CENUSIL® M 825 A/B

$CENUSIL<sup>®</sup> M 825 A/B

Pourable, addition-curing RTV-2 silicone rubber that cures at room temperature.

Main application: Making molds for concrete casting.


特性

  • Excellent flowability and self-deaeration
  • High tear strength
  • Low hardness (Shore A 25)
  • Mixing ratio of 1:1 for straightforward processing
  • Fast and non shrink cure at room temperature which can be accelerated considerably by the application of heat
  • Excellent long-term stability of  the mechanical properties of the vulcanizate
  • Good resistance to common reproduction materials    

CENUSIL® M 825 A/B的特殊性能

  • 低粘度
  • 加成固化
  • 双组分
  • 室温下快速固化
  • 无化学收缩
  • 易流动的

Due to its good resisitance to all common reproduction materrials, e.g. casting resins, concrete, as well as the superior mechanical properties, CENUSIL® M 825 A/B is especially suittable for all molds of models with 
extensive undercuts.

As a low-Shore A addition silicone rubber that cures
without undergoing dimensional shrinkage,  CENUSIL® M 825 A/B  is also suitable if absolutely  accurate copies of models are required.

储存

The 'Best use before end' date of each batch is shown on the product label.

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Quimica do Brasil Ltda.
Rua Municipal, 325
06612-060 Jandira
巴西
+55  11  4789-8300 （电话）
+55 11 4789-8345  （传真）
Contact Sales
网站

我们可以为您提供什么帮助？

  • 您在选择产品方面需要帮助或者需要技术咨询？ 请联系我们的专家
Ask a question

您是否需要产品样本？

您可以在此处索取产品样本。

索取样本

更多产品

个产品 技术数据
Viscosity, dynamic 动态粘度 Tear-growth resistance Shore density A Breaking strength 断裂伸长率
CENUSIL® M 810 A/B - - 3000 mPa·s[1] 3000 mPa·s[1] 15 N/mm[10] 15 N/mm[10] 10[13] 10[13] 3.5 N/mm²[15] 3.5 N/mm²[15] 600 %[18] 600 %[18]
CENUSIL® M 820 A/B - - 6000 mPa·s[2] 6000 mPa·s[2] - - 20[13] 20[13] 4 N/mm²[15] 4 N/mm²[15] 500 %[18] 500 %[18]
CENUSIL® M 825 A/B - - 8000 mPa·s[3] 8000 mPa·s[3] 20 N/mm[10] 20 N/mm[10] 25[13] 25[13] 5 N/mm²[15] 5 N/mm²[15] 450 %[18] 450 %[18]
CENUSIL® M 830 A/B - - 8000 mPa·s[3] 8000 mPa·s[3] > 20 N/mm[10] > 20 N/mm[10] 26[13] 26[13] 5 N/mm²[15] 5 N/mm²[15] 500 %[18] 500 %[18]
ELASTOSIL® FX 10 A/B - - 6000 mPa·s[3] 6000 mPa·s[3] > 20 N/mm[11] > 20 N/mm[11] 10[13] 10[13] 4.5 N/mm²[15] 4.5 N/mm²[15] 950 %[18] 950 %[18]
ELASTOSIL® M 1470 - - - - > 10 N/mm[10] > 10 N/mm[10] 45[14] 45[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 230 %[19] 230 %[19]
ELASTOSIL® M 4115 A/B - - 2500 mPa·s[3] 2500 mPa·s[3] 5 N/mm[10] 5 N/mm[10] 17[13] 17[13] 3 N/mm²[15] 3 N/mm²[15] 400 %[18] 400 %[18]
ELASTOSIL® M 4125 F A/B - - 6000 mPa·s[3] 6000 mPa·s[3] - - 28[14] 28[14] 5.0[17] 5.0[17] 500[19] 500[19]
ELASTOSIL® M 4370 A/B - - 350 mPa·s[4] 350 mPa·s[4] > 4 N/mm[10] > 4 N/mm[10] 55[13] 55[13] 3.0 N/mm²[16] 3.0 N/mm²[16] 130 %[19] 130 %[19]
ELASTOSIL® M 4400 - - 30000 mPa·s[5] 30000 mPa·s[5] > 3 N/mm[10] > 3 N/mm[10] 23[14] 23[14] 2 N/mm²[16] 2 N/mm²[16] 250 %[19] 250 %[19]
ELASTOSIL® M 4440 - - 25000 mPa·s[5] 25000 mPa·s[5] 4.5 N/mm[10] 4.5 N/mm[10] 37[14] 37[14] 2.5 N/mm²[16] 2.5 N/mm²[16] 220 %[19] 220 %[19]
ELASTOSIL® M 4470 - - 15000 mPa·s[6] 15000 mPa·s[6] > 4 N/mm[10] > 4 N/mm[10] 60[14] 60[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 120 %[19] 120 %[19]
ELASTOSIL® M 4503 - - 40000 mPa·s[6] 40000 mPa·s[6] > 20 N/mm[10] > 20 N/mm[10] 25[13] 25[13] 20 N/mm²[16] 20 N/mm²[16] 350 %[19] 350 %[19]
ELASTOSIL® M 4511 - - 25000 mPa·s[5] 25000 mPa·s[5] > 18 N/mm[10] > 18 N/mm[10] 12[14] 12[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 600 %[19] 600 %[19]
ELASTOSIL® M 4512 - - 30000 mPa·s[5] 30000 mPa·s[5] > 24 N/mm[10] > 24 N/mm[10] 20[14] 20[14] 3.5 N/mm²[16] 3.5 N/mm²[16] 500 %[19] 500 %[19]
ELASTOSIL® M 4514 - - 35000 mPa·s[6] 35000 mPa·s[6] > 25 N/mm[10] > 25 N/mm[10] 25[13] 25[13] 4.5 N/mm²[16] 4.5 N/mm²[16] 450 %[19] 450 %[19]
ELASTOSIL® M 4541 - - 40000 mPa·s[6] 40000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 32[14] 32[14] 5 N/mm²[16] 5 N/mm²[16] 400 %[19] 400 %[19]
ELASTOSIL® M 4600 A/B - - 20000 mPa·s[6] 20000 mPa·s[6] > 20 N/mm[10] > 20 N/mm[10] 20[14] 20[14] 7[16] 7[16] 800 %[19] 800 %[19]
ELASTOSIL® M 4601 A/B - - 15000 mPa·s[6] 15000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 28[14] 28[14] 6.5 N/mm²[16] 6.5 N/mm²[16] 700 %[19] 700 %[19]
ELASTOSIL® M 4642 A/B - - 20000 mPa·s[6] 20000 mPa·s[6] > 30 N/mm[10] > 30 N/mm[10] 37[14] 37[14] 7 N/mm²[16] 7 N/mm²[16] 480 %[19] 480 %[19]
ELASTOSIL® M 4643 A/B - - 40000 mPa·s[6] 40000 mPa·s[6] > 10 N/mm[10] > 10 N/mm[10] 48[14] 48[14] 5 N/mm²[16] 5 N/mm²[16] 300 %[19] 300 %[19]
ELASTOSIL® M 4670 A/B - - 120000 mPa·s[6] 120000 mPa·s[6] 15 N/mm[10] 15 N/mm[10] 55[13] 55[13] 5.5 N/mm²[15] 5.5 N/mm²[15] 280 %[18] 280 %[18]
ELASTOSIL® RT 480 - - 300000 - 400000 mPa·s[7] 300000 - 400000 mPa·s[7] > 7 N/mm[10] > 7 N/mm[10] 55[14] 55[14] 4.5 N/mm²[16] 4.5 N/mm²[16] 170 %[19] 170 %[19]
ELASTOSIL® RT 625 A/B - - 25000 mPa·s[6] 25000 mPa·s[6] 30 N/mm[10] 30 N/mm[10] 25[13] 25[13] 6.5 N/mm²[15] 6.5 N/mm²[15] 600 %[18] 600 %[18]
ELASTOSIL® RT 646 A/B - - 110000 mPa·s[3] 110000 mPa·s[3] 12 N/mm[10] 12 N/mm[10] 53[13] 53[13] 5 N/mm²[15] 5 N/mm²[15] 280 %[18] 280 %[18]
ELASTOSIL® RT K - - - - > 3 N/mm[12] > 3 N/mm[12] 45[14] 45[14] 2 N/mm²[16] 2 N/mm²[16] 130 %[19] 130 %[19]
ELASTOSIL® VARIO 15 5.000 mPa·s[8] 5.000 mPa·s[8] - - 15[10] 15[10] 15[13] 15[13] 6.5 N/mm²[15] 6.5 N/mm²[15] 900 %[18] 900 %[18]
ELASTOSIL® VARIO 40 - - 15.000 mPa·s[9] 15.000 mPa·s[9] 15 N/mm[10] 15 N/mm[10] 40[13] 40[13] 8 N/mm²[15] 8 N/mm²[15] 450 %[18] 450 %[18]
说明
[1] 动态粘度 | Brookfield,  [2] 动态粘度 23°C | ISO 3219,  [3] 动态粘度 | 23 °C | ISO 3219,  [4] 动态粘度 搅拌后 | 23 °C ,  [5] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219,  [6] 动态粘度 after stirring | 23 °C | ISO 3219,  [7] 动态粘度 | 23 °C | Brookfield,  [8] Viscosity, dynamic 23°C, stirred | ISO 3219,  [9] 动态粘度 23° C, stirred | ISO 3219,  [10] Tear-growth resistance | ASTM D 624 B,  [11] Tear-growth resistance | ASTM D 624, Die B,  [12] Tear-growth resistance | ASTM 624 B,  [13] Shore density A | DIN ISO 48-4,  [14] Shore density A | ISO 868,  [15] Breaking strength | ISO 37 type 1,  [16] Breaking strength | ISO 37,  [17] Breaking strength | DIN ISO 37,  [18] 断裂伸长率 | ISO 37 type 1,  [19] 断裂伸长率 | ISO 37 

同类产品

购物车

我的媒体


转至订单表

联系方式

Wacker Quimica do Brasil Ltda.
Rua Municipal, 325
06612-060 Jandira
+55  11  4789-8300 （电话）

收藏夹

我的产品