130 %[23] 130 %[23] | - | - | - | - | Condensation-curing, Two-component | - | ||
| 5.000 mPa·s[11] 5.000 mPa·s[11] | 15[13] 15[13] | 15[16] 15[16] | - - | 6.5 N/mm²[19] 6.5 N/mm²[19] | 900 %[22] 900 %[22] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 15.000 mPa·s[12] 15.000 mPa·s[12] | 15 N/mm[13] 15 N/mm[13] | 40[16] 40[16] | - - | 8 N/mm²[19] 8 N/mm²[19] | 450 %[22] 450 %[22] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
Legend
[1] Viscosity, dynamic | Brookfield, [2] Viscosity, dynamic 23°C | ISO 3219, [3] Viscosity, dynamic | 23 °C | ISO 3219, [4] Viscosity, dynamic | 23 °C , [5] Viscosity, dynamic after stirring | 23 °C | ISO 3219, [6] Viscosity, dynamic after stirring | 23 °C , [7] Viscosity, dynamic after stirring | 23 °C | DIN EN ISO 3219, [8] Viscosity, dynamic after stirring | 23 °C | Brookfield, [9] Viscosity, dynamic | 22 °C | ISO 3219, [10] Viscosity, dynamic | 23 °C | Brookfield, [11] Viscosity, dynamic 23°C, stirred | ISO 3219, [12] Viscosity, dynamic 23° C, stirred | ISO 3219, [13] Tear strength | ASTM D 624 B, [14] Tear strength | ASTM D 624, Die B, [15] Tear strength | ASTM 624 B, [16] Hardness Shore A | DIN ISO 48-4, [17] Hardness Shore A | ISO 868, [18] Hardness Shore A | ISO 867, [19] Tensile strength | ISO 37 type 1, [20] Tensile strength | ISO 37, [21] Tensile strength | DIN ISO 37, [22] Elongation at break | ISO 37 type 1, [23] Elongation at break | ISO 37, [24] Hardness Shore 00 | ASTM D 2240
[1] Viscosity, dynamic | Brookfield, [2] Viscosity, dynamic 23°C | ISO 3219, [3] Viscosity, dynamic | 23 °C | ISO 3219, [4] Viscosity, dynamic | 23 °C , [5] Viscosity, dynamic after stirring | 23 °C | ISO 3219, [6] Viscosity, dynamic after stirring | 23 °C , [7] Viscosity, dynamic after stirring | 23 °C | DIN EN ISO 3219, [8] Viscosity, dynamic after stirring | 23 °C | Brookfield, [9] Viscosity, dynamic | 22 °C | ISO 3219, [10] Viscosity, dynamic | 23 °C | Brookfield, [11] Viscosity, dynamic 23°C, stirred | ISO 3219, [12] Viscosity, dynamic 23° C, stirred | ISO 3219, [13] Tear strength | ASTM D 624 B, [14] Tear strength | ASTM D 624, Die B, [15] Tear strength | ASTM 624 B, [16] Hardness Shore A | DIN ISO 48-4, [17] Hardness Shore A | ISO 868, [18] Hardness Shore A | ISO 867, [19] Tensile strength | ISO 37 type 1, [20] Tensile strength | ISO 37, [21] Tensile strength | DIN ISO 37, [22] Elongation at break | ISO 37 type 1, [23] Elongation at break | ISO 37, [24] Hardness Shore 00 | ASTM D 2240