ELASTOSIL® M 4511

$ELASTOSIL<sup>®</sup> M 4511

Pourable, condensation-curing, two-component silicone rubber that vulcanizes at room temperature.

 

Main application: Making cost effective molds, specially suited for casting PE and PU resins.


Properties

  • very good flowability and self-deaeration
  • very low Shore A hardness (approx. 12)
  • high tear strength
  • extremely high elongation and flexibility
  • outstanding chemical resistance to attack by polyester and polyurethane resins, mold life is significantly extended

Specific features of ELASTOSIL® M 4511

  • Condensation-curing
  • Flowable
  • Resistance against polyester
  • Resistance against PU
  • Two-component

ELASTOSIL® M 4511 is a high-performance moldmaking compound, which is particularly suitable for the reproduction of models with extensive undercuts. ELASTOSIL® M 4511 is especially suitable for the processing of polyester and polyurethane resins.


Due to its very high extensibility and low flexural modulus, ELASTOSIL® M 4511 is best suited for the reproduction of fine or fragile models, where the piece may be damaged by more rigid molding materials on demolding.


ELASTOSIL® M 4511 exhibits low hardness and high strength, plus excellent ink transfer characteristics. These make it a perfect base material for the production of printing pads.

If molds for processing epoxy or polyurethane resins are to be made, ELASTOSIL M 4511 is cured by adding 5 wt % Catalyst T 21.

 

For molds used to process other reproduction materials such as polyester resins, plaster, concrete, synthetic stone, wax or low-melting alloys, 5 wt % Catalyst T 51 should be used.


Pot lifes and curing times of both catalysts may be accelerated, and thus adjusted to suit the individual application by blending with Catalyst T 47.
For faster curing either catalyst may be blended with Catalyst T 47. E.g. at a ratio of 95 : 5 (T51 : T47) the pot life decreases to about 30 min, and the mold needs only about 4 h to cure.
Further instructions on blending any catalyst with Catalyst T 47 may be found in our data-sheet: "WACKER® T-series catalysts".

The pot life is the period of time at 23 °C / 50 % rel. humidity during which the catalyzed mix to attain a viscosity of 100000 mPa s and still be just pourable

Please check also our brochures and info sheets.

Storage

The 'Best use before end' date of each batch is shown on the product label.

 

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

Sales and support

IMCD South Africa (Pty) Ltd.
275 Oak Avenue
2125 Randburg
南非
27  11  5704260 (Phone)
27 11 7873513   (Fax)
Contact
Website

How can we help you?

  • Do you need help in choosing a product or do you require technical support? If so, please contact our experts.
Ask a question

您是否需要产品样本？

您可以在此处索取产品样本。

索取样本

更多产品

个产品 技术数据
动态粘度 Tear-growth resistance Shore density A Breaking strength 断裂伸长率
CENUSIL® M 810 A/B 3000 mPa·s[1] 3000 mPa·s[1] 15 N/mm[10] 15 N/mm[10] 10[13] 10[13] 3.5 N/mm²[15] 3.5 N/mm²[15] 600 %[18] 600 %[18]
CENUSIL® M 820 A/B 6000 mPa·s[2] 6000 mPa·s[2] - - 20[13] 20[13] 4 N/mm²[15] 4 N/mm²[15] 500 %[18] 500 %[18]
CENUSIL® M 825 A/B 8000 mPa·s[3] 8000 mPa·s[3] 20 N/mm[10] 20 N/mm[10] 25[13] 25[13] 5 N/mm²[15] 5 N/mm²[15] 450 %[18] 450 %[18]
CENUSIL® M 830 A/B 8000 mPa·s[3] 8000 mPa·s[3] > 20 N/mm[10] > 20 N/mm[10] 26[13] 26[13] 5 N/mm²[15] 5 N/mm²[15] 500 %[18] 500 %[18]
ELASTOSIL® FX 10 A/B 6000 mPa·s[3] 6000 mPa·s[3] > 20 N/mm[11] > 20 N/mm[11] 10[13] 10[13] 4.5 N/mm²[15] 4.5 N/mm²[15] 950 %[18] 950 %[18]
ELASTOSIL® M 1470 - - > 10 N/mm[10] > 10 N/mm[10] 45[14] 45[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 230 %[19] 230 %[19]
ELASTOSIL® M 4115 A/B 2500 mPa·s[3] 2500 mPa·s[3] 5 N/mm[10] 5 N/mm[10] 17[13] 17[13] 3 N/mm²[15] 3 N/mm²[15] 400 %[18] 400 %[18]
ELASTOSIL® M 4125 F A/B 6000 mPa·s[3] 6000 mPa·s[3] - - 28[14] 28[14] 5.0[17] 5.0[17] 500[19] 500[19]
ELASTOSIL® M 4370 A/B 350 mPa·s[4] 350 mPa·s[4] > 4 N/mm[10] > 4 N/mm[10] 55[13] 55[13] 3.0 N/mm²[16] 3.0 N/mm²[16] 130 %[19] 130 %[19]
ELASTOSIL® M 4400 30000 mPa·s[5] 30000 mPa·s[5] > 3 N/mm[10] > 3 N/mm[10] 23[14] 23[14] 2 N/mm²[16] 2 N/mm²[16] 250 %[19] 250 %[19]
ELASTOSIL® M 4440 25000 mPa·s[5] 25000 mPa·s[5] 4.5 N/mm[10] 4.5 N/mm[10] 37[14] 37[14] 2.5 N/mm²[16] 2.5 N/mm²[16] 220 %[19] 220 %[19]
ELASTOSIL® M 4470 15000 mPa·s[6] 15000 mPa·s[6] > 4 N/mm[10] > 4 N/mm[10] 60[14] 60[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 120 %[19] 120 %[19]
ELASTOSIL® M 4503 40000 mPa·s[6] 40000 mPa·s[6] > 20 N/mm[10] > 20 N/mm[10] 25[13] 25[13] 20 N/mm²[16] 20 N/mm²[16] 350 %[19] 350 %[19]
ELASTOSIL® M 4511 25000 mPa·s[5] 25000 mPa·s[5] > 18 N/mm[10] > 18 N/mm[10] 12[14] 12[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 600 %[19] 600 %[19]
ELASTOSIL® M 4512 30000 mPa·s[5] 30000 mPa·s[5] > 24 N/mm[10] > 24 N/mm[10] 20[14] 20[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 500 %[19] 500 %[19]
ELASTOSIL® M 4514 35000 mPa·s[6] 35000 mPa·s[6] > 25 N/mm[10] > 25 N/mm[10] 25[13] 25[13] 4.5 N/mm²[16] 4.5 N/mm²[16] 450 %[19] 450 %[19]
ELASTOSIL® M 4541 40000 mPa·s[6] 40000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 32[14] 32[14] 5 N/mm²[16] 5 N/mm²[16] 400 %[19] 400 %[19]
ELASTOSIL® M 4600 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 20 N/mm[10] > 20 N/mm[10] 20[14] 20[14] 7[16] 7[16] 800 %[19] 800 %[19]
ELASTOSIL® M 4601 A/B 15000 mPa·s[6] 15000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 28[14] 28[14] 6.5 N/mm²[16] 6.5 N/mm²[16] 700 %[19] 700 %[19]
ELASTOSIL® M 4642 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 37[14] 37[14] 7 N/mm²[16] 7 N/mm²[16] 480 %[19] 480 %[19]
ELASTOSIL® M 4643 A/B 40000 mPa·s[6] 40000 mPa·s[6] > 10 N/mm[10] > 10 N/mm[10] 48[14] 48[14] 5 N/mm²[16] 5 N/mm²[16] 300 %[19] 300 %[19]
ELASTOSIL® M 4670 A/B 120000 mPa·s[6] 120000 mPa·s[6] 15 N/mm[10] 15 N/mm[10] 55[13] 55[13] 5.5 N/mm²[15] 5.5 N/mm²[15] 280 %[18] 280 %[18]
ELASTOSIL® RT 480 300000 - 400000 mPa·s[7] 300000 - 400000 mPa·s[7] > 7 N/mm[10] > 7 N/mm[10] 55[14] 55[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 170 %[19] 170 %[19]
ELASTOSIL® RT 625 A/B 25000 mPa·s[6] 25000 mPa·s[6] 30 N/mm[10] 30 N/mm[10] 25[13] 25[13] 6.5 N/mm²[15] 6.5 N/mm²[15] 600 %[18] 600 %[18]
ELASTOSIL® RT 646 A/B 110000 mPa·s[3] 110000 mPa·s[3] 12 N/mm[10] 12 N/mm[10] 53[13] 53[13] 5 N/mm²[15] 5 N/mm²[15] 280 %[18] 280 %[18]
ELASTOSIL® RT K - - > 3 N/mm[12] > 3 N/mm[12] 45[14] 45[14] 2 N/mm²[16] 2 N/mm²[16] 130 %[19] 130 %[19]
ELASTOSIL® VARIO 15 5.000 mPa·s[8] 5.000 mPa·s[8] 15[10] 15[10] 15[13] 15[13] 6.5 N/mm²[15] 6.5 N/mm²[15] 900 %[18] 900 %[18]
ELASTOSIL® VARIO 40 15.000 mPa·s[9] 15.000 mPa·s[9] 15 N/mm[10] 15 N/mm[10] 40[13] 40[13] 8 N/mm²[15] 8 N/mm²[15] 450 %[18] 450 %[18]
说明
[1] 动态粘度 | Brookfield,  [2] 动态粘度 23°C | ISO 3219,  [3] 动态粘度 | 23 °C | ISO 3219,  [4] 动态粘度 搅拌后 | 23 °C ,  [5] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219,  [6] 动态粘度 after stirring | 23 °C | ISO 3219,  [7] 动态粘度 | 23 °C | Brookfield,  [8] 动态粘度 23°C, stirred | ISO 3219,  [9] 动态粘度 23° C, stirred | ISO 3219,  [10] Tear-growth resistance | ASTM D 624 B,  [11] Tear-growth resistance | ASTM D 624, Die B,  [12] Tear-growth resistance | ASTM 624 B,  [13] Shore density A | DIN ISO 48-4,  [14] Shore density A | ISO 868,  [15] Breaking strength | ISO 37 type 1,  [16] Breaking strength | ISO 37,  [17] Breaking strength | DIN ISO 37,  [18] 断裂伸长率 | ISO 37 type 1,  [19] 断裂伸长率 | ISO 37 

同类产品

Order

My media


Go to order form

Sales Contact

Wacker Chemicals Middle East
Dubai Silicon Oasis s/n
0001 Dubai
+971  4  709-9999 （电话）

My favorites

My products