制模和原型制造
制模行业用ELASTOSIL® RTV-2有机硅弹性体具有极为准确的复制效果和出色的脱模性能，同时对各种常见的复制材料都有很高的耐受性。ELASTOSIL® M和ELASTOSIL® RT产品系列的应用范围非常广泛：从艺术到手工艺再到工业化大规模生产。
English
Download
Product Recommendations
Table is scrollable
|
Products
|
Technical data
|
Product properties
|
|||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 动态粘度 | Tear strength | Hardness Shore A | Hardness Shore 00 | Tensile strength | Elongation at break | Resistance | Surface property | Regulation | Product Rheology | Crosslinking Property | Vulcanizate | ||
| 3000 mPa·s[1] 3000 mPa·s[1] | 15 N/mm[11] 15 N/mm[11] | 10[14] 10[14] | - - | 3.5 N/mm²[16] 3.5 N/mm²[16] | 600 %[19] 600 %[19] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 6000 mPa·s[2] 6000 mPa·s[2] | - - | 20[14] 20[14] | - - | 4 N/mm²[16] 4 N/mm²[16] | 500 %[19] 500 %[19] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 8000 mPa·s[3] 8000 mPa·s[3] | 20 N/mm[11] 20 N/mm[11] | 25[14] 25[14] | - - | 5 N/mm²[16] 5 N/mm²[16] | 450 %[19] 450 %[19] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 8000 mPa·s[3] 8000 mPa·s[3] | > 20 N/mm[11] > 20 N/mm[11] | 26[14] 26[14] | - - | 5 N/mm²[16] 5 N/mm²[16] | 500 %[19] 500 %[19] | Resistance against concrete | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 20000 mPa·s[3] 20000 mPa·s[3] | 25 N/mm[11] 25 N/mm[11] | 25[14] 25[14] | - - | 5 N/mm²[16] 5 N/mm²[16] | 500 %[19] 500 %[19] | Resistance against polyester, Resistance against epoxy resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| - - | - - | - - | - - | - - | - - | - | - | - | - | - | - | ||
| 6000 mPa·s[3] 6000 mPa·s[3] | > 20 N/mm[12] > 20 N/mm[12] | 10[14] 10[14] | - - | 4.5 N/mm²[16] 4.5 N/mm²[16] | 950 %[19] 950 %[19] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 5000 mPa·s[4] 5000 mPa·s[4] | 25 N/mm[12] 25 N/mm[12] | 20[14] 20[14] | - - | > 6 N/mm²[16] > 6 N/mm²[16] | > 750 %[19] > 750 %[19] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 10000 mPa·s[4] 10000 mPa·s[4] | 28 N/mm[11] 28 N/mm[11] | 28[14] 28[14] | - - | 6 N/mm²[16] 6 N/mm²[16] | 500 %[19] 500 %[19] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 4000 mPa·s[4] 4000 mPa·s[4] | 5.5 N/mm[12] 5.5 N/mm[12] | - - | 30[21] 30[21] | > 1.5 N/mm²[16] > 1.5 N/mm²[16] | > 900 %[19] > 900 %[19] | - | - | Suitable for skin contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| - - | > 10 N/mm[11] > 10 N/mm[11] | 45[15] 45[15] | - - | 4.5 N/mm²[17] 4.5 N/mm²[17] | 230 %[20] 230 %[20] | Heat resistant | - | - | Kneadable | Condensation-curing, Two-component | - | ||
| 2500 mPa·s[3] 2500 mPa·s[3] | 5 N/mm[11] 5 N/mm[11] | 17[14] 17[14] | - - | 3 N/mm²[16] 3 N/mm²[16] | 400 %[19] 400 %[19] | - | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 6000 mPa·s[3] 6000 mPa·s[3] | - - | 28[15] 28[15] | - - | 5.0[18] 5.0[18] | 500[20] 500[20] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing, Fast curing at room temperature | - | ||
| 350 mPa·s[5] 350 mPa·s[5] | > 4 N/mm[11] > 4 N/mm[11] | 55[14] 55[14] | - - | 3.0 N/mm²[17] 3.0 N/mm²[17] | 130 %[20] 130 %[20] | Heat resistant, Resistance against casting resins, Resistance against low melting metals and metal alloys | - | - | Flowable | Two-component, Addition Curing | - | ||
| 30000 mPa·s[6] 30000 mPa·s[6] | > 3 N/mm[11] > 3 N/mm[11] | 23[15] 23[15] | - - | 2 N/mm²[17] 2 N/mm²[17] | 250 %[20] 250 %[20] | - | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 25000 mPa·s[6] 25000 mPa·s[6] | 4.5 N/mm[11] 4.5 N/mm[11] | 37[15] 37[15] | - - | 2.5 N/mm²[17] 2.5 N/mm²[17] | 220 %[20] 220 %[20] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 15000 mPa·s[4] 15000 mPa·s[4] | > 4 N/mm[11] > 4 N/mm[11] | 60[15] 60[15] | - - | 4.5 N/mm²[17] 4.5 N/mm²[17] | 120 %[20] 120 %[20] | Heat resistant | - | - | Flowable | Condensation-curing, Two-component | Thermally conductive | ||
| 40000 mPa·s[4] 40000 mPa·s[4] | > 20 N/mm[11] > 20 N/mm[11] | 25[14] 25[14] | - - | 20 N/mm²[17] 20 N/mm²[17] | 350 %[20] 350 %[20] | - | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 25000 mPa·s[6] 25000 mPa·s[6] | > 18 N/mm[11] > 18 N/mm[11] | 12[15] 12[15] | - - | 3.5 N/mm²[17] 3.5 N/mm²[17] | 600 %[20] 600 %[20] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 30000 mPa·s[6] 30000 mPa·s[6] | > 24 N/mm[11] > 24 N/mm[11] | 20[15] 20[15] | - - | 3.5 N/mm²[17] 3.5 N/mm²[17] | 500 %[20] 500 %[20] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 35000 mPa·s[4] 35000 mPa·s[4] | > 25 N/mm[11] > 25 N/mm[11] | 25[14] 25[14] | - - | 4.5 N/mm²[17] 4.5 N/mm²[17] | 450 %[20] 450 %[20] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 40000 mPa·s[4] 40000 mPa·s[4] | > 30 N/mm[11] > 30 N/mm[11] | 32[15] 32[15] | - - | 5 N/mm²[17] 5 N/mm²[17] | 400 %[20] 400 %[20] | Resistance against polyester, Resistance against PU | - | - | Flowable | Condensation-curing, Two-component | - | ||
| 20000 mPa·s[4] 20000 mPa·s[4] | > 20 N/mm[11] > 20 N/mm[11] | 20[15] 20[15] | - - | 7[17] 7[17] | 800 %[20] 800 %[20] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 15000 mPa·s[4] 15000 mPa·s[4] | > 30 N/mm[11] > 30 N/mm[11] | 28[15] 28[15] | - - | 6.5 N/mm²[17] 6.5 N/mm²[17] | 700 %[20] 700 %[20] | Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 15000 mPa·s[4] 15000 mPa·s[4] | > 30 N/mm[11] > 30 N/mm[11] | 28[15] 28[15] | - - | 6.5 N/mm²[17] 6.5 N/mm²[17] | 700 %[20] 700 %[20] | Resistance against concrete, Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 20000 mPa·s[4] 20000 mPa·s[4] | > 30 N/mm[11] > 30 N/mm[11] | 37[15] 37[15] | - - | 7 N/mm²[17] 7 N/mm²[17] | 480 %[20] 480 %[20] | Resistance against concrete, Resistance against casting resins | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 50000 mPa·s[7] 50000 mPa·s[7] | > 25 N/mm[11] > 25 N/mm[11] | 43[15] 43[15] | - - | > 4.5 N/mm²[17] > 4.5 N/mm²[17] | > 300 %[20] > 300 %[20] | Resistance against PU | Dry surface | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | Highly transparent | ||
| 20000 mPa·s[4] 20000 mPa·s[4] | > 30 N/mm[11] > 30 N/mm[11] | 37[15] 37[15] | - - | 7 N/mm²[17] 7 N/mm²[17] | 480 %[20] 480 %[20] | Resistance against casting resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 40000 mPa·s[4] 40000 mPa·s[4] | > 10 N/mm[11] > 10 N/mm[11] | 48[15] 48[15] | - - | 5 N/mm²[17] 5 N/mm²[17] | 300 %[20] 300 %[20] | Resistance against casting resins | - | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 70000 mPa·s[4] 70000 mPa·s[4] | > 25 N/mm[11] > 25 N/mm[11] | 40[15] 40[15] | - - | 5.5 N/mm²[17] 5.5 N/mm²[17] | 400 %[20] 400 %[20] | Resistance against PU | Slightly oil bleeding | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | Highly transparent | ||
| 50000 mPa·s[4] 50000 mPa·s[4] | > 28 N/mm[11] > 28 N/mm[11] | 40[15] 40[15] | - - | 5 N/mm²[17] 5 N/mm²[17] | 330 %[20] 330 %[20] | Resistance against PU | Strong oil bleeding | - | Flowable | No chemical shrinkage, Two-component, Addition Curing | Highly transparent | ||
| 120000 mPa·s[4] 120000 mPa·s[4] | 15 N/mm[11] 15 N/mm[11] | 55[14] 55[14] | - - | 5.5 N/mm²[16] 5.5 N/mm²[16] | 280 %[19] 280 %[19] | Resistance against polyester, Resistance against epoxy resins, Resistance against PU | Dry surface | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 300000 - 400000 mPa·s[8] 300000 - 400000 mPa·s[8] | > 7 N/mm[11] > 7 N/mm[11] | 55[15] 55[15] | - - | 4.5 N/mm²[17] 4.5 N/mm²[17] | 170 %[20] 170 %[20] | - | - | - | Spreadable self-levelling flow | Condensation-curing, Two-component, Fast curing at room temperature | - | ||
| 25000 mPa·s[4] 25000 mPa·s[4] | 30 N/mm[11] 30 N/mm[11] | 25[14] 25[14] | - - | 6.5 N/mm²[16] 6.5 N/mm²[16] | 600 %[19] 600 %[19] | - | - | - | Flowable | Two-component, Addition Curing | - | ||
| 110000 mPa·s[3] 110000 mPa·s[3] | 12 N/mm[11] 12 N/mm[11] | 53[14] 53[14] | - - | 5 N/mm²[16] 5 N/mm²[16] | 280 %[19] 280 %[19] | Resistance against casting resins | - | - | Flowable | Two-component, Addition Curing | - | ||
| - - | > 3 N/mm[13] > 3 N/mm[13] | 45[15] 45[15] | - - | 2 N/mm²[17] 2 N/mm²[17] | 130 %[20] 130 %[20] | - | - | - | - | Condensation-curing, Two-component | - | ||
| 5.000 mPa·s[9] 5.000 mPa·s[9] | 15[11] 15[11] | 15[14] 15[14] | - - | 6.5 N/mm²[16] 6.5 N/mm²[16] | 900 %[19] 900 %[19] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
| 15.000 mPa·s[10] 15.000 mPa·s[10] | 15 N/mm[11] 15 N/mm[11] | 40[14] 40[14] | - - | 8 N/mm²[16] 8 N/mm²[16] | 450 %[19] 450 %[19] | - | - | Food-contact | Flowable | No chemical shrinkage, Two-component, Addition Curing | - | ||
Legend
[1] 动态粘度 | Brookfield, [2] 动态粘度 23°C | ISO 3219, [3] 动态粘度 | 23 °C | ISO 3219, [4] 动态粘度 after stirring | 23 °C | ISO 3219, [5] 动态粘度 搅拌后 | 23 °C , [6] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219, [7] 动态粘度 搅拌后 | 23 °C | ISO 3219, [8] 动态粘度 | 23 °C | Brookfield, [9] 动态粘度 23°C, stirred | ISO 3219, [10] 动态粘度 23° C, stirred | ISO 3219, [11] Tear strength | ASTM D 624 B, [12] Tear strength | ASTM D 624, Die B, [13] Tear strength | ASTM 624 B, [14] Hardness Shore A | DIN ISO 48-4, [15] Hardness Shore A | ISO 868, [16] Tensile strength | ISO 37 type 1, [17] Tensile strength | ISO 37, [18] Tensile strength | DIN ISO 37, [19] Elongation at break | ISO 37 type 1, [20] Elongation at break | ISO 37, [21] Hardness Shore 00 | ASTM D 2240
[1] 动态粘度 | Brookfield, [2] 动态粘度 23°C | ISO 3219, [3] 动态粘度 | 23 °C | ISO 3219, [4] 动态粘度 after stirring | 23 °C | ISO 3219, [5] 动态粘度 搅拌后 | 23 °C , [6] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219, [7] 动态粘度 搅拌后 | 23 °C | ISO 3219, [8] 动态粘度 | 23 °C | Brookfield, [9] 动态粘度 23°C, stirred | ISO 3219, [10] 动态粘度 23° C, stirred | ISO 3219, [11] Tear strength | ASTM D 624 B, [12] Tear strength | ASTM D 624, Die B, [13] Tear strength | ASTM 624 B, [14] Hardness Shore A | DIN ISO 48-4, [15] Hardness Shore A | ISO 868, [16] Tensile strength | ISO 37 type 1, [17] Tensile strength | ISO 37, [18] Tensile strength | DIN ISO 37, [19] Elongation at break | ISO 37 type 1, [20] Elongation at break | ISO 37, [21] Hardness Shore 00 | ASTM D 2240